Influence of Ferrite Content on Fatigue Strength of Quenched and Tempered 42CrMoS4 Steel

Specimens of steel 42CrMoS4 were quenched from the austenite (γ) and the ferrite (α) + austenite + cementite phase fields to produce fully martensitic matrices with 0 – 14 % ferrite dispersed in the matrix. After tempering at 300°C or 600°C mechanical and fatigue properties were determined. As expected yield strength, tensile strength and hardness decreased with increased tempering temperature and ferrite content. Quite unexpected, the fatigue properties were mildly affected. A small amount of ferrite, approximately 3% even appears to improve the fatigue strength. Then, at even higher ferrite amounts, slightly below 20% the fatigue strength appears to decrease again.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-102023
Date January 2012
CreatorsHanno, Mithaq Elias
PublisherKTH, Materialvetenskap
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0014 seconds