Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-08T12:43:19Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_CompositoArgamassaCimento.pdf: 6622862 bytes, checksum: e349e7437866547d6f36bd348b74718a (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-18T13:12:34Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_CompositoArgamassaCimento.pdf: 6622862 bytes, checksum: e349e7437866547d6f36bd348b74718a (MD5) / Made available in DSpace on 2014-06-18T13:12:34Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_CompositoArgamassaCimento.pdf: 6622862 bytes, checksum: e349e7437866547d6f36bd348b74718a (MD5)
Previous issue date: 2010 / Neste trabalho, foi desenvolvido um novo material compósito utilizando-se como
matriz a argamassa de cimento reforçado com fibra de sisal a 1% em peso, que
foram cortadas manualmente nos comprimentos de 15 mm e 25 mm utilizadas sem
tratamento superficial utilizando-se o menor nível possível de processamento
tecnológico nas etapas de fabricação. A pesquisa foi direcionada para estudar os mecanismos de falha desse novo material. Os compósitos foram produzidos com moldagem manual utilizando-se vibrador de imersão para melhor adensamento. Foram confeccionados corpos de prova da matriz pura e do compósito com fibra de
sisal, com entalhes pré definidos, de 1,7 mm, 3,0 mm e 5,0 mm. As propriedades
mecânicas foram avaliadas por ensaio de flexão em três pontos e correlacionadas
com o aspecto fractográfico realizados no Microscópio Eletrônico de Varredura. Os
resultados mostraram que a presença das fibras de sisal, inseridas na pasta de
cimento, provocou restrição à retração plástica da mistura fresca, possivelmente pela
elevada capacidade de absorção de água do reforço fibroso, um incremento na
resistência mecânica e aumento da tenacidade do compósito em relação a matriz
entre as séries de entalhes, diminuindo a tendência de fratura brusca. / In this work, we developed a new composite material using as a matrix of cement
mortar reinforced with sisal fibers to 1% by weight, which were manually cut into
lengths of 15 mm and 25 mm used without surface treatment using the
lowest possible level of technological processes in manufacturing steps. The
research was conducted to study the mechanisms of failure of this new material. The
composites were produced with manual molding using immersion vibrator for better
densification. Specimens were fabricated of the pure base and with the composites
with sisal fiber, with pre-defined slots of 1.7 mm, 3,0 mm and 5,0 mm. The
mechanical properties were evaluated by a bending test at three points and
correlated with the fractographic appearance made in the Scanning Electron
Microscope. The results showed that the presence of sisal fibers, embedded in
cement paste,plastic shrinkage caused restriction of fresh mixture, possibly due to
high water absorption capacity of fibrous reinforcement, an increase in mechanical
strength and increased toughness of the composite over the base between the series
of notches, decreasing the tendency to sudden fracture.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/5094 |
| Date | January 2010 |
| Creators | PERES, Maria das Neves Pontes Barata |
| Contributors | FUJIYAMA, Roberto Tetsuo |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Mecânica, UFPA, Brasil, Instituto de Tecnologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds