Previous issue date: 2007 / Capes / O interesse pela preservação dos recursos naturais e a busca pelo desenvolvimento sustentável tem despertado interesse de um grande número de pesquisadores visando obter conhecimento de materiais não convencionais. Entre esses materiais, destaca-se a reciclagem dos resíduos produzidos pela construção civil e pela indústria de beneficiamento de granito, as quais são geradoras de um volume considerável de resíduos, causando grandes impactos ambientais. O principal obstáculo para o uso
generalizado desses materiais está relacionado ao seu comportamento ao longo do tempo. Para que haja confiabilidade nas características tecnológicas de um novo material e sua indicação como nova tecnologia a ser disponibilizada no mercado é fundamental o conhecimento de suas condições de uso e sua durabilidade. Este trabalho tem como objetivo principal estudar a durabilidade das argamassas alternativas incorporadas com resíduos de construção civil e das indústrias beneficiadoras de granitos. Para quantificar a durabilidade dos materiais estudados, foram realizados ensaios de envelhecimento natural e ensaios de envelhecimento acelerado através de ciclos de molhagem e secagem. Assim estes materiais foram expostos a condições que simulam sua utilização, para avaliar a degradação. As propriedades físico-mineralógicas das matérias-primas foram analisadas através dos ensaios de análise granulométrica por difração a laser, área específica pelo método do permeâmetro de Blaine, análise química, análise termodiferencial, análise termogravimétrica e difração de raios X. Verificou-se também a atividade pozolânica desses resíduos através das normas da ABNT. Após o conhecimento das propriedades estudou-se a durabilidade das argamassas para assentamento, utilizando-se percentagens de substituição, em peso, da cal por resíduo reciclado, que variou de 30% a 50%. Determinou-se a influência desses teores de substituição nas resistências à compressão simples. Os corpos de prova confeccionados foram submetidos ao envelhecimento natural e acelerado após 28 dias de cura em água. No envelhecimento natural os corpos de prova foram submetidos aos 60 dias, 90 dias, 120 dias e 180 dias. Para o envelhecimento acelerado através de ciclos de molhagem e secagem, os corpos de prova foram submetidos a 20 ciclos, 30 ciclos, 45 ciclos, 60 ciclos e 90 ciclos. Os resultados evidenciaram que as argamassas incorporadas com resíduos possuem atividade pozolânica. Para o envelhecimento natural evidenciou-se o comprometimento da durabilidade do material após 60 dias com redução no comportamento mecânico, sendo os melhores resultados para os corpos de prova com 30% e 50% de resíduos de construção. No envelhecimento acelerado para os tratamentos adotados, os resultados evidenciaram ação da formação de silicoaluminatos de cálcio e potássio que favoreceram um aumento no comportamento mecânico, e além disso, não foi observado o comprometimento da durabilidade do material. / The preservation of natural resources and search for sustainable development are increase in interest by the researchers with the aim to obtain knowledge of non conventional materials. Among these materials stand out the recycling of residues from civil construction and from granite industry, which are producers of large amount of residues and causing great environmental impacts. The main impediment for the general use of these materials is related to their behavior with the time. To have a confidence in the technological characteristics of a new material and to indicate as a new technology to be used is necessary to know the use conditions and its durability. The aim of this work is to study the durability of the alternative mortar incorporated with residues from civil construction and from granite industry. To quantify the durability of the studied materials, it was made test of natural and accelerated weathering through wetting and drying cycles. The materials were submitted to conditions that simulated their use to evaluate their degradation. The physical and mineralogical properties of the raw materials were analyzed by granulometric size by laser diffraction, specific surface area, Blaine air permeability, chemical analyzes, differential thermo analyzes, thermogravimetric analyzes and X-ray diffraction. Also it was measured the pozolanic activity of the residues according to the Brazilian norms. After it was studied the durability of the mortar by using percentages of substitutions, w/w%, of lime by recycling residue. The amount changed from 30 to 50%. It was measured the influence of these amounts in the simple compression strength. The samples were submitted to natural and accelerated weathering after 28 days of cure in water. In the natural weathering the samples were submitted to 60, 90, 120 and 180 days. To the accelerated weathering, the samples were submitted the 20, 30, 45, 60 and 90 cycles of wetting and drying. The results that the mortars incorporated with residues have pozolanic activity. The natural weathering cause a compromise in the durability of the material after 60 days with a decrease in the mechanical behavior and the best results occur to the sample with 30% and 50% of residue. In the accelerated weathering, the results show indicate the formation of calcium and potassium aluminosilicates that can give an increase in the mechanical behavior, however, it was not observed a compromise in the durability of the material.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1874 |
| Date | 02 October 2018 |
| Creators | FARIAS FILHO, João de. |
| Contributors | NEVES, Gelmires de Araújo., FERREIRA, Heber Carlos., OLIVEIRA, Djane de Fátima., LUCENA, Luciana de Figueiredo Lopes., NASCIMENTO, José Wallace Barbosa do., LIRA, Hélio de Lucena., BEZERRA, Ulisses Targino. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.004 seconds