Orientador: Mario Fernando de Goes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T03:34:21Z (GMT). No. of bitstreams: 1
Guimaraes_IsadoraRabelo_D.pdf: 1408417 bytes, checksum: 663b3f486f91d8f3589f07a988f8ba2c (MD5)
Previous issue date: 2015 / Resumo: O objetivo deste estudo foi avaliar o efeito da interação de sistemas adesivos multi-mode e cimentos resinosos de polimerização química e dual sobre a superfície da dentina. Quarenta terceiros molares humanos não cariados foram separados em 5 grupos (n=8). Uma superfície plana em dentina foi obtida para cada dente. Blocos de 3,0x12x12 mm de resina composta indireta (Lava Ultimate) foram jateados com partículas óxido de alumínio e cimentados na superfície de dentina, formando os seguintes grupos: I- All Bond Universal fotoativado (AB)/C&B Bond Cement (CB); II- Scotchbond Universal fotoativado (SBU)/RelyXUltimate químico (RXU); III- SBU fotoativado/RXU fotoativado, IV- SBU químico/RXU fotoativado, V- SBU químico /RXU químico. Após a cimentação, os dentes foram mantidos em umidade relativa a 37?C por 24 horas. Os dentes foram seccionados para obter palitos de aproximadamente 0,8 mm². Os espécimes foram posicionados na máquina de ensaio universal EZ-Test para o ensaio de resistência de união com uma velocidade de 0,5 mm/min. Os dados foram estatisticamente analisados por ANOVA um fator e Teste de Fisher's PLSD (?=0,05). Os modos de fratura foram analisados e classificados em microscópio eletrônico de varredura. Para análise das interfaces dentina/adesivo/cimento, cinco espécimes de cada grupo foram corados com Rodamina B a 1% por uma hora e analisados em microscópio confocal de varredura a laser. Nenhuma diferença estatística de resistência da união (MPa) foi observada entre os grupos: I- 59,9 (9,3); II- 57,6 (15,9); III- 63,9 (12,7) e IV- 53,7 (13,9), e todos foram diferentes estatisticamente do grupo V, que apresentou o menor valor de resistência da união 16,2 (6,4). O modo de fratura coesivo foi predominante na interface entre o adesivo e cimento resinoso em todos os grupos. A análise ultraestrutural sugere a interação entre os sistemas adesivos multi-mode e o cimento resinoso na dentina, quando o adesivo ou o cimento resinoso foi fotoativado. A interação adesiva ocorreu entre os adesivos multi-mode e cimentos resinosos, sempre que o adesivo e/ou o cimento resinoso foi fotoativado / Abstract: This study evaluated the dentin surface interaction effect of multi-mode adhesives on bonding to chemical-cured and dual-cured resin cements. Forty non-carious human third molars were divided into five groups (n=8). A flat dentin surface was created for each tooth. Indirect resin composite block 3,0x12x12 mm (Lava Ultimate) were sandblasted with aluminum oxide particles and cemented to the dentin surface following the treatment groups: I- All Bond Universal light-cured/C&B Bond (self-cured cement), II- Scotchbond Universal (SBU) light-cured/RelyX Ultimate (RXU) self-cured, III- SBU light-cured/RXU light-cured, IV - SBU no light-cured/RXU light-cured and V- SBU no light-cured/RXU self-cured. After 24 h, the teeth were sectioned into beans to produce a cross-sectional area of 0.8 mm². Specimens of each group were individually mounted on a jig and placed on a tensile testing universal machine. A tensile force was applied at a 0.5mm/min cross-speed. The bond strength was recorded and failure modes were classified using scanning electron microscopy. In order to observe dentin/adhesive-cement interface, selected beans from each group were stained with 0.1% Rodhamine B for 1 h and analyzed using Confocal Laser Scanning Microscopy. Statistical analysis was performed using ANOVA and Fisher¿s PLSD test (?=0.05). For bond strength (MPa) no statistical difference of was observed among the groups: I - 59.9 (9.3); II- 57.6 (15.9); III - 63.9 (12.7) and IV- 53.7 (13.9). Group V showed statistical lower average value 16.2 (6.4) compared with all others groups. Cohesive failure modes occurred predominately along of adhesive and resin cement to all groups. The ultrastructural observation suggested the dentin surface interaction between multi-mode adhesives and resin cement when the adhesive or resin cement was light-cured. The adhesive interaction occurred between multi-mode adhesive systems and resin cements whenever the adhesive and/or resin cement was light-activated / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288149 |
| Date | 27 August 2018 |
| Creators | Guimarães, Isadora Rabêlo, 1985- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Goes, Mario Fernando de, 1954-, Francci, Carlos Eduardo, Naufel, Fabiana Scarparo, Correr, Americo Bortolazzo, Pascon, Fernanda Miori |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Multilíngua |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 32 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds