Previous issue date: 2015-02-27 / A introdução das bolsas plásticas de policloreto de vinila (PVC) para coleta e
armazenamento de sangue e seus componentes constituiu um grande avanço no
processo transfusional. O uso destas bolsas trouxe aos serviços de hemoterapia
uma coleta, preparação e transfusão do sangue de forma mais rápida, segura e
eficiente. A influência de processos extremos no processamento e armazenamento
das bolsas de sangue, como variações de temperatura de esterilização de 115ºC a
120ºC, temperaturas de armazenamento de sangue de até -70ºC e sucessivas
centrifugações de até 5000rpm, podem levar a alterações no material. Estas
alterações podem causar ruptura das bolsas de sangue com perda de seu conteúdo,
gerando com isso, riscos biológicos, prejuízos econômicos e aspectos sociais pela
doação de sangue. Este trabalho teve como objetivo a avaliação das propriedades
químicas e térmicas das bolsas de policloreto de vinila. As amostras de bolsas
plásticas nacionais utilizadas para este estudo foram selecionadas no Sistema de
Dados da ANVISA - DATAVISA entre as bolsas regularizadas. As bolsas
constituídas de PVC foram caracterizadas por Espectroscopia na Região de
Infravermelho com Transformada de Fourier (FTIR), Microscopia Eletrônica de
Varredura (MEV), Espectroscopia por Energia Dispersa de raios X (EDS),
Calorimetria Exploratória Diferencial (DSC) e Análise Termogravimétrica (TG). De
acordo com os resultados observados no ensaio de FTIR, pode-se afirmar que todas
as bolsas apresentaram os grupos funcionais característicos do PVC. O MEV
mostrou uma superfície homogênea. O ensaio de EDS detectou os elementos
químicos característicos do material estudado. A Análise Termogravimétrica
demonstrou que as bolsas de ambos os fabricantes apresentaram perfil de
degradação térmica similar iniciando por volta de 200ºC. Já o ensaio de DSC
corroborou com o ensaio de TG, mostrando a degradação inicial também em 200ºC.
Fundamentado pelos dados obtidos neste trabalho verificou-se que as bolsas
obedecem a um mesmo critério de composição, possivelmente a recomendada pela
Farmacopeia Europeia. / The introduction of plastic bags of polyvinyl chloride (PVC) for collection and storage
of blood and blood components was a breakthrough in transfusion process. The use
of these bags brought to transfusion services a collection, preparation and
transfusion of blood more quick, safe and efficient. The influence of extreme
processes in the processing and storage of blood bags, as sterilization temperature
of 115 to 120 ° C, blood storage temperature to - 70°C and successive
centrifugations of up to 5000rpm, can lead to changes in the material. These
changes can cause ruptures of blood bags with the consequence of losing contents
causing economic losses, biological risk and negative implications for voluntary
donation. This research has the objective the chemical and thermal evaluation of
polyvinyl chloride blood bags. The samples from national blood bags used for this
research were selected through ANVISA database from regularized blood bags. The
PVC blood bags were characterized by Fourier Transform Infrared Spectroscopy
(FTIR), Scanning Electron Microscopy (SEM), Energy-Dispersive X-Ray
Spectroscopy (EDS), Differential Scanning Calorimetry (DSC) and
Thermogravimetric Analysis (TG). According to the results observed on FTIR, it can
be affirmed that all bags had the characteristic functional groups of PVC. The SEM
showed a homogeneous surface. The EDS essay detected the characteristic
chemical elements of the studied material. The Thermogravimetric Analysis has
shown the bags from both manufacturers have similar thermal degradation profile
starting around 200°C. The DSC essay confirmed with the TG essay also showing
the initial degradation at 200 °C. Based on the data obtained in this work it was
identified that the bags conform to the same standard composition, possibly
recommended by the European Pharmacopoeia.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1065 |
| Date | 29 June 2018 |
| Creators | MOURA, Leandro Silva. |
| Contributors | NEVES, Gelmires de Araújo., FOOK, Marcus Vinicius Lia., LIMA, Rodrigo José da Silva., PINTO, Maria Roberta Oliveira. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds