Orientador: Claudia Longo / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Química / Made available in DSpace on 2018-08-18T16:06:49Z (GMT). No. of bitstreams: 1
Santos_ReginaldodaSilva_D.pdf: 4843119 bytes, checksum: 3b7dd1f72628c75da40e0f76317b6cfa (MD5)
Previous issue date: 2011 / Resumo: Nanopartículas de TiO2 foram preparadas por método sol-gel a partir da hidrólise de isopropóxido de titânio, tratamento hidrotérmico (200 °C, 8 h) e calcinação (450 °C, 30 min); amostras de TiO2 dopado com ferro (Fe:TiO2) foram obtidas pela mesma metodologia incluindo nitrato férrico nos precursores (razão molar Fe/Ti de 1, 3 e 5%). Para comparação, investigou-se também uma mistura de a-Fe2O3/TiO2 (Fe/Ti = 4 %). O intervalo de banda proibida, de 3,2 eV para o TiO2, diminuiu de 3,0 para 2,7 eV com o aumento do teor de Fe. Análises por difração de raios X e refinamento Rietveld revelaram que o TiO2 é constituído por anatasa (82 %) e brookita (18 %); para Fe:TiO2, observou-se 30 % de brookita e identificou-se 0,5; 1,0 e 1,2 wt % de hematita nas amostras com Fe/Ti de 1; 3 e 5%. Filmes porosos, com espessura de 1,5 mm, foram depositados em eletrodos de vidro a partir de suspensões com polietilenoglicol e calcinação. Em solução aquosa, irradiados com um simulador solar, os eletrodos apresentaram comportamento de semicondutor tipo-n: para o TiO2, fotopotencial de -0,95 V em circuito aberto e fotocorrente de 0,34 mA cm em 0,8 V; valores muito menores foram observados para Fe:TiO2 e a-Fe2O3/TiO2. O TiO2 também apresentou maior atividade fotocatalítica para degradação de fenol e, quando utilizado como foto-anodo em célula de dois compartimentos, polarizado a + 0,7 V por 4 h, promoveu a oxidação de formiato e a produção de 18 mmol de H2 sobre contra-eletrodo de Pt. Os eletrodos de Fe:TiO2 e a-Fe2O3/TiO2 apresentaram valores menores de corrente, impossibilitando a obtenção de H2 no catodo. Embora as amostras de Fe:TiO2 tenham apresentado maior aproveitamento da luz visível, a inserção do ferro como dopante e a hematita segregada podem dificultar a separação das cargas fotogeradas e o transporte de elétrons através dos contornos de grãos, resultando em menor atividade fotocatalítica nas aplicações decorrentes da conversão de energia solar / Abstract: TiO2 nanoparticles were synthesized by sol-gel method from hydrolysis of titanium isopropoxide followed by hydrothermal treatment (200 °C, 8 h) and annealing (450 °C, 30 min). Fe doped TiO2 (Fe:TiO2) samples were synthesized by similar methodology adding ferric nitrate, with Fe/Ti atomic ratio corresponding to 1, 3 and 5 %. A mixture of a-Fe2O3/TiO2 (with Fe/Ti = 4 at %) was also investigated. The band gap energy, estimated as 3.2 eV for TiO2, gradually ranged from 3.0 to 2.7 eV with increasing iron content. Rietveld refinement of X ray diffraction data revealed that TiO2 consisted of 82 % anatase and 18 % brookite; for Fe:TiO2, brookite increased to 30 % and hematite was also identified (0.5; 1.0 and 1.2 wt % for samples prepared with 1; 3 and 5 % of Fe/Ti). Porous films, 1.5 mm thick, were deposited on transparent electrodes from aqueous suspension with polyethylene glycol and annealing. In aqueous solution, irradiated by a solar simulator, the electrodes exhibited n-type semiconductor behavior: for TiO2 electrode, -0,95 V of photo-potential at open circuit condition and 0,34 mA cm of photocurrent when biased at 0.8 V; much lower values were observed for Fe:TiO2 and a-Fe2O3/TiO2 electrodes. TiO2 film also exhibited higher photocatalytic activity for phenol oxidation than other samples. The electrodes were also used as photo-anodes in a two-compartment electrochemical cell with Pt counter-electrode and HCOONa as hole scavenger. The cell assembled with irradiated TiO2 anode biased at + 0.7 V for 4 h produced 18 mmol of H2 at the cathodic compartment. H2 evolution was not detected and very low currents were observed for Fe:TiO2 or a-Fe2O3/TiO2 photo- anodes. Although Fe:TiO2 samples exhibited higher sunlight harvesting, inserted iron and segregated hematite can hinder the separation of photogenerated charges, as well as the electron transport across the grain boundaries, resulting in lower photocatalytic activity for solar energy conversion / Doutorado / Físico-Química / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/250022 |
| Date | 18 August 2018 |
| Creators | Santos, Reginaldo da Silva |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Longo, Cláudia, 1968-, Zanoni, Maria Valnice Boldrin, Filho, Germano Tremiliosi, Kubota, Lauro Tatsuo, Mayolo, Carlos Manuel Giles Antunes de |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Ciências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds