The superior properties of carbon nanotubes (CNTs) are best manifest in bulk materials when the CNTs are organized in tandem and embedded in a continuous matrix. Decorating the CNTs with magnetic nanoparticles (MNPs) facilitates their expedient organization with a magnetic field. One of the most convenient methods for their decoration is to first treat the CNTs with oxidative acids, and then coprecipitated MNPs in situ. This method results magnetized CNTs that are covalently functionalized with the MNPs. The associated destruction in the CNTs required running a comparative study of this protocol to identify the influence of the acid treatment on the decoration of multiwalled CNTs (MWNTs). Further, we explore means to tune the physical properties of these magnetized CNTs (mMWNTs) by varying the (1) MNP material composition, and (2) MNP:MWNT (w/w) magnetization weight ratio (γ). The resulted composite materials (mMWNTs) are utilized to synthesize a novel and hitherto unreported class of colloidal suspensions (MCCs) for which the dispersed phase, which consists of MWNTs decorated with MNPs, is both magnetoresponsive and electrically conductive. Synthesis of the dispersed phase merges processes for producing ferrofluids and mMWNTs. Later, these MCCs are adapted and engineered to produce a biological ink containing MWNTs that are twice functionalized, first with MNPs and thereafter with the anti-c-Myc monoclonal antibodies (Abs). The ink is pipetted and dynamically self-organized by an external magnetic field into a dense electrically conducting sensor strip that measures the decrease in current when a sample containing c-Myc antigens (Ags) is deposited on it. On the other side, a nondestructive methods to magnetize MWNTs and provide a means to remotely manipulate them is through the electroless deposition of magnetic nickel nanoparticles on their surfaces. The noncovalent bonds between Ni nanoparticles and MWNTs produce a Ni-MWNT hybrid material (NiCH) that is electrically conductive and has an enhanced magnetic susceptibility and elastic modulus. Raising γ (Ni:MWNT weight ratios) increases the coating layer thickness, which influences the NiCH magnetic properties and tunes its elastic modulus. The NiCH was used to fabricate Ni-MWNT macrostructures and tune their morphologies by changing the direction of an applied magnetic field. Leveraging the hydrophilic Ni-MWNT outer surface, a water-based conductive ink was created and used to print a conductive path that had an electrical resistivity of 5.9 Ωm, illustrating the potential of this material for printing electronic circuits. Further, the NiCHs are introduced into an epoxy matrix at low 0.25-1% volume fractions and aligned along the direction of an applied magnetic field, which produces anisotropic bulk properties. However, nanoparticles aligned in perpendicular directions in sequential layers result in an effectively isotropic composite material. Furthermore, the subsequent annealing of the NiCH in the presence of air oxidizes nickel to nickel oxide whereas carbon is released as gaseous carbon dioxide, which leads to a novel approach for the fabrication of nickel oxide nanotubes (NiONTs) based on MWNTs as a sacrificial template. New chelating polyelectrolytes are used as dispersing agents to achieve high colloidal stability both for NiCH and NiONTs. A gravimetric specific capacitance of 245.3 F g-1 and areal capacitance of 3.28 F cm-2 at a scan rate of 2 mV s-1 is achieved with an electrode fabricated using nickel oxide nanotubes as the active element with a mass loading of 24.1 mg/cm2. / Thesis / Doctor of Philosophy (PhD) / The superior properties of carbon nanotubes (CNTs) are best manifested in bulk materials when the CNTs are organized axially and in tandem, and embedded in a continuous matrix. Decorating the CNTs with magnetic nanoparticles (MNPs) facilitates their organization through “action from a distance” with a magnetic field. The attachment of MNPs to the surfaces of CNTs can be realized through covalent or non-covalent (i.e. physical) bonding. This work develops both methodologies to investigate how the physical properties of magnetized CNT (mCNT) can be tuned and produce new CNT-based nanostructures for particular applications. First, mCNTs are utilized to synthesize a hitherto unreported class of colloidal suspensions based on which a magnetic bio-ink is fabricated to print a fast-response biological sensor. Next, nickel-coated CNTs prepared using electroless deposition are used in the form of a filler at low volume fractions in an epoxy matrix, where they are aligned along multiple-direction using a magnetic field, producing either anisotropic or isotropic bulk properties on demand. Finally, subsequent annealing of nickel-coated CNTs in air oxidizes nickel to nickel oxide while carbon is released in the form of gaseous carbon dioxide. This leads to another novel approach for the fabrication of nickel oxide nanotubes, which are demonstrated to be an alternate viable material to fabricate electrodes for use in supercapacitors.
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/21958 |
| Date | 11 1900 |
| Creators | Abdalla, Ahmed Mohamed Sayed Ahmed |
| Contributors | Puri, Ishwar K., Engineering Physics |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.002 seconds