Because of the anticipated high demand for Indium, ongoing growth of CIGS technology may be limited. Kesterite materials, which replace In with a Zn/Sn couple, are thought to be a solution to this issue. However, efficiencies are still below the 10% level, and these materials are proving to be complex. Even determination of the bandgap is not settled because of the occurrence of secondary phases. We use a film growth process, 2SSS, which we believe helps control the formation of secondary phases. Under the right growth conditions we find 1/1 Zn/Sn ratios and XRD signatures for Cu2ZnSnSe4 with no evidence of secondary phases. The optical absorption profile of our films is also a good match to the CIS profile even for films annealed at 500° C. We see no evidence of phase separation. The effect of intentional variation of the Zn/Sn ratio on material and device properties is also presented.
| Identifer | oai:union.ndltd.org:USF/oai:scholarcommons.usf.edu:etd-4200 |
| Date | 01 January 2011 |
| Creators | Bendapudi, Sree Satya Kanth |
| Publisher | Scholar Commons |
| Source Sets | University of South Flordia |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Graduate Theses and Dissertations |
| Rights | default |
Page generated in 0.002 seconds