Conducting polymer coating is the new developing area in the field of advanced textiles. In this project the rheological behaviour of paste containing conducting polymer was studied during formulation to coating application. The literature study is done by keeping all the contents of project in mind and a wide area of conductive polymer, coating methods, binder system and rheology modifier is covered. The rheological behaviour of different fluid containing newtanion and non-newtanion behaviour is discussed for better understanding of the project working. Polyester fabric was coated by knife coating method. In paste formulation, the chemicals used were polyurethane binder with two HEUR based rheology modifiers. A lot of experiments were performed to determine the right amount of rheology modifier alone or in combination for paste formulation and coating application and interesting findings were observed during the experimental work which had been justified in results and analysis. After application, the coated fabric was checked for resistivity. / Program: Magisterutbildning i textilteknologi
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hb-20146 |
Date | January 2010 |
Creators | IQBAL, KASHIF |
Publisher | Högskolan i Borås, Institutionen Textilhögskolan, University of Borås/Swedish School of Textiles |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Magisteruppsats, |
Page generated in 0.0146 seconds