Orientador: Itamar Ferreira / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-06T19:34:05Z (GMT). No. of bitstreams: 1
Sant'Anna_PedroCarneiro_D.pdf: 9344836 bytes, checksum: 94a9ee7db0c54b4a0cb6d76fffb44467 (MD5)
Previous issue date: 2006 / Resumo: Investigou-se o efeito de tratamentos térmicos intercríticos na microestrutura e propriedades mecânicas do aço API 5L X65 comumente utilizado em tubulações soldadas para transporte de óleo e gás. Vários pesquisadores demonstraram a existência de zonas frágeis na região intercrítica da zona afetada pelo calor (ZAC) de aços C-Mn e ARBL (alta resistência e baixa liga), produzidas durante o procedimento de soldagem de passe único e passes múltiplos. Além dos efeitos nocivos da martensita e da bainita superior, o microconstituinte formado por martensita-austenita retida, denominado constituinte M-A, é usualmente apontado como sendo o principal responsável pela degradação da tenacidade à fratura de alguns destes aços. Após os tratamentos térmicos de homogeneização e normalização, amostras do aço API 5L X65 foram submetidas a tratamentos térmicos intercríticos, realizados a 780 °C por 20 minutos e resfriadas com taxas equivalentes às dos insumos de calor obtidos em soldagens por arco submerso em chapas de 12 mm. As propriedades mecânicas foram avaliadas por meio dos ensaios de tração, dureza, resistência ao impacto Charpy e tenacidade à fratura CTOD. As características microestruturais foram analisadas por meio de microscopia ótica e microscopia eletrônica de varredura. O tratamento térmico de homogeneização foi eficiente para eliminar o bandeamento e a linha de segregação central da chapa. Verificou-se que o constituinte M-A está presente em todas as condições de resfriamento dos tratamentos térmicos realizados na região intercrítica, incluindo aquelas que promoveram alta tenacidade à fratura. A redução da taxa de resfriamento aumenta a quantidade do constituinte M-A até um determinado limite, pois ele se decompõe em ferrita + carbonetos. Pode-se concluir que os baixos níveis de tenacidade à fratura e ductilidade estão relacionados com a fração volumétrica da martensita obtida em altas taxas de resfriamento ou ao constituinte M-A com caráter martensítico. A condição intercrítica resfriada com taxa de 19 °C/s foi a que promoveu melhor relação resistência mecânica e tenacidade à fratura. Deve-se, portanto, selecionar procedimentos de soldagem que reduzam a fração volumétrica da martensita e do constituinte M-A / Abstract: The intercritical heat treatment effect on the microstructure and mechanical properties of the API 5L X65 steel, widely used in oil and gas pipeline, was investigated. Many researchers have suggested the existence of local brittle zones in the intercritical heat treatment zone (haz) of C-Mn and HSLA (high strenth low alloy) steels of single and multipass welding. Beyond deleterious effect of the martensite and upper bainite, the martensite and retained austenite microstructure, named MA constituent, is usualy pointed as being responsible for the toughness degradation of some of these steels. The specimens were submitted to homogenization and normalizing heat treatments, and then they were submitted to intercritical heat treatments performed at 780 oC for 20 minutes; after that the specimens were cooled using different cooling rates. The cooling rates were equivalent to the heat input obtained with 12 mm steel plate submerged arc weld. The tension, Vickers hardness, Charpy impact and CTOD tests were conducted. Microstructure characterizations were performed by using optical and scanning electron microscopy. Homogenization heat treatment was efficient to eliminate banding and the centerline segregation. It was verified that M-A constituent is present in all intercritical heat treatment conditons, including those of high fracture toughness. The cooling rate reduction increases the amount of M-A constituent until a certain limit, then it decomposes in ferrite + carbides. It was concluded that low toughness and ductility levels are closely related with the volume fraction of martensite obtained in high colling rates or with M-A constituent with a martensite character. The intercritical condition with 19°C/s cooling rate promoted the best correlation between strength and fracture toughness. To improve the intercrictical HAZ toughness of welds, it is suggested to select a welding procedure that diminishes the proportion of martensite and M-A constituent / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263175 |
| Date | 30 March 2006 |
| Creators | Sant'Anna, Pedro Carneiro |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Ferreira, Itamar, 1952-, Ierardi, Maria Clara Filippini, Santos, Rezende Gomes dos, Gomes, Samuel Irati Novaes, Rollo, Joao Manoel Domingos de Almeida |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 147p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |