Aceleração da nitretação iônica pela nanoestruturação de superfícies metálicas induzidas por bombardeio com gases nobres / Entanglement and matrix product states in quantum phase transitions

Orientador: Fernando Alvarez / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-11T13:13:51Z (GMT). No. of bitstreams: 1
OchoaBecerra_ErikaAbigail_D.pdf: 5724102 bytes, checksum: c62c9d58c0f942077a9cfd1ba1d75d94 (MD5)
Previous issue date: 2007 / Resumo: A presente tese trata o estudo as propriedades físicas resultantes em sistemas metálicos com superfícies nanoestrutura as pelo bombardeio com gás nobre e posteriormente nitretados com técnicas basea as em plasma. A busca e novas condições e tratamento que aumentem a velocidade a ifusão o nitrogênio é e grande interesse para a modificação e superfícies metálicas. Para isto, o pré-tratamento a superfície o material, através e métodos e refinamento os grãos a superfície, é fundamental na melhora a incorporação e nitrogênio no material. Este trabalho visa o estudo e sistemas basea os em ferro, especialmente aços e interesse tecnológico, com superfícies refinadas até a escala nanométrica e submeti os ao processo e nitretação. Neste caso, a superfície a amostra considera a po e ser nanoestrutura a por bombar eiodiônico com gases nobres ("atomic attrition") e posteriormente nitreta a usan o feixe e íons. O material escolhi o para o presente trabalho é o aço enomina o AISI 4140, um aço e baixa liga. O tratamento superficial ("atomic attrition") prévio ao processo e nitretação possibilita o aumento o conteúdo e nitrogênio em profundidade permitindo ainda que a nitretação possa ser realizada a temperaturas relativamente mais baixas (T ~ 300 °C). A caracterização as amostras pré-trata as e/ou nitretadas é realizada in-situ por espectroscopia e elétrons fotoemitidos garantindo condições únicas para o estudo o fenômeno e nanoestruturação e sua influência na ifusão o nitrogênio. Outras técnicas usuais e caracterização utiliza as foram a nano-in entação, raios-X (em nosso grupo e no LNLS) e microscopia óptica e eletrônica. Os resultados indicam o sucesso na nanoestruturação a superfície as amostras pela formação e caminhos e rápida difusão e nitrogênio e assim aumentando a dureza resultante o material / Abstract: The present thesis treats the stu y of the physical resultant properties in metallic systems with nano-structure surfaces by the bombar ment with noble gas an subsequently nitri e with techniques base on plasma. The search for new con itions of treatment that increase the spee of diffusion of the nitrogen is of great interest for the modification of metal surfaces. For this, the pre-treatment of the material surface, through methods of refinement of the grains at the surface, is fundamental in the improvement of the incorporation of nitrogen in the material. This work aims at the study of systems base on iron, especially steels of technological interest, with surfaces refine up to the nanometric scale an subjecte to the nitriding process. In this case, the surface of the considere sample can be nano - structure by ionic bombar ment with noble gases ("atomic attrition") an subsequently nitride using bundle of ions. The material chosen for the present work is the steel AISI 4140, a steel of low alloy. The superficial treatment ("atomic attrition") prior to the process of nitriding makes possible the increase of the content of nitrogen in epth allowing still that nitriding could be carrie out to relatively lower temperatures (T ~ 300 °C). The characterization of the samples pre-treate an / or nitride is carrie out in-situ by spectroscopy of photo-emitte electrons guaranteeing singular conditions for the study of the phenomenon of nano-structuring an its influence in the nitrogen iffusion. Other usual techniques of characterization use were nano - in dentation, X-rays (in our group an at LNLS), optical an electronic microscopy. The results indicate the success in the nano - structuring of the sample surface for the formation of ways of quick diffusion of nitrogen an so increasing the resultant har ness of the material / Doutorado / Física da Matéria Condensada / Doutor em Ciências

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/277721
Date26 October 2007
CreatorsOchoa Becerra, Erika Abigail
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Alvarez, Fernando, 1946-, Junior, Clodomiro Alves, Zanatta, Antonio Ricardo, Cardoso, Lisandro Pavie, Kleinke, Maurício Urban
Publisher[s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format140p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds