The aim of master thesis was to study structural and transport properties of PVA films modified with method of semi-IPN with suitable polyectrolytes and plasticizers. The first important step was optimalization of PVA films preparation, when time of heating was set at 90 °C for 1 hour. Drying was set at 50 °C for 24 hours. Molecular weight of PVA was chosen 85–124 kDa in concentration 10 wt.%. For preparation of PVA-based semi-IPN thin films polyelectrolytes (polyglutamic acid, DEAE-dextran hydrochloride) and plasticizer (glycerol) were selected. Basic characterization of prepared materials was performed with FTIR, TGA, SEM and specific surface analysis. The difference between modified PVA films was in the chargé of individual functional groups carried by used polyelectrolytes. Surfaces of all the PVA films were smooth without visible defects. Transport properties were characterized with the method of horizontal diffusion cell with methylen blue used as a probe. Diffusion coefficients of methylen blue through PVA films were determined. It was found, that the fastest pass was throw PVA film without additives. The slowest diffusion was observed through PVA/DEAE-dextran film, because of the same charge of the film with a probe. PVA/PGA reacted with methylen blue to form a complex. Plasticizer effect on the diffusion was only minor; it caused a slight decrease of diffusion coefficient. These films were easier to handle.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:449409 |
| Date | January 2021 |
| Creators | Dobiášová, Andrea |
| Contributors | Smilek, Jiří, Kalina, Michal |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0021 seconds