<p>Silicon carbide is a promising wide bandgap semiconductormaterial for high-temperature, high-power, and high-frequencydevice applications. However, there are still a number offactors that are limiting the device performance. Among them,one of the most important and critical factors is the formationof low resistivity Ohmic contacts and high-temperature stableSchottky diodes on silicon carbide.</p><p>In this thesis, different metals (TiW, Ti, TiC, Al, and Ni)and different deposition techniques (sputtering andevaporation) were suggested and investigated for this purpose.Both electrical and material characterizations were performedusing various techniques, such as I-V, C-V, RBS, XRD, XPS,LEED, SEM, AFM, and SIMS.</p><p>For the Schottky contacts to n- and p-type 4H-SiC, sputteredTiW Schottky contacts had excellent rectifying behavior afterannealing at 500 ºC in vacuum with a thermally stableideality factor of 1.06 and 1.08 for n- and p-type,respectively. It was also observed that the SBH for p-type SiC(Φ<sub>Bp</sub>) strongly depends on the choice the metal with alinear relationship Φ<sub>Bp</sub>= 4.51 - 0.58Φ<sub>m</sub>, indicating no strong Fermi-level pinning.Finally, the behavior of Schottky diodes was investigated byincorporation of size-selected Au nano-particles in Ti Schottkycontacts on silicon carbide. The reduction of the SBH isexplained by using a simple dipole layer approach, withenhanced electric field at the interface due to the small sizeof the circular patch (Au nano-particles) and large differenceof the barrier height between two metals (Ti and Au) on both n-and p-SiC.</p><p>For the Ohmic contacts, titanium carbide (TiC) was used ascontacts to both n- and p-type 4H-SiC epilayers as well as onAl implanted layers. The TiC contacts were epitaxiallydeposited using a co-evaporation method with an e-beam Tisource and a Knudsen cell for C<sub>60</sub>, in a UHV system at low substrate temperature(500 ºC). In addition, we extensively investigatedsputtered TiW (weight ratio 30:70) as well as evaporated NiOhmic contacts on both n- and p-type epilayers of SiC. The bestOhmic contacts to n-type SiC are annealed Ni (>950ºC)with the specific contact resistance of ≈ 8× 10<sup>-6</sup>Ω cm<sup>2</sup>with doping concentration of 1.1 × 10<sup>-19</sup>cm<sup>-3</sup>while annealed TiW and TiC contacts are thepreferred contacts to p-type SiC. From long-term reliabilitytests at high temperature (500 ºC or 600 ºC) invacuum and oxidizing (20% O<sub>2</sub>/N<sub>2</sub>) ambient, TiW contacts with a platinum cappinglayer (Pt/Ti/TiW) had stable specific contact resistances for>300 hours.</p><p><b>Keywords</b>: silicon carbide, Ohmic and Schottky contacts,co-evaporation, current-voltage, capacitance-voltagemeasurement, power devices, nano-particles, Schottky barrierheight lowering, and TLM structures.</p>
| Identifer | oai:union.ndltd.org:UPSALLA/oai:DiVA.org:kth-3335 |
| Date | January 2002 |
| Creators | Lee, Sang Kwon |
| Publisher | KTH, Microelectronics and Information Technology, IMIT, Kista : Mikroelektronik och informationsteknik |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, text |
| Relation | Trita-EKT, 1650-8599 ; 2002:1 |
Page generated in 0.0019 seconds