Orientador: Maria do Carmo Gonçalves / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Química / Made available in DSpace on 2018-08-25T19:32:01Z (GMT). No. of bitstreams: 1
Brandao_LarissaReis_D.pdf: 4901816 bytes, checksum: e2662ff13e1db4f6ba5a090882ebef83 (MD5)
Previous issue date: 2013 / Resumo: Neste trabalho foram preparados compósitos de acetato de celulose e polissiloxano, usando 3-isocianatopropiltrietoxissilano como agente de acoplamento em dois solventes distintos: tetrahidrofurano e N,N-dimetilformamida. A estrutura, os comportamentos térmico e dinâmico-mecânico, e a morfologia dos compósitos obtidos foram investigados. Inicialmente, o acetato de celulose foi modificado com o agente de acoplamento, por meio da reação entre os grupos hidroxila presentes na cadeia do acetato de celulose e os grupos isocianato presentes no agente de acoplamento. Os compósitos de acetato de celulose/polissiloxano foram então preparados usando duas etapas: (1) hidrólise seguida pela reação de condensação do acetato de celulose modificado na presença de água e (2) reação de condensação do acetato de celulose modificado na presença de polidimetilssiloxano com terminações silanol. Os compósitos, preparados em ambos solventes, apresentaram separação de fases que foi confirmada pela presença de micro e nanodomínios de siloxano dispersos na matriz de acetato de celulose, com boa adesão interfacial entre as fases. Os resultados demonstraram, para os compósitos preparados em tetrahidrofurano, que a incorporação da fase polissiloxano na matriz de acetato de celulose causou uma diminuição na temperatura de transição vítrea, módulo de armazenamento e dureza e um aumento do caráter hidrofóbico da superfície do acetato de celulose. Por outro lado, para os compósitos em N,N-dimetilformamida, a incorporação da fase polissiloxano causou um aumento na temperatura de transição vítrea, módulo de armazenamento e caráter hidrofóbico. Os compósitos apresentaram estabilidade térmica similar ao acetato de celulose puro, para os compósitos preparados em ambos os solventes. Foram preparados também nanocompósitos de acetato de celulose/nanocristais de celulose, pelo método casting, usando 3-isocianatopropiltrietoxissilano como agente de acoplamento. Os nanocristais de celulose foram obtidos a partir da hidrólise ácida com ácido clorídrico de fibras de algodão. Os nanocristais apresentaram formato de agulha. Os nanocompósitos preparados foram avaliados quanto às suas características estruturais, térmicas, dinâmico-mecânicas e morfológicas. Os nanocompósitos de acetato de celulose/nanocristais de celulose apresentaram uma diminuição na Tg e um aumento no módulo de armazenamento e no caráter hidrofóbico da superfície do acetato de celulose. Por outro lado, o nanocompósito de acetato de celulose modificado/nanocristais de celulose apresentou diminuição do caráter hidrofóbico quando comparado com o compósito acetato de celulose/polissilsesquioxano. Não foi observada variação na estabilidade térmica. Análises de microscopia eletrônica confirmaram a boa dispersão dos nanocristais de celulose na matriz de acetato de celulose, o que foi também confirmada pela transparência dos filmes obtidos. A metodologia proposta é, portanto, conveniente para a preparação de compósitos de acetato de celulose/polissiloxano, bem como nanocompósitos contendo nanocristais de celulose, o que permite obter materiais com propriedades úteis / Abstract: In this work, cellulose acetate and polisiloxane composites were prepared from 3-isocianatepropiltrietoxisilane as a coupling agent in two different solvents: tetrahidrofurane and N,N-dimethilformamide. The structure, thermal and dynamic-mechanical behavior, and morphology of the obtained composites were investigated. Initially, the cellulose acetate was modified with the coupling agent, by means of a reaction between the hydroxyl groups present in the cellulose acetate chain and the isocianate groups present in the coupling agent. The cellulose acetate/polisiloxane composites were prepared using two steps: (1) hydrolysis followed by condensation reaction of the cellulose acetate modified in the presence of water and (2) condensation reaction of the cellulose acetate modified in the presence of the polidimethilsiloxane with silanol endings. The composites prepared in both solvents presented phase separation which was confirmed by siloxane micro and nanodomains dispersed in the matrix of the cellulose acetate with good interfacial adhesion between the phases. The results demonstrated that for the composites prepared in THF, the incorporation of the polisiloxane phase in the cellulose acetate matrix caused a decreasing in the vitreous transition, storage and hardness moduli and an increasing of the hydrophobic character of the surface of the cellulose acetate. On the other hand, for the composites in DMF, the incorporation of the polisiloxane phase caused an increase in the vitreous transition, storage modulus and hydrophobic character. The composites presented thermal stability similar to the pure cellulose acetate for the composites prepared in both solvents. Nanocomposites of cellulose acetate/cellulose nanocrystals were also prepared of by the casting method using 3-isocianatepropiltrietoxisilane as a coupling agent. The cellulose nanocrystals were obtained from an acidic hydrolysis of cotton fibers. The nanocomposites prepared were investigated according to their structural, thermal, dynamic-mechanical and morphological characteristics. The nanocomposites of cellulose acetate/cellulose nanocrystals presented a decrease in the Tg and an increase in the storage modulus in relation to the CA matrix, but it was not observed a variation in the thermal stability. Microscopic analysis confirmed the good dispersion of the cellulose nanocrystals in the cellulose acetate matrix, which it was also confirmed by the transparency of the obtained films. Therefore, the proposed methodology is convenient for the preparation of the cellulose acetates/polisiloxane as well as nanocomposites containing cellulose nanocrystals, which allows to obtain materials with useful properties / Doutorado / Físico-Química / Doutora em Ciências
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248732 |
Date | 25 August 2018 |
Creators | Brandão, Larissa Reis, 1978- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Gonçalves, Maria do Carmo, 1957-, Romero, Rafaelle Bonzanini, Lima, Juliana Aristeia de, Morales, Ana Rita, Paoli, Marco-Aurelio De |
Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
Source Sets | IBICT Brazilian ETDs |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 112 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds