Relationships between thermomechanical processing, microstructure and mechanical properties of the beta metastable Ti-LCB alloy

Despite of their costs, titanium alloys are often used for structural applications due to their high performance to density ratio that allows the manufacturers to reach the aimed mechanical properties. Users are more and more inclined to turn towards the ƓÒ-metastable alloys since they provide a wider range of processing conditions, very attractive corrosion resistance and higher strength levels in comparison to the ƓÑƓyƓÒ alloys. Nevertheless, these alloys present a high sensitivity to the variation in the applied heat- or thermomechanical treatment influencing the final mechanical properties. That is why the understanding of the relationships existing between these heat- or thermomechanical treatments and the corresponding modifications of the microstructures, as well as the influence of several characteristics of the microstructure on the mechanical properties under static and cycling loading conditions is of primary importance. This research allows to characterise and to better understand the precipitation and growth sequences of the ƓÑ phase in the Ti-LCB alloy during classical heat- and thermomechanical treatments in order to be able to predict the microstructure resulting from a defined treatment. Furthermore, to improve the understanding of the relationships existing between the manufacturing process, the corresponding microstructures modifications, and the mechanical properties, tensile tests are performed on the different microstructures and microstructural parameters playing an important role on the static properties are identified. Microstructural features governing the static fracture process in two different microstructures are determined by using a micromechanical model based on a physical understanding of the mechanisms of damage. Finally, the crack initiation and the first stage of crack propagation under high cycle fatigue conditions are investigated at a local scale on two different microstructures.

Identiferoai:union.ndltd.org:UCL/oai:ucl.ac.be:ETDUCL:BelnUcetd-01042008-185446
Date14 December 2007
CreatorsLenain, Astrid
PublisherUniversite catholique de Louvain
Source SetsUCL
LanguageEnglish
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://edoc.bib.ucl.ac.be:81/ETD-db/collection/available/BelnUcetd-01042008-185446/
Rightsrestricted, J'accepte que le texte de la thèse (ci-après l'oeuvre), sous réserve des parties couvertes par la confidentialité, soit publié dans le recueil électronique des thèses UCL. A cette fin, je donne licence à l'UCL : - le droit de fixer et de reproduire l'oeuvre sur support électronique : logiciel ETD/db - le droit de communiquer l'oeuvre au public Cette licence, gratuite et non exclusive, est valable pour toute la durée de la propriété littéraire et artistique, y compris ses éventuelles prolongations, et pour le monde entier. Je conserve tous les autres droits pour la reproduction et la communication de la thèse, ainsi que le droit de l'utiliser dans de futurs travaux. Je certifie avoir obtenu, conformément à la législation sur le droit d'auteur et aux exigences du droit à l'image, toutes les autorisations nécessaires à la reproduction dans ma thèse d'images, de textes, et/ou de toute oeuvre protégés par le droit d'auteur, et avoir obtenu les autorisations nécessaires à leur communication à des tiers. Au cas où un tiers est titulaire d'un droit de propriété intellectuelle sur tout ou partie de ma thèse, je certifie avoir obtenu son autorisation écrite pour l'exercice des droits mentionnés ci-dessus.

Page generated in 0.0022 seconds