Previous issue date: 2004-08-20 / Capes / O objetivo desta pesquisa foi estudar o efeito das técnicas de: a) congelamento nas
temperaturas de -20 °C, -196 °C e -170 °C; b) armazenamento as temperaturas de (-20 °C, -30 °C e -170 °C, e c) do método de descongelamento (temperatura ambiente:
aproximadamente 25 °C e em banho termostatizado: 35 °C) sobre duas amostras de camarão: 1) com exoesqueleto e cabeça e 2) sem exoesqueleto e sem cabeça, por um período de 12 meses de armazenamento. Foram determinados os seguintes parâmetros: a) características físicas (massa, comprimento, espessura e volume); b) cinética de congelamento as temperaturas de -20 °C, -170 °C e -196 °C; c) propriedades termofisicas (densidade, calor específico, difusividade térmica e condutividade térmica); d) características físico-químicas (conteúdo de água, cinzas, proteínas, pH, carboidratos, gorduras, calorias, exsudado e um atributo de textura: dureza); e) caracterização microbiológica (salmonela, coliformes fecais, vibrio parahaemolyticus) e f) avaliação sensorial (sabor, odor, textura e aparência), visando verificar a eficácia das técnicas de congelamento e descongelamento na qualidade do camarão armazenado. Na análise da cinética, as curvas de congelamento obtidas à temperatura de -20 °C para o camarão com exoesqueleto e cabeça e para o filé foram observadas claramente as três fases, ou seja, resfriamento, cristalização e pós-congelamento. Este fato também ocorreu para o camarão com cabeça congelado a -170 °C, já para o filé congelado a -170 °C
não se distinguiu com clareza a fase I da Fase II, ou seja, a fase de resfriamento e a fase de cristalização, fato este atribuído a maior velocidade de congelamento. Nas curvas de
congelamento do camarão com cabeça e filé quando estes foram submetidos ao congelamento por imersão em N2 líquido (-196 °C) também não se observou uma distinção entre as fases de resfriamento e cristalização. Com relação às propriedades termofisicas, a densidade do camarão "fresco" (25 °C) com exoesqueleto e cabeça foi de l,066g/cm3 e do filé foi de l,02g/cm3. Os valores médios do calor específico do camarão com exoesqueleto e do filé "fresco" foram de 0,84 e 0,86 kcal/kg °C, respectivamente e para o camarão com exoesqueleto e filé à temperatura de -170 °C foram de 0,28 kcal/kg °C, 0,31 kcal/kg °C e a -196 °C foram de 0,25 kcal/kg °C e 0,28 kcal/kg °C, respectivamente. A difusividade efetiva média do camarão com exoesqueleto às temperaturas de -20 °C, -170 °C e -196 °C, foi de 9,13 x 10 3 mm2/s; 29 x 10 3 mm2/s; 571,8 x 10 3 mm2/s e para o filé nas mesmas temperaturas foi 9,9 x 10 3 mm2/s; 28,1 x IO"3 mm2/s; 384,3 x IO"3 mm2/s. A condutividade térmica média para o camarão com exoesqueleto às temperaturas de -170°C e -196 °C foi de 0,032 W/m °C e 0,499 W/m °C e para o filé nas mesmas temperaturas foi de 0,029 W/m °C e 0,371 W/m °C, respectivamente. Na caracterização físico-química, tanto nos camarões com cabeça quanto nos filés, congelados e armazenados em vapor de N2 (-170 °C) mantiveram-se inalterados o conteúdo de água, cinzas, proteínas, pH, gorduras e exsudado, durante todo o período de armazenagem. Os resultados das análises microbiológicas dos camarões frescos, depois de congelados e durante os 12 meses de armazenamento, apresentaram ausência de salmonela, de coliformes fecais e vibrio parahaemolyticus. Na avaliação sensorial quanto aos atributos sabor, odor, textura e aparência, os degustadores demonstraram preferência pelas amostras congeladas e armazenadas em vapor de N2, as amostras que tiveram menores índices de aceitabilidade foram às congeladas e armazenadas a -20 °C. Concluiu-se ainda que tanto no sabor, odor e textura, em todos os tratamentos, as médias das notas dos camarões descongelados em banho termostatizado à temperatura de 35 °C foram menores que as descongeladas a temperatura ambiente, todavia, na avaliação da aparência do camarão com exoesqueleto e cabeça, quando descongeladas em banho termostatizado a 35 °C, apresentaram notas mais elevadas que as descongeladas à temperatura ambiente, tal fato é atribuído a astaxantina existente em crustáceos, que quando aquecida dá a cor alaranjada ao camarão. / The objective of this research was to study the effect of techniques of: 1) freezing in
temperatures of-20 °C, -196 °C and -170 °C; 2) storage in temperatures of (-20 °C, -30 °C
and -170 °C, and 3) of unfreezing method ( environmental temperature: approximately 25
°C and in thermostatized bath: 35 °C) on two samples of shrimp: 1) with exoskeleton and
head and 2) without exoskeleton and head, for a period of 12 months of storage. The
following parameters had been determined: 1) physical characteristics (mass, length,
thickness and volume); 2) kinetic freezing of temperatures at -20 °C, -170 °C and -196 °C; 3) thermophysical properties (density, specific heat, thermal diffusivity and thermal
conductivity); 4) physicochemical characteristic (water content, ashes, proteins, pH,
carbohydrates, fats, calories, exuded and an texture attribution: hardness); 5) microbiological characterization (salmonella, fecale coliform, vibrio parahaemolyticus) and 6) sensorial evaluation (flavor, scent, texture and appearance), aiming to verify the effectiveness of freezing and unfreezing techniques in the quality of the stored shrimp. During kinetic analysis, the curves of freezing obtained at the temperature of -20 °C for the shrimp with the head and exoskeleton for the filet, the three phases, or better saying, cooling, crystallization and after-freezing were clearly observed. This fact also occurred for the shrimp with frozen head at -170 °C, on the other hand for the filet at -170 °C, it was not easy to distinguish with clarity phase I from Phase II, in other words, the phases of cooling and crystallization, due to the speed of freezing. At the shrimps with head freezing curve, it was observed that when these were submitted to freezing by immersion in liquid N2 (-196 °C) there was not any distinction between the phases of cooling and crystallization. In relation to the thermophysical properties, the density of fresh shrimp (25 °C) with exoskeleton and head were of l,066g/cm3 and of that of filet was l,02g/cm3. The average values of the specific heat of the shrimp with exoskeleton and fresh filet is of 0,84 and 0,86 kcal/kg °C, respectively and for shrimp with exoskeleton and filet at temperature of -170 °C were of 0,28 kcal/kb °C, 0.31 kcal/kg °C and 196°C were of 0,25 kcal/kg °C and 0,28 kcal/kg °C, respectively. The medium diffusivity effectiveness of the shrimp with exoskeleton at the temperatures of -20 °C, -170 °C and -196 °C, was of 9,13 x 10"3 mm2/s; 29 x 10"3 mm2/s; 571,8 x 10"3 mm2/s and for the filet at the same
temperature was 9,9 x 10"3 mm2/s temperatures was; 28.1 x 10"3 mm2/s; 384,3 x 10"3 mm2/s. The average thermal conductivity for shrimp with exoskeleton at -170 °C and -196 °C was of 0,032 W/m °C and 0,499 W/m °C and for filet at the temperature was of 0,029 W/m °C and 0.371 W/m °C, respectively. For physicist-chemistry characterization, both in shrimps with head as well as that of filet, frozen and stored in N2 vapor (-170 °C) the water content, proteins, pH, fats and exuded remained unchanged during all the period of storage. The results of the microbiological analyses of the fresh shrimps, after been frozen and during 12 months of storage, presented absence of salmonella, fecal coliform and vibrio parahaemolyticus. In the sensorial evaluation as much as flavor, scent, texture and appearance are concerned, the testators demonstrated preference for samples frozen and stored in vapor of N2, the samples with the least acceptability indices were those frozen and stored at -20 °C. It was concluded that in the flavor, scent and texture, in all the treatments, the average notes of defrosted shrimps in thermostatized bath of 35 °C temperature were less than those defrosted at environmental temperature, however, in the evaluation of the appearance of the shrimp with exoskeleton and head, when defrosted at thermostatized bath of 35 °C, presented higher notes than those defrosted at environmental temperature, such facts are attributed to astaxantine existing in crustaceans, which when heated, gives the shrimp that gives the orange color to the shrimp,
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/2003 |
| Date | 17 October 2018 |
| Creators | CASTRO, Alessandra Almeida., PAGANI, Alessandra Almeida Castro. |
| Contributors | CAVALCATI-MATA, Mário Eduardo Rangel Moreira., DUARTE, Maria Elita Martins., FORTES, Mauri., FIOREZE, Romeu., SILVA, Gabriel Francisco da., QUEIROZ, Alexandre José de M. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds