To accelerate environmentally friendly thin film photovoltaic (PV) technologies, copper-based chalcogenides are attractive as absorber materials. Chalcopyrite copper indium gallium selenide (CIGS ≡ CuIn1–xGaxSe2) is today a commercially important PV material, and it is also in many aspects a very interesting material from a scientific point of view. Copper zinc tin sulfide selenide (CZTSSe ≡ Cu2ZnSn(S1–xSex)4) is considered as an emerging alternative thin film absorber material. Ternary Cu2SnS3 (CTS) is a potential absorber material, thus its related alloys Cu2Sn1–xGexS3 (CTGS) and Cu2Sn1–xSixS3 (CTSS) are attractive due to the tunable band gap energies. CuSb(Se1–xTex)2 and CuBi(S1–xSex)2 can be potential as ultra-thin (≤ 100 nm) film absorber materials in the future. In the thesis, analyses of these Cu-based chalcogenides are based on first-principles calculations performed by means of the projector augmented wave method and the full-potential linearized augmented plane wave formalisms within the density functional theory as implemented in the VASP and WIEN2k program packages, respectively. The electronic and optical properties of CIGS (x = 0, 0.5, and 1) are studied, where the lowest conduction band (CB) and the three uppermost valence bands (VBs) are parameterized and analyzed in detail. The parameterization demonstrates that the corresponding energy dispersions of the topmost VBs are strongly anisotropic and non-parabolic even very close to the Γ-point. Moreover, the density-of-states and constant energy surfaces are calculated utilizing the parameterization, and the Fermi energy level and the carrier concentration are modeled for p-type CIGS. We conclude that the parameterization is more accurate than the commonly used parabolic approximation. The calculated dielectric function of CuIn0.5Ga0.5Se2 is also compared with measured dielectric function of CuIn0.7Ga0.3Se2 collaborating with experimentalists. We found that the overall shapes of the calculated and measured dielectric function spectra are in good agreement. The transitions in the Brillouin zone edge from the topmost and the second topmost VBs to the lowest CB are responsible for the main absorption peaks. However, also the energetically lower VBs contribute significantly to the high absorption coefficient. CTS and its related alloys are explored and investigated. For a perfectly crystalline CTS, reported experimental double absorption onset in dielectric function is for the first time confirmed by our calculations. We also found that the band gap energies of CTGS and CTSS vary almost linearly with composition over the entire range of x. Moreover, those alloys have comparable absorption coefficients with CZTSSe. Cu2XSnS4 (X = Be, Mg, Ca, Mn, Fe, Ni, and Zn) are also studied, revealing rather similar crystalline, electronic, and optical properties. Despite difficulties to avoid high concentration of anti-site pairs disordering in all compounds, the concentration is reduced in Cu2BeSnS4 partly due to larger relaxation effects. CuSb(Se1–xTex)2 and CuBi(S1–xSex)2 are suggested as alternative ultra-thin film absorber materials. Their maximum efficiencies considering the Auger effect are ~25% even when the thicknesses of the materials are between 50 and 300 nm. / <p>QC 20170523</p>
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-207626 |
| Date | January 2017 |
| Creators | Chen, Rongzhen |
| Publisher | KTH, Materialvetenskap, Stockholm |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds