Titanium has been widely used for dental implants, and in particular, roughened titanium surfaces have provided a means for increasing bone apposition and strengthening the implant-to-bone interface. Finding a way to further increase osseointegration is important because there is a significant clinical benefit to patients if a stable anchor can be established instead of anchoring orthodontic hardware to the molars. In this study, the effect of recombinant human bone morphogenetic protein-2 (rhBMP-2) on the ability of temporary anchorage devices (TADs) to osseointegrate was investigated. The temporary anchorage devices (TADs) used in this study were manufactured from commercially pure titanium and divided into 2 types of treatments: (1) sandblasted and acid-etched (i.e. the control) and (2) sandblasted and acid-etched treated with Medtronic INFUSE® Bone Graft (recombinant human bone morphogenetic protein-2 placed on an absorbable collagen sponge). The implants were placed on the cranial bones of 10 adult male Sprague-Dawley rats. The rats were euthanized by carbon dioxide asphyxiation 6 weeks following surgery for histological examination and biomechanical testing. The results from visual inspection and biomechanical testing showed that the sandblasted and acid-etched TADs treated with rhBMP-2 promoted better osseointegration than TADs that were only sandblasted and acid-etched. Specifically, surface modified TADs treated with rhBMP-2 on bottom showed an increased surface coverage by bone and an increase in the adhesion strength at the TAD-to-bone interface.
| Identifer | oai:union.ndltd.org:CALPOLY/oai:digitalcommons.calpoly.edu:theses-1347 |
| Date | 01 May 2010 |
| Creators | Cruz, Eden E |
| Publisher | DigitalCommons@CalPoly |
| Source Sets | California Polytechnic State University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Master's Theses |
Page generated in 0.0031 seconds