Orientadores: Lourenço Correr Sobrinho, Mário Alexandre Coelho Sinhoreti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-18T00:18:54Z (GMT). No. of bitstreams: 1
Guarda_GuilhermeBottene_M.pdf: 2504078 bytes, checksum: 72f1d754db2ac04524c40271b35d7366 (MD5)
Previous issue date: 2011 / Resumo: O objetivo neste estudo foi investigar o efeito de diferentes tratamentos de superfície, fadiga mecânica e termociclagem na resistência da união à microtração da cerâmica IPS e.max (Ivoclar) e do cimento resinoso de ativação dupla. Métodos: 18 blocos de cerâmica (10 mm de comprimento x 7 mm de largura x 3 mm de espessura) foram confeccionados e divididos em 6 grupos (n=3): Grupos 1, 2 e 3 - jateamento por 5 segundos com partículas de óxido de alumínio de 50?m; Grupos 4, 5 e 6 - condicionamento com acido hidrofluorídrico à 10% por 20 segundos. O silano Rely X Ceramic Primer foi aplicado sobre todos os espécimes e seco por 5 minutos. Após, os blocos de cerâmica foram unidos à blocos de compósito restaurador Tetric N-Ceram (Ivoclar-Vivadent) com cimento resinoso RelyX ARC (3M ESPE), sob carga estática de 500 gf por 2 minutos. O excesso de cimento foi removido com micropincel e fotoativado por 160 segundos (40 s cada face) com um aparelho de LED (UltraLume 5, Ultradent). Os espécimes dos grupos 1 e 4 foram armazenados em água destilada a 37°C por 24 h. Nos grupos 2 e 5, os espécimes foram submetidos a 3.000 ciclos térmicos entre 5°C e 55°C. Para os grupos 3 e 6, os espécimes foram submetidos ao ensaio de fadiga mecânica por 100.000 ciclos com 2 Hz. Os espécimes foram seccionados perpendiculares a área de união para obtenção de palitos com área seccional de 1mm2 (25 palitos por grupo) e submetidos ao ensaio de resistência de união à microtração em máquina de teste universal (EZ Test - Shimadzu) com velocidade de 0,5 mm/min. Foi utilizado para verificar o padrão de fratura uma lupa estereoscópica (Olympus) com aumento de 40x. Os dados foram submetidos à Análise de Variância de 2 fatores e ao teste de Tukey (p<0,05). Os valores de resistência de união à microtração (MPa) foram: 26,9 ± 6,9, 22,2 ± 7,8 e 21,2 ± 9,1 para os Grupos 1 a 3 e 35,0 ± 9,6, 24,3 ± 8,9 e 23,9 ± 6,3 para os Grupos 4 a 6. O grupo controle submetido ao teste de fadiga e termociclado mostrou predominância de padrão de fratura adesiva para o tratamento de superfície com acido hidrofluorídrico a 10% e padrões adesiva e mista para tratamento de superfície com 50um de oxido de alumínio. Concluindo a fadiga e a termociclagem diminuíram significantemente a resistência de união à microtração para ambos os tratamentos de superfície das cerâmicas comparada ao grupo controle. Condicionamento com acido hidrofluorídrico a 10% aumentou a resistência de união à microtração para o grupo controle / Abstract: The aim of this study was to investigate the effect of surface treatments, mechanic fatigue and thermocycling tested on the microtensile bond strength of the ceramic IPS e.max Press (Ivoclar Vivadent) luted with dual-cured resin cement. Eighteen ceramic bars (10mm length x 7mm width x 3.0mm thickness) were fabricated, and divided into 6 groups (n=3): Groups 1, 2 and 3 - air particle abraded for 5 s with 50?m aluminum oxide particles; Groups 4, 5 and 6 - acid etched with 10% hydrofluoric acid for 20 s. Coupling agent silane was applied on to all bond surface specimens and allowed to dry for 5 s and the ceramic bars were bonded to a block of composite resin Tetric N-Ceram (Ivoclar-Vivadent) with Rely X ARC (3M ESPE) resin cement and placed under a 500 g static load for 2 min. The cement excess was removed with a disposable microbrush and 40 s light-activation (four activations) were performed using a LED curing unit (UltraLume LED 5, Ultradent). The specimens of the groups 1 and 4 were stored in distilled water at 37°C for 24 hours, groups 2 and 5 were submitted to 3,000 thermocycles between 5°C and 55°C and groups 3 and 6 submitted to a fatigue test for 100,000 cycles with 2 HZ. Specimens were sectioned perpendicular to the bonding area to obtain 1mm2 sectional area beams (25 beams per group) and submitted to a microtensile bond strength test in a universal testing machine (EZ Test - Shimadzu), at a crosshead speed of 0.5mm/min. The fracture specimens were observed under optical microscopy (Olympus) at a 40x magnification. Data were submitted to ANOVA and Tukey's test (p?0.05). Results: The microtensile bond strength values (MPa) were: 26.9 ± 6.9, 22.2 ± 7.8 and 21.2 ± 9.1 for G1-G3 and 35.0 ± 9.6, 24.3 ± 8.9 and 23.9 ± 6.3 for G4-G6. The control group, fatigue tested and thermocycled groups showed a predominance of failure adhesive for surface treatment with 10% hydrofluoric acid and adhesive and mixed for surface treatment with 50 ?m Al2O3. In conclusion the fatigue and thermocycling decreased significantly the microtensile bond strength for both ceramic surface treatments compared to control groups. Etching with 10% hydrofluoric acid increased the microtensile bond strength for the control group / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289605 |
| Date | 18 August 2018 |
| Creators | Guarda, Guilherme Bottene, 1987- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Sinhoreti, Mário Alexandre Coelho, 1969-, Correr Sobrinho, Lourenço, 1960-, Borges, Gilberto Antonio, Consani, Simonides |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 46 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds