Electrospun nanofibers have been used for many applications, but a reliance on organic solvents limits their use in biomedical fields. In this study, we successfully electrospun nanofibers from aqueous chitosan-hyaluronic acid complex coacervates. We studied how solvent’ properties affected the average nanofiber diameter by using pure water as a solvent versus ethanol-water solutions. Experimentally, we investigated the effect of electrospinning apparatus parameters, such as how the applied voltage affected fiber formation and morphology. The smallest average nanofiber diameter was determined to be around 115 ± 30 nm when 3 wt% ethanol coacervate samples were electrospun using the applied voltage of 24 kV. Linear viscoelastic measurements were used to study the rheological characterization of complex coacervate with different salt concentrations and cosolvents (e.g., ethanol weight percent). Chitosan-hyaluronic acid nanofibers hold potential in biomedical applications such as wound dressing, tissue engineering, would healing scaffolds.
Identifer | oai:union.ndltd.org:UMASS/oai:scholarworks.umass.edu:masters_theses_2-1807 |
Date | 20 August 2019 |
Creators | Sun, Juanfeng |
Publisher | ScholarWorks@UMass Amherst |
Source Sets | University of Massachusetts, Amherst |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | Masters Theses |
Page generated in 0.0019 seconds