Previous issue date: 2017-02-23 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Os aços de ultra alta resistência como o aço 4340 tem sido amplamente utilizados pela indústria aeronáutica e aeroespacial em aplicações como trens de pouso de aeronaves e o veículo lançador de satélite brasileiro (VLS), além de um uso extensivo para diversos setores da indústria em geral. Isso se deve, em grande medida, às suas propriedades mecânicas. Este trabalho se propõe a avaliar as propriedades tribológicas do par aço 4340, inicialmente submetido ao tratamento térmico de têmpera e revenimento, e a liga bronze alumínio 630, utilizados em trens de pouso. Será estudado o comportamento destas estruturas após o aço ser submetido a tratamentos de superfície por nitretação a plasma e carbonetação a laser, como forma de melhorar seu desempenho com relação ao atrito e ao desgaste. Neste estudo foi escolhido o ensaio tipo pino-disco para simular a situação real de desgaste. Os discos foram confeccionados a partir do aço AISI/SAE 4340 e os pinos foram feitos da liga bronze-alumínio 630. Foram realizadas análises microestruturais das estruturas e das camadas de compostos formadas devido ao tratamento de superfície, Após os ensaios de desgaste foram feitas observações das superfícies através de microscopia e perfilometria óptica, microscopia eletrônica de varredura, difratometria de raios-X, testes de riscamento (scratching tests), dureza, observação de rugosidade e pesagem dos corpos de prova. Foram levantados os parâmetros do desgaste e alterações microestuturais devido à interação entre as superfícies de contato durante os ensaios de deslizamento. Foi analisada a perda de massa e levantadas as curvas de desgaste e dos parâmetros relacionados ao atrito em função da distância percorrida e/ou do tempo de ensaio. Nos ensaios foram utilizadas três velocidades de ensaio: 0,5; 1,0 e 1,5 m/s. Foi possível o cálculo da taxa de desgaste para cada par e velocidades estudadas. De uma maneira geral constatou-se que os mecanismos de desgaste detectados são semelhantes para todas as condições de superfície dos discos. As imagens mostram que partículas do pino são deformadas sobre o disco, em forma de camadas, evidenciando o mecanismo de adesão. A carbonetação a laser criou uma camada rica em carbono com a presença de grafite que contribuiu para reduzir o coeficiente de atrito e o desgaste do pino, principalmente, para as velocidades de 0,5 e 1,0 m/s. A nitretação a plasma reduziu a perda de massa do disco e do pino, com indicativos de pequena perda de massa para todas as velocidades estudadas; a rugosidade e o aumento do coeficiente de atrito no par pino-disco para as velocidades de 1,0 e 1,5 m/s podem ter sido induzidas por alteração no tipo de desgaste, de adesivo para uma abrasão a três corpos. / Ultra high strength steels as 4340 steel has been widely used by the aerospace industry in applications such as aircraft landing gears and the Brazilian satellite launch vehicle (VLS), plus an extensive use for various sectors of the industry in general. This is due largely to their mechanical properties. This work aims to evaluate the tribological properties of 4340 steel pair, initially submitted to heat treatment of quenching and tempering, and aluminum bronze 630 alloy, used in landing gear. The behavior of these structures after the steel be subjected to surface treatment by plasma nitriding and laser carbonetation will be studied, as a way to improve its performance with respect to friction and wear. For this study, pin-on-disc test was chosen in order to simulate the real situation of wear. The discs were made from 4340 steel and pins were made of aluminium bronze 630 alloy. Micro-structural analyses were undertaken of the structures and compound layers formed due to surface treatment. After the wear tests surface observations were made through microscopy and perfilometry optical, scanning electron microscopy, x-ray diffractometry, x-ray tests, scratching tests, hardness, roughness and weighing of the specimens. Parameters of wear and microestuturals changes were raised due to interaction between the contact surfaces during rehearsals. Loss of mass was analyzed and curves of wear and friction related parameters were plotted in function of the slided distance and/or time of test. In the tests three test velocities were used: 0.5; 1.0 and 1.5 m/s. It was possible to calculate the wear rate for each pair and studied velocities. In general it was noted that the mechanisms of wear detected are similar for all conditions of the surface of the discs. The images show that the particles are bent on the disc, in the form of layers, showing the mechanism of adhesion. The laser carbonetation created a carbon-rich layer with the presence of graphite, which contributed to reduce the friction coefficient and pin wear, mainly for the 0.5 and 1.0 m/s velocities. The plasma nitriding reduced the loss in mass of the disk and pin, with indicative of small mass loss for all velocities studied; the roughness and the increase of the coefficient of friction in the couple pin-disc for the velocities of 1.0 and 1.5 m/s may have been induced by changes in the type of wear, from adhesive wear to a three-body abrasion. / CAPES: 99999.002441/2014-04
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/148983 |
| Date | 23 February 2017 |
| Creators | Barros, Renato Araujo [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Abdalla, Antonio Jorge [UNESP], Rodrigues, Humberto Lopes [UNESP], Denape, Jean |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600, 600, 600, 600 |
Page generated in 0.0027 seconds