Utilização de blendas poliméricas no reparo de defeitos cranianos de ratos / Use of polymer blends in the repair of cranial defects in rats

Na clínica ortopédica e traumatológica existem diversos desafios clínicos envolvendo as extensas perdas de tecido ósseo, relacionados primordialmente com causas traumáticas, tumorais, congênitas e infecciosas. No tratamento, podem ser utilizados os enxertos autólogos, homólogos, xenólogos e os enxertos periostais. Os substitutos sintéticos, conhecidos como biomateriais, também são uma boa alternativa. O objetivo deste trabalho foi avaliar o processo de neoformação óssea durante o reparo de defeitos ósseos, provocados experimentalmente no crânio de animais enxertados com blenda polimérica, constituída de colágeno de tendão bovino e quitosana associada à hidroxiapatita. Foram utilizados 30 ratos (Rattus norvegicus, Wistar), machos, com peso aproximado de 330 gramas e 4 meses de idade. Os animais foram submetidos ao procedimento cirúrgico para a criação de defeito ósseo no osso parietal esquerdo da calota craniana para o preenchimento com os biomateriais pesquisados. Foram divididos em 3 grupos com 10 animais cada, sendo um grupo controle sem a implantação de biomaterial, outro com implantação de blenda de colágeno e quitosana e o último com a utilização desta blenda em associação com hidroxiapatita. Cada grupo foi subdividido em dois subgrupos com 5 animais de acordo com o tempo do sacrifício pós-operatório, sendo com 3 semanas nos grupos de G1 a G3 e com 8 semanas de G4 a G6. Após o sacrifício, as calotas cranianas foram retiradas para foto documentação macroscópica e exames radiográficos. Em seguida, as amostras foram submetidas aos procedimentos histotécnicos de confecção das lâminas para avaliação histológica da neoformação óssea no local cirúrgico. A pesquisa foi aprovada pelo comitê de ética da Faculdade de Medicina de Jundiaí, protocolo nº 301/12. As análises macroscópicas e radiográficas demonstraram a biocompatibilidade das blendas utilizadas. Histologicamente, houve discreta neoformação óssea em continuidade com as margens da lesão óssea, porém predominou a presença de tecido conectivo na área cirúrgica. As blendas poliméricas apresentaram biocompatibilidade com o tecido receptor, porém com baixa capacidade osteogênica devido à permanência do defeito ósseo. Não houve a sua osteointegração em virtude da presença de tecido conectivo em grande quantidade e adjacente ao implante. / In orthopedics and traumatology there are several clinical challenges involving extensive bone loss, primarily related to trauma, tumors, congenital and infectious diseases. These conditions can be usually treated by autologous, periosteal, homologous and xenologous grafts. A good alternative is to use synthetic biomaterials as substitute. The aim of this study was to evaluate the process of bone formation during repair of bone defects experimentally induced in animals skull, grafted by a polymer blend consisting of bovine tendon collagen and chitosan associated with hydroxyapatite. A total of 30 rats (Rattus norvegicus, Wistar) male, weighing approximately 330 grams and 4 months old was used. The animals underwent the surgical procedure for the creation of defect in the left parietal bone of the skull. They were divided into 3 groups of 10 animals each: a control group without biomaterials implantation, another with a blend of collagen and chitosan and the latest with the use of this blend in association with hydroxyapatite. Each group was subdivided into two subgroups of 5 animals according to the sacrifice schedule after surgery. The groups were named G1, G2 and G3 when the sacrifice occurred after 3 weeks postoperative and G4, G5 and G6 after eight weeks. After sacrifice, the calvarias were removed for macroscopic photo documentation and radiographic examinations. Then the samples were subjected to histotechnical procedures for histological evaluation of new bone formation at the surgical site. The study was approved by the ethics committee of the Faculdade de Medicina de Jundiaí (protocol # 301/12). The macroscopic and radiographic analysis demonstrated the biocompatibility of the blends. Histologically, there was a slight bone formation in continuity with the edges of the bone lesion, but the predominant presence of connective tissue in the surgical area. The polymer blends showed biocompatibility with the host tissue but low osteogenic capacity due to the bone defect. There was no osseointegration due to the presence of connective tissue in large quantity adjacent to the implant.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-12022014-114736
Date13 December 2013
CreatorsMarcelo de Azevedo e Souza Munhoz
ContributorsMarcelo Rodrigues da Cunha, Itibagi Rocha Machado, Ana Maria de Guzzi Plepis
PublisherUniversidade de São Paulo, Bioengenharia, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0027 seconds