Although high strength steels represent yield strength up to 1300 MPa, welded structures reveal lowerstrength values. The strongest commercially available electrode provides the yield strength of about900 MPa. Therefore, in welded steels with strength above this type of filler metal, achieving anacceptable global strength is a crucial issue. In this master thesis, affects of different welding procedures on static strength of welded jointsof Weldox 960 and Weldox 1100 steels, were studied. These steels are produced by SSAB inOxelösund. Meanwhile, finite element method analyses were applied in order to investigatethe static strength behavior of such weldments under uniaxial tension. The welding parameters which were selected as variables are:  Heat input Weld joint geometry Filler metal When weld metal is undermatching in strength levels than the base material, by applyingtension the soft weld metal begins to deform before parent metal. At that point thedeformation of resulted soft zone, including the weld metal and the heat affected zone, ishindered by high strength parent metal. Thus, uniaxial stress caused by uniaxial load isconverted to multiaxial stress. This conversion in tension results in increase in the staticstrength of weldment. The increase in strength is emphasized by increase in the width of thewelded joint while the thickness of the plate is kept as constant. After experiments and performing FEM studies, it was revealed that the static strength ofWeldox 960 welded joints approaches towards the tensile strength of parent metal by increasein the width of the weldment. In Weldox 1100 joints; a slight increase in tensile properties ofthe weldments, when the width of the sample increases, was observed.

In presented diploma thesis is studied problematics of welding of high strength steels. This work also describes arc welding in protective atmosphere CMT Advanced. In experimental part of this work is CMT Advanced method compared with conventional arc welding in protective atmosphere in shortcut mode used for welding of Hardox 450 and Weldox 700 E. Comparing of mechanical properties of weld material are realized via transverse tensile testing and measuring of microhardness. Macrostructure and microstructure of weld was evaluated too. In the last part of this thesis is a brief economical assessment of both studied methods.

The diploma thesis is focused on characterization of fine – grained steels, choosing of welding technology and effects of heat transmission on weld joint quality. The effect of transmitted heat on microscopic structure and stiffness of weld have been studied. Based on obtained results the optimal parameters for welding of fine - grained steel have been determined.

This master thesis work has been carried out at the company SSAB EMEA in Oxelösund which is a global leader in quenched and tempered high-strength steel. The aim is to examine the importance of the material properties for the bendability of the specific steel grade Weldox. There are many conditions for various applications such as mobile cranes and vehicles that need to be fulfilled in order for the material to be approved, where one main prerequisite is the bendability. It is very important to be able to bend the material without the occurrence of cracks. The purpose of this work has therefore been to investigate and try to find the relationship between the material properties and the critical bending radius. Furthermore has another aim been to find the most suitable treatment process for the composition of this specific steel grade.The work was divided into two parts, where the first part was to examine two equally treated Weldox 960 plates that differed significantly in properties such as bendability and toughness. In the second part seven different plates of the steel grade Weldox 1100 have been investigated where all the plates were treated in various ways. The leveling of the plates was performed in two different ways; either according to the standard leveling or to the property affected leveling (ERIK). The experimental part includes tests such as bending, hardness, toughness, tensile and inclusions measurements.The results have shown that the most significant material properties affecting the bendability are the yield strength and the purity close to the plate surface. Leveling with ERIK as the last treatment step has shown that the toughness of the material can be increased but it does not affect the bendability for these specific steel grades. Other properties such as hardness, ultimate tensile strength and elongation have no major impact on the bendability for this specific composition. The most suitable treatment proved to be tempering at 200°C as the last step in the process chain.

Properties of weld at the high-powered welding methods. Description of MIG/MAG welding, LaserHybrid, Time Twin Digital. Steel Characteristic IMEX 700/DILLIMAX 690. Evaluation of weld with methods Time Twin Digital. Results of drawing, bending examinations, examination of hardness test and structure of weld surface.