Previous issue date: 2011-04-29 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / In this study it was used two metallic oxides, Ta2O5 and TiO2, in order to obtain
metallic powders of Ta and Ti through aluminothermic reduction ignited by plasma. Ta2O5
and TiO2 powders were mixed with Al in a planetary mill, using different milling times. A
thermal analysis study (DTA and TG) was carried out, in order to know the temperature to
react both the mixtures. Then, these mixtures were submitted to a hollow cathode discharge,
where they were reacted using aluminothermic reduction ignited by plasma. The product
obtained was characterized by XRD and SEM, where it was proven the possibility of
producing these metallic particles, different from the conventional process, where metallic
ingots are obtained. It was verified that the aluminothermic reduction ignited by plasma is
able to produce metallic powders of Ta and Ti, and a higher efficiency was observed to the
process with Ta2O5-Al mixtures. Among different microstructural aspects observed, it can be
noted the presence of metallic nanoparticles trapped into an Al2O3 matrix, besides acicular
structures (titanium) and dendritic structures (tantalum), which are a product characteristic
from a fast cooling / No presente estudo foram utilizados dois ?xidos met?licos, Ta2O5 e TiO2, visando a
obten??o de part?culas de Ta e Ti met?licos, por meio da redu??o aluminot?rmica com igni??o
a plasma. P?s de Ta2O5 e TiO2 foram misturados com p? de Al e mo?dos em um moinho
planet?rio por diferentes per?odos. Um estudo de an?lise t?rmica (DTA e TG) foi realizado,
visando se conhecer a temperatura de rea??o para ambas as misturas. Conhecidas essas
temperaturas, as misturas foram submetidas a uma descarga em c?todo oco, onde foram
reagidas pelo processo de redu??o aluminot?rmica com igni??o a plasma. O material obtido
foi caracterizado por DRX e MEV, onde se comprovou a possibilidade da obten??o de um
produto na forma de p?, algumas vezes de dimens?es nanom?tricas, diferentemente do
processo convencional, onde o produto final ? obtido na forma de lingote. Verificou-se que a
redu??o aluminot?rmica com igni??o a plasma ? capaz de produzir p?s de Ta e Ti met?licos,
com uma efici?ncia maior para a rea??o da mistura Ta2O5-Al. Dentre os diferentes aspectos
microestruturais observados, destaca-se a presen?a de nanopart?culas do metal de interesse
embebidas em uma matriz de Al2O3, al?m de estruturas acicular (tit?nio) e dendr?tica
(t?ntalo), que s?o caracter?sticas de um resfriamento r?pido
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/12776 |
Date | 29 April 2011 |
Creators | Brito, Roseane Aparecida de |
Contributors | CPF:09621199468, http://lattes.cnpq.br/7441669258580942, Souza, Carlson Pereira de, CPF:13681389420, http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4781094H3, Costa, Francin? Alves da, CPF:45327220478, http://lattes.cnpq.br/8698567925323942, Silva, Gilson Garcia da, CPF:56634161453, http://lattes.cnpq.br/8681275097040450, Gomes, Uilame Umbelino, Alves J?nior, Clodomiro |
Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Ci?ncia e Engenharia de Materiais, UFRN, BR, Processamento de Materiais a partir do P?; Pol?meros e Comp?sitos; Processamento de Materiais a part |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | application/pdf |
Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0101 seconds