Dissertação (mestrado)—Universidade de Brasília, Faculdade em Ciências da Saúde, Programa de Pós-Graduação em Ciências da Saúde, 2013. / Submitted by Albânia Cézar de Melo (albania@bce.unb.br) on 2013-11-19T15:44:37Z
No. of bitstreams: 1
2013_MarcelaBatistaPereiraCarvalho.pdf: 19426211 bytes, checksum: dbf19bbb4b0468de7b3f32a7979dd79e (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2013-12-04T10:33:26Z (GMT) No. of bitstreams: 1
2013_MarcelaBatistaPereiraCarvalho.pdf: 19426211 bytes, checksum: dbf19bbb4b0468de7b3f32a7979dd79e (MD5) / Made available in DSpace on 2013-12-04T10:33:26Z (GMT). No. of bitstreams: 1
2013_MarcelaBatistaPereiraCarvalho.pdf: 19426211 bytes, checksum: dbf19bbb4b0468de7b3f32a7979dd79e (MD5) / O objetivo do presente estudo foi avaliar a resistência de união de bráquetes metálicos e cerâmicos à superfície cerâmica, analisando dois tempos de fotoativação com aparelho LED (light emitting diode). O ensaio de resistência de união foi realizado em bráquetes de aço inoxidável (Morelli), cerâmicos monocristalinos (Inspire ICE) e cerâmicos policristalinos (InVu). Os discos cerâmicos (IPS Empress Esthetic) incluídos em cilindros de resina acrílica foram condicionados com ácido fluorídrico gel a 10% por 60 segundos. Após a aplicação de silano, por 30 segundos, os bráquetes foram colados seguindo o protocolo recomendado para o compósito Transbond XT. Os corpos-de-prova, para cada tipo de bráquete, foram distribuídos aleatoriamente em 2 grupos (n=15) conforme o tempo de fotoativação,
de 20 e 10 segundos, usando o aparelho LED Bluephase. Todos os corpos-de-prova
foram armazenados a 37°C e 100% de umidade por 24 horas, posteriormente,
termociclados (1000 ciclos, de 5°C à 55°C) e retornaram ao ambiente úmido de
armazenamento. O teste de cisalhamento foi realizado após 24 horas na máquina
universal de ensaio a uma velocidade de 1 mm/min. Em seguida, o Índice
Remanescente de Adesivo (IRA) foi avaliado. Os dados foram submetidos à Análise
de Variância e ao teste de Tukey (5%). Todos os bráquetes fotoativados por 20
segundos apresentaram valores de resistência de união significativamente (p<0,05)
superiores aos bráquetes fotoativados por 10 segundos. Os bráquetes cerâmicos
monocristalinos apresentaram valores de resistência de união significativamente
(p<0,05) superiores aos bráquetes cerâmicos policristalinos e de aço inoxidável,
sendo estes, estatisticamente semelhantes (p>0,05) quando fotoativados por 20
segundos. Para o tempo de fotoativação de 10 segundos, os bráquetes cerâmicos
policristalinos apresentaram valores superiores (p<0,05) aos de aço inoxidável.
Enquanto nos grupos de 20 segundos de tempo de fotoativação, o escore 1 (IRA) foi
observado com predominância para os bráquetes de aço inoxidável e cerâmicos
monocristalinos, e o escore 3 para o bráquete cerâmico policristalino, nos grupos de
10 segundos, o bráquete cerâmico monocristalino apresentou predominância do
escore 1, e escore 3 para os bráquetes de aço inoxidável e cerâmicos policristalinos.
Pôde-se concluir que o tempo de fotoativação teve influência significativa na resistência de união de bráquetes metálicos e cerâmicos à superfície cerâmica e que os bráquetes cerâmicos monocristalinos apresentaram os maiores valores de
resistência de união. ______________________________________________________________________________ ABSTRACT / The aim of this study was to evaluate the bond strength of metallic and ceramic brackets bonded to ceramic, by testing two photoactivation times using a LED (light emitting diode) curing unit. Bond strength testing was performed on stainless steel brackets (Morelli), monocrystalline ceramic brackets (Inspire ICE), and polycrystalline ceramic brackets (InVu). Disc-shaped-ceramic specimens (IPS Empress Esthetic) embedded in acrylic resin blocks were etched with 10% hydrofluoric acid gel for 60
seconds. After application of silane for 30 seconds, brackets were bonded following
the protocol recommended for Transbond XT. Specimens for each bracket type were
assigned to two groups (n=15), according to the photoactivation times: 20 seconds or
10 seconds, using a Bluephase LED unit. All specimens were stored at 37°C and
100% relative humidity for 24 hours, then thermocycled (1,000 cycles, 5°C to 55°C),
and they returned to the humid storage conditions. Shear bond testing was carried out after 24 hours with a universal testing machine at a crosshead speed of 1-mm/min. Adhesive Remnant Index (ARI) scores were evaluated. Data were subjected to two-way ANOVA and Tukey's test. All bracket types photoactivated for 20 seconds showed significantly (p<0.05) higher bond strength compared to specimens photoactivated for 10 seconds. Monocrystalline brackets showed
significantly (p<0.05) higher bond strength compared to polycrystalline and stainless
steel brackets, which are statistically similar (p>0,05) when photoactivated for 20 seconds. For 10 seconds photoactivation time, the polycrystalline ceramic brackets
showed higher values (p<0.05) than stainless steel brackets. For the 20 second photoactivation time group, an ARI score 1 was observed with predominance for SS
and monocrystalline brackets, and score 3 for polycrystalline brackets; for the 10
second photoactivation time group, an ARI score 1 was observed with predominance
for the monocrystalline brackets, and score 3 for stainless steel and polycrystalline brackets. In conclusion, photoactivation time had significant influence on the bond strength of metallic and ceramic brackets bonded to a ceramic surface, and monocrystalline brackets showed the highest bond strength values.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/14758 |
| Date | 28 August 2013 |
| Creators | Carvalho, Marcela Batista Pereira de |
| Contributors | Garcia, Fernanda Cristina Pimentel |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
| Rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess |
Page generated in 0.0136 seconds