Orientador: Amauri Hassui / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-26T13:15:15Z (GMT). No. of bitstreams: 1
Silva_NelsonCoutinhoda_M.pdf: 3269726 bytes, checksum: cff763b01ba2bd71b0f177a7764ec81c (MD5)
Previous issue date: 2014 / Resumo: O torneamento de aços endurecidos como alternativa a retificação cilíndrica, tem se tornado cada vez mais comum no meio industrial. Devido a melhorias do desempenho mecânico das máquinas, aliada aos avanços nos materiais de ferramenta, particularmente do PCBN, os bons resultados obtidos em aplicações e estudos realizados, vem estimulando cada vez mais essa prática. As diversas geometrias de peças utilizadas em componentes mecânicos submetem as ferramentas destinadas ao torneamento de aços endurecidos a condições de corte variadas, seja essas obtidas a partir de superfícies contínuas ou interrompidas. No entanto, a maior parte dos estudos já realizados, relacionados ao torneamento de aços endurecidos está voltada ao corte contínuo, fazendo do corte interrompido uma aplicação ainda pouco explorada. Este trabalho tem como objetivo estudar o comportamento da frequência de interrupção no torneamento de aços endurecidos com ferramenta de PCBN, além de sua interação com o ângulo de posição (?r) e velocidade de corte (vc). Para isso foram realizados experimentos de torneamento em corpos de prova com três frequências de interrupções diferentes, sendo um com baixa frequência de interrupção contendo dois rasgos, outro com média frequência de interrupção contendo quatro rasgos e finalmente outro com alta frequência de interrupção contendo oito rasgos, sendo esses transversais e equidistantes. Para a construção dos mesmos foi utilizado o aço ABNT 4340 com dureza entre 52 e 56 HRC, usando uma classe comercial de ferramenta PCBN 7525 (ISO H25) com alto teor de CBN (90%), recomendada para corte interrompido. Os parâmetros de saída analisados foram temperatura (°C), rugosidade (Ra), desgaste (VBmáx) e volume removido (mm3). Dentre as diversas conclusões desse trabalho, a principal delas indica que entre os parâmetros variados a frequência de interrupção é o que exerce maior influência sobre a temperatura e o volume removido, sendo que nos corpos de prova com maior frequência maiores volumes removidos foram alcançados, enquanto que nos corpos de prova com frequências menores, a temperatura atingiu níveis mais elevados / Abstract: Turning of hardened steels is becoming an important alternative to cylindrical grinding at industrial level. The increasing interest on this technique results from the good mechanical performance of the machine parts, which is accompanied by enhancements of the cutting tool materials, particularly PCBN, and the good results of using this technique, as reported in prior studies. Machine elements are characterized by a diversity of geometric forms. These characteristics promote that the cutting tools used for turning hardened steel are subjected to varying cutting conditions in both continuous and interrupted surfaces. However, most of the studies in this area have been related to turning hardened steels in continuous cutting. As a consequence, cutting of interrupted surfaces remains under-exploited. This work aims at studying the behavior of the interruption frequency during turning of hardened steels by using PCBN tools, as well as the interaction with the cutting tool¿s position angle (?r) and cutting speed (vc). For this, turning tests were performed on samples with three different interruption frequencies: a) low interruption frequency containing two slots, b) average interruption frequency containing four slots, and c) high interruption frequency containing eight slots. AISI 4340 steels with hardness between 52 and 56 HRC were used for manufacturing the samples. A commercial grade PCBN tool 7525 (ISO H25) with high CBN content (90%) was used as a cutting tool. The output parameters were temperature (°C), roughness (Ra), wear (VBmáx), and volume removed (mm3). Results indicate that the interruption frequency is the parameter that most affects the temperature and the volume removed. The samples mechanized at higher frequencies presented higher volume removed. Meanwhile, the samples turned with lower frequencies reached higher temperatures / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265862 |
| Date | 12 November 2014 |
| Creators | Silva, Nelson Coutinho da, 1971- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Hassui, Amauri, 1967-, Anholon, Rosley, Sanches, Luiz Eduardo de Angelo |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 80 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0045 seconds