Desenvolvimento de uma nova metodologia para a funcionalização de nanopartículas magnéticas com peptóides

Dissertação (mestrado)–Universidade de Brasília, Faculdade UnB Planaltina, Pós-Graduação em Ciência de Materiais, 2014. / Submitted by Jaqueline Ferreira de Souza (jaquefs.braz@gmail.com) on 2014-12-09T11:07:34Z
No. of bitstreams: 1
2014_ElianeGoncalvesdeSiqueira.pdf: 1151936 bytes, checksum: 4f8a66ecf9c2e6e4f6682c8e79efa1d9 (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2014-12-11T14:48:38Z (GMT) No. of bitstreams: 1
2014_ElianeGoncalvesdeSiqueira.pdf: 1151936 bytes, checksum: 4f8a66ecf9c2e6e4f6682c8e79efa1d9 (MD5) / Made available in DSpace on 2014-12-11T14:48:38Z (GMT). No. of bitstreams: 1
2014_ElianeGoncalvesdeSiqueira.pdf: 1151936 bytes, checksum: 4f8a66ecf9c2e6e4f6682c8e79efa1d9 (MD5) / A síntese de nanopartículas magnéticas de óxido de ferro tem sido intensivamente investigada devido a seu vasto campo de aplicações em separação, regeneração, transporte e marcação de biomoléculas. Neste trabalho, foi explorada a possibilidade de desenvolver uma metodologia para a funcionalização da superfície de nanopartículas magnéticas de óxido de ferro utilizando reações multicompontentes Ugi. As nanopartículas de óxido de ferro foram obtidas pelo método de coprecipitação de soluções aquosas de sais de Fe+2 (usamos apenas solução de Fe II) com adição de uma base. Posteriormente as nanopartículas magnéticas foram recobertas por peptóides através da reação Ugi. As amostras de nanopartículas-peptóides foram caracterizadas por difração de raios-X (DRX), espectroscopia na região do infravermelho, fluorescência de raios-X (EDX) e termogravimetria (TGA). Os resultados revelaram uma estrutura bem ordenada da maioria das nanopartículas magnéticas-peptóides. A estrutura cristalina, bem como o diâmetro médio das nanopartículas sintetizadas foram deduzidas a partir dos padrões de difração de raios X e foi da ordem de 19 a 24nm para as nanopartículas mangnéticas-peptóides funcionalizados. Pela espectroscopia na região do infravermelho evidenciou a incorporação das estruturas do peptóides a nanopartícula magnética. A presença do ferro das nanopartículas foi comprovada por meio de dicromatometria e de Espectroscopia de Energia Dispersiva de Raio-X. _________________________________________________________________________________ ABSTRACT / The synthesis of magnetic nanoparticles of iron oxide has been intensively investigated due to their wide range of applications as concentration, separation, regeneration, transport and labeling of biomolecules. In this study, we explored the possibility of developing a methodology for functionalization of magnetic nanoparticles of iron oxide surface using Ugi reaction. The nanoparticles of iron oxide were obtained by coprecipitation of aqueous solutions of Fe+2 salts method (use only solution Fe II) with addition of a base. Subsequently, the magnetic nanoparticles were coated with peptoids via Ugi reaction. Samples of nanoparticles-peptoids were characterized by X-ray diffraction (XRD), infrared spectroscopy, X-ray fluorescence (EDX) and thermogravimetric analysis (TGA). The results revealed a well-ordered from most magnetic nanoparticles-peptoids structure. The crystal structure as well as the average diameter of the synthesized nanoparticles were deduced from the diffraction patterns of X-rays and it was approximately 19-24 nm for nanoparticles functionalized with peptoids. Iinfrared spectroscopy showed the incorporation of the structures of peptoids on magnetic nanoparticle. The presence of iron nanoparticles was confirmed by dicromatometry and energy dispersive spectroscopy X-ray.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/17319
Date30 January 2014
CreatorsSiqueira, Eliane Gonçalves de
ContributorsVercillo, Otilie Eichler
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB
RightsA concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess

Page generated in 0.0021 seconds