Previous issue date: 2006-04-20 / A presença de óleo na água produzida durante a extração de petróleo, causa sérios problemas tanto ao ser descartada no meio ambiente como ao ser reinjetada nos
poços produtores de petróleo. Os métodos convencionais utilizados na separação
óleo/água não conseguem limpar toda a água com eficiência e baixo custo. Assim
sendo, a busca por novas alternativas para solucionar este problema foi a motivação
principal deste trabalho, sendo este parte integrante de uma série de pesquisas,
financiadas pela Agência Nacional de Petróleo (ANP), que visa otimizar todas as etapas
de produção de petróleo. Assim o objetivo deste trabalho foi produzir membranas
cerâmicas visando a sua aplicação na separação óleo/água. Inicialmente foram obtidos
dois tipos de membranas tubulares de alumina, denominadas tipo 1 e tipo 2, com
diferentes tamanhos de poros de aproximadamente 0,9\im e 15,5nm e com eficiências
mínimas de aproximadamente 97,5% e 93,8%, respectivamente. Porém a membrana
tipo 2 apresentou um fluxo 40 vezes maior que a membrana tipo 1. Assim, visando
melhorar mais ainda o desempenho da membrana tipo 2 depositou-se sobre a mesma
uma camada fina de zircônia, de forma que pudesse melhorar sua eficiência sem alterar
significativamente seu fluxo. O pó de zircônia foi obtido com sucesso pelo método
Pechini. Com este método foi possível a obtenção da zircônia cristalina cujos tamanhos
de aglomerados indicaram que este material pode ser usado na obtenção de
membranas de ultrafiltração. Para obtenção da camada de zircônia foi preparada uma
suspensão com a zircônia obtida e esta foi depositada na parte interna da membrana
de alumina tipo 2 usando a técnica de deposição "dip coating". A camada de zircônia
formada apresentou uma espessura de 23,9 ^im, um fluxo superior a membrana de
alumina tipo 1 e uma eficiência mínima de 97,8%. Para todas as membranas obtidas, a
concentração de óleo no permeado foi abaixo de 7 ppm, usando concentração máxima
de 1000 ppm na alimentação. A água permeada através das membranas estudadas se
enquadraram nas especificações para uso na reinjeção e no descarte. / The presence of oil in water produced during the petrol extraction can cause serious
problems during the discharge in the environment as well as in the re-injection in the oil
well. The conventional methods used to remove oil from water can not clean with
efficiency and low cost. So, the search for new alternatives to solve this problem is the
motivation of this work. This study is part of a series of researches supported by Agência
Nacional de Petróleo (ANP), with the aim to optimize ali the steps in the oil production.
The aim of this work is to make ceramic membrane to be applied in the oil/water
separation. Firstly, it was prepared two types of tubular alumina membranes, called type
I and type 2, with different pore size of approximately 0.9nm and 15, 48nm, respectively.
The minimal efficiency of these membranes was approximately 97.5% and 93.8% for
membrane type I and type 2, respectively. However, the membrane type 2 shown a flux
40 times greater than the membrane type 1. To improve the use of the membrane type 2
it was coating the internai surface with a thin layer of zircônia to get better efficiency
without to decrease the flux. The zircônia powder was prepared with success by Pechini
method and it was obtained a crystalline zircônia with agglomerates that indicate the use
to make ultrafiltration membranes. To obtain the zircônia layer it was prepared
dispersion and deposited in the internai surface of the membrane type 2 by dip coating
technique. The zircônia layer presented a thickness of 23.88}im, a flux grater than the
alumina type 1 and a minimal efficiency of 97.8%. Ali studied membrane presented oil
content in permeate below 7ppm, using a maximum concentration of lOOOppm in the
feed tank. The permeate water through the studied membranes is in agreement with the
norms to be discharge in the environment or to be re-injected in the oil well. / PRH 25.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/2005 |
Date | 17 October 2018 |
Creators | MAIA, Divanira Ferreira. |
Contributors | LIRA, Hélio de Lucena., VIEIRA, Lucianna da Gama Fernandes., COSTA, Ana Cristina Figueiredo de Melo., OLIVEIRA, João Bosco Lucena de., BARBOSA SOBRINHO, Ariosvaldo., OLIVEIRA, Djane de Fátima. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Relation | Agência Nacional do Petróleo - ANP. |
Page generated in 0.0068 seconds