In this work, we investigated the nonlinear optical properties of five types of Ionic Liquids (ILs): BMI.NTf−2, HMI.NTf−2, OMI.NTf−2, DMI.NTf−2 and dodMI.NTf−2 . Using the technique of Z-scan was unable to determine the values of the thermal contributions n2 the refractive index of nonlinear ionic liquids. The experiment used a laser to the Titanium Sapphire operating in modelocked regiment, tuned to 820 nm, emitting pulses of 200 fs duration, with a repetition rate of 76 MHz and tune to 410 nm was used a crystal BBO for the second harmonic generation. All ILs had not self-desfocalizadora linearity. We observed that with the change of anion BF−4 and PF−6 by anion NTf−2 was a decrease in the amount of n2 to heat the home at a wavelength of 820 nm. The increase in chains of carbons with the anion NTf−2 in order to observe an increase in the contribution of n2 heat was not as significant for wave-length at 820 nm. For the wavelength at 410 nm we can observe an increase in the amount of n2. / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Nesta dissertação, investigamos as propriedades ópticas não-lineares de cinco tipos de líquidos Iônicos (LIs): BMI.NTf−2 , HMI.NTf−2 , OMI.NTf−2 , DMI.NTf−2 e dodMI.NTf−2 , utilizando a técnica de varredura Z (Z-scan). Estes materiais são sais orgânicos, apresentam uma baixa temperatura de fusão e pressão de vapor desprezível. Nós utilizamos para o experimento de varredura Z um laser de Titânio de Safira operando no regime modelocked, sintonizado em 820 nm, emitindo pulsos de 200 fs de duração, com taxa de repetição de 76 MHz. Também utilizamos o segundo harmônico produzido através de um cristal de BBO, para gerar comprimento de onda sintonizado em 410 nm. Todos os LIs apresentaram não linearidade auto-desfocalizadora. Observamos que com a mudança do ânion BF−4 e PF−6 pelo ânion NTf−2 houve uma diminuição no valor de n2 de origem térmica para comprimento de onda em 820 nm. O aumento das cadeias de carbonos com o ânion NTf−2 com objetivo de observar um aumento na contribuição térmica de n2 não foi tão expressiva para comprimento de onda em 820 nm. Para o comprimento de onda em 410 nm podemos observar um aumento no valor de n2 de origem térmica.
Identifer | oai:union.ndltd.org:IBICT/oai:www.repositorio.ufal.br:riufal/1003 |
Date | 09 March 2009 |
Creators | Santos, Cássio Eráclito Alves dos |
Contributors | Hickmann, Jandir Miguel, http://lattes.cnpq.br/0235913656361156, Caetano, Dílson Pereira, http://lattes.cnpq.br/3176702506687398, Teixeira, Sérgio Ribeiro, http://lattes.cnpq.br/5321503129467150 |
Publisher | Universidade Federal de Alagoas, BR, Física geral; Física teórica e computacional; Mecânica estatística; Ótica; Ótica não linear; Proprie, Programa de Pós-Graduação em Física da Matéria Condensada, UFAL |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Repositório Institucional da UFAL, instname:Universidade Federal de Alagoas, instacron:UFAL |
Rights | info:eu-repo/semantics/openAccess |
Relation | bitstream:http://www.repositorio.ufal.br:8080/bitstream/riufal/1003/1/Dissertacao_CassioEraclitoAlvesDosSantos_2009.pdf, bitstream:http://www.repositorio.ufal.br:8080/bitstream/riufal/1003/2/Dissertacao_CassioEraclitoAlvesDosSantos_2009.pdf.txt |
Page generated in 0.0214 seconds