Suscetibilidade à CorrosÃo Sob TensÃo Dos AÃos AISI 321 E 347 Em Meio De H2so4 + Cuso4 / Stress Corrosion Cracking Suscetiblity Of Stainless Steels AISI 321 And 347 In Copper Sulfate Soluction

Os aÃos inoxidÃveis austenÃticos tÃm sido bastante utilizados em equipamentos de utilidades de dessulfurizaÃÃo de petrÃleo devido à sua boa resistÃncia à corrosÃo em temperatura elevada.Contudo, esses materiais estÃo sujeitos a sensitizaÃÃo (deficiÃncia em cromo na regiÃo vizinha ao contorno de grÃo) quando expostos a temperaturas de 425 a 815ÂC, durante a operaÃÃo ou processos de fabricaÃÃo. A sensitizaÃÃo torna o equipamento suscetÃvel à corrosÃo sob tensÃo causada por aÃos politiÃnicos, formados pela interaÃÃo de compostos sulforoso, umidade e ar em temperatura ambiente. A resistÃncia à corrosÃo sob tensÃo de amostras de aÃo inoxidÃvel austenÃtico AISI 321 e 347, removidas de um tubo, foi investigada atravÃs do procedimento ASTM 262 Pr. E â ensaio alternativo e de execuÃÃo mais fÃcil do que a simulaÃÃo dos aÃos politiÃnicos. Os corpos de prova foram submetidos aos tratamentos tÃrmicos de estabilizaÃÃo (900ÂC, durante 75 minutos) e de sensitizaÃÃo (600ÂC, durante 20, 40, 80, 120 e 140 horas), apÃs o que foram expostos ao meio corrosivo de CuSO4 + H2SO4 durante 72 horas e depois dobradas, nÃo apresentando trincamento. A agressividade do meio utilizado no ensaio foi verificada atravÃs da utilizaÃÃo de amostras de aÃo AISI 304L sensitizadas (600ÂC, 24, 28 e 72 horas e 677ÂC durante 4, 45 e 72 horas). Neste caso, somente as amostras com acabamento superficial feito com lixa n 100 sofreram um intensivo processo corrosivo. / Os aÃos inoxidÃveis austenÃticos tÃm sido bastante utilizados em equipamentos de utilidades de dessulfurizaÃÃo de petrÃleo devido à sua boa resistÃncia à corrosÃo em temperatura elevada.Contudo, esses materiais estÃo sujeitos a sensitizaÃÃo (deficiÃncia em cromo na regiÃo vizinha ao contorno de grÃo) quando expostos a temperaturas de 425 a 815ÂC, durante a operaÃÃo ou processos de fabricaÃÃo. A sensitizaÃÃo torna o equipamento suscetÃvel à corrosÃo sob tensÃo causada por aÃos politiÃnicos, formados pela interaÃÃo de compostos sulforoso, umidade e ar em temperatura ambiente. A resistÃncia à corrosÃo sob tensÃo de amostras de aÃo inoxidÃvel austenÃtico AISI 321 e 347, removidas de um tubo, foi investigada atravÃs do procedimento ASTM 262 Pr. E â ensaio alternativo e de execuÃÃo mais fÃcil do que a simulaÃÃo dos aÃos politiÃnicos. Os corpos de prova foram submetidos aos tratamentos tÃrmicos de estabilizaÃÃo (900ÂC, durante 75 minutos) e de sensitizaÃÃo (600ÂC, durante 20, 40, 80, 120 e 140 horas), apÃs o que foram expostos ao meio corrosivo de CuSO4 + H2SO4 durante 72 horas e depois dobradas, nÃo apresentando trincamento. A agressividade do meio utilizado no ensaio foi verificada atravÃs da utilizaÃÃo de amostras de aÃo AISI 304L sensitizadas (600ÂC, 24, 28 e 72 horas e 677ÂC durante 4, 45 e 72 horas). Neste caso, somente as amostras com acabamento superficial feito com lixa n 100 sofreram um intensivo processo corrosivo. / Because of their resistance to high temperature corrosion by hydrogen sulfide, austenitic stanless steels are commonly used for equipment in desulfurization process. However, these materials are subject to sensitization (chromium carbide precipitation) from exposure in the temperature range 425 to 815ÂC during fabrication or operation. Sensitization makes the equipment susceptible to failure from intergranular stress corrosion cracking caused by polythionic acid. Polythionic acid is formed by sulfur
compounds, moisture, and air at ambient temperature. The main goal of the present work is to investigate the stress corrosion cracking susceptibility of stainless steels AISI
321 and 347 in polythionic acids using an alternative process that is to submit the samples to cooper-cooper sulfate-16% sulfuric acid test (ASTM A262 Pr.E). After the
stabilization heat treatment at 900ÂC for 75 minutes, samples were heat treated at 600ÂC during 20, 40, 80, 120 and 140 hours and then exposed to boiling acidified copper
sulfate solution for 72 hours. After exposure, the specimens were bent. The appearance of fissures or cracks was not observed in AISI 321 and 347 samples. The effectiveness of the solution has been made by submitting AISI 304L samples to the same environment . The AISI 304L samples with higher finishing have been cracked. The
ones with fine-ground finishing have not been attacked. / Because of their resistance to high temperature corrosion by hydrogen sulfide, austenitic stanless steels are commonly used for equipment in desulfurization process. However, these materials are subject to sensitization (chromium carbide precipitation) from exposure in the temperature range 425 to 815ÂC during fabrication or operation. Sensitization makes the equipment susceptible to failure from intergranular stress corrosion cracking caused by polythionic acid. Polythionic acid is formed by sulfur
compounds, moisture, and air at ambient temperature. The main goal of the present work is to investigate the stress corrosion cracking susceptibility of stainless steels AISI
321 and 347 in polythionic acids using an alternative process that is to submit the samples to cooper-cooper sulfate-16% sulfuric acid test (ASTM A262 Pr.E). After the
stabilization heat treatment at 900ÂC for 75 minutes, samples were heat treated at 600ÂC during 20, 40, 80, 120 and 140 hours and then exposed to boiling acidified copper
sulfate solution for 72 hours. After exposure, the specimens were bent. The appearance of fissures or cracks was not observed in AISI 321 and 347 samples. The effectiveness of the solution has been made by submitting AISI 304L samples to the same environment . The AISI 304L samples with higher finishing have been cracked. The
ones with fine-ground finishing have not been attacked.

Identiferoai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:5245
Date22 August 2003
CreatorsClÃudio Valadares Farias Campos
ContributorsHamilton Ferreira Gomes de Abreu, Pedro de Lima Neto, SÃrgio Souto Maior Tavares
PublisherUniversidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds