Previous issue date: 2006 / Resumo: O objetivo deste trabalho foi preparar e avaliar o comportamento de blendas ternárias PPO/AES/PS com relação aos aspectos de miscibilidade, compatibilidade, propriedades mecânicas e estabilidade fotoquímica, bem como comparar estas propriedades com as das blendas PPO/HIPS. Neste trabalho as blendas ternárias PPO/AES/PS foram elaboradas a partir da mistura mecânica no estado fundido de PS, poliestireno, PPO, poli(2,6-dimetil-1,4-óxido de fenileno) e AES, um elastômero termoplástico obtido pela enxertia de SAN, poli(estireno-co-acrilonitrila) no EPDM, poli(etileno-co-propileno-co-5-etilideno-2-norboneno). Foram preparadas três séries de blendas ternárias, contendo respectivamente 40, 50 e 60 % de PPO. Em cada série variou-se a fração mássica do AES de 10, 15, 20 e 30 %. Para fins de estudos comparativos, também foram preparadas as blendas binárias PPO/AES, PPO/PS e AES/PS na composição 50/50 e as blendas binárias de PPO e poliestireno de alto impacto, HIPS, contendo o mesmo teor de PPO que as blendas ternárias. A análise dinâmico-mecânica das blendas ternárias revelou um comportamento de fases complexo, sendo possível verificar a existência de uma fase elastomérica de EPDM dispersa em uma matriz constituída por várias fases, sendo uma delas a mistura miscível PPO/PS. Tal comportamento deve-se ao fato do PPO e PS serem totalmente miscíveis, já o PS é miscível com SAN quando este contém menos que 5% em massa de acrilonitrila, e o PPO é miscível com SAN quando este contém menos que 10% em massa de acrilonitrila. As blendas ternárias apresentam propriedades mecânicas dependentes do teor de AES. O aumento do teor de AES promoveu um significativo aumento na resistência ao impacto com ligeira queda no módulo e na resistência à tração. Entretanto, somente algumas composições apresentaram desempenho mecânico superior às blendas PPO/HIPS. Ensaios de envelhecimento acelerado mostraram que as blendas ternárias são mais estáveis que as blendas PPO/HIPS que possuem uma fase elastomérica insaturada / Abstract: The aim of this work was to prepare and to evaluate the PPO/AES/PS ternary blends behavior with respect to miscibility, compatibility, mechanical properties and photochemical stability aspects, as well as to compare these properties to the PPO/HIPS blends. In this work, the PPO/AES/PS ternary blends were obtained from the melt mixture PS, polystyrene, PPO, poly(2,6-dimethyl-1,4-phenylene oxide), AES, a thermoplastic elastomer constituted by a grafting of SAN, poly(styrene-co-acrylonitrile), on EPDM, a poly(ethylene-co-propylene-co-diene) elastomer.Three series of the ternary blends containing 40, 50 and 60 % of PPO were prepared. In each ternary blends series the AES¿s mass fraction variation was 10, 15, 20 and 30 %. To perform a comparative study, the binary blends PPO/AES, PPO/PS and AES/PS, with composition 50/50%, and the PPO/HIPS binary blend with the same PPO¿s contents that the ternary blends, were also prepared. The dynamical mechanical analysis of the ternary blends showed a complex phases behavior, with the EDPM elastomeric phase dispersed in a matrix constituted by several phases, one of them the miscible blend PPO/PS. Such behavior is due to the fact that PPO and PS blends are miscible blends, while PS is only miscible with SAN when it contains less than 10 % wt of acrylonitrile and PPO/SAN blends are also miscible if the acrylonitrile composition is less than 5 wt %. The ternary blends presents mechanical properties dependent on the blend AES content. The increase in the AES content in the blends resulted in a significative increase in the impact resistance and a slight drop in the modulus and tensile resistence. However, only some compositions showed better mechanical performance than PPO/HIPS blends. Accelerated aging showed that the ternary blends are more stable than the PPO/HIPS blends that present an unsaturated elastomeric phase / Doutorado / Físico-Química / Doutor em Quimica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248779 |
| Date | 22 September 2006 |
| Creators | Turchet, Renato |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Felisberti, Maria Isabel, 1959-, Lopes, Cristina Moniz Araujo, Cassu, Silvana Navarro, Paoli, Marco-Aurelio De, Jorge, Renato Atilio |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 119p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds