Analysis of calcium and oxygen atom arrays of known cement minerals and the structures of cellulose polymorphs were performed to see if it was possible to arrange a cellulose fibre on a cement mineral face such that the fibre is bonded by a repeating array of hydrogen or hydroxide coordination bonds for the full length of the attachment. Of the sixteen important cement minerals modelled, xonotlite, foshagite, tricalcium aluminate hydrate, chondronite and rosenhahnite could form such bonds to modified cellulose fibre. However, this was not the case for other cement minerals, especially tobermorite. Alumium hydroxide, when added to cement-quartz pastes and autoclaved at 180 degrees C, was found to improve the cement's ability to resist carbonation. / Doctor of Philosophy (PhD)
| Identifer | oai:union.ndltd.org:ADTP/189416 |
| Date | January 2001 |
| Creators | Peng, Joe Zhou, University of Western Sydney, College of Science, Technology and Environment, School of Science, Food and Horticulture |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
Page generated in 0.0016 seconds