Today, in the automotive industry, many of the interior parts in the car are made of ABS and PC/ABS polymeric blend. These materials are used in the areas for example: instrument panels, tunnel consoles and door panels. The extensive use of these materials means that it is important to gain in-depth knowledge about the materials,their properties; and also their behaviour when in contact with different chemicals andat different conditions.This study aims to address the potential problem of the polymers used in the interiorof the car - ABS and PC/ABS cracking due to environmental factors. This study proposes to introduce a low-cost test method to compare the polymeric materials and choose the best one for future purposes with the environmental circumstances in mind for materials to have a good service life.During the thesis project, ABS and PC/ABS samples were tested for environmental stress cracking to compare the strained materials against PEG 400 and an assemblyfluid chemical. These tests were conducted at three different temperature levels.Differential Scanning Calorimetry (DSC) was used to verify the polymeric materialsthat the samples were made of. Optical microscope and FTIR were employed to analyzethe samples for crazes / cracks and degradation of material, respectively.This thesis helped in establishing a good starting point for ESC testing of different materials for the organization. The test method was used to test the failure of material sin ESC. It was observed that the chemicals used for the testing were aggressive and accelerated the cracking process in the materials rapidly. Another observation of the tests was that high strain also caused the materials to fail quickly. While comparing the materials, PC/ABS polymer blend was more resistant than ABS materials to cracking when exposed to same strain level during the creep rupture test (test in absence ofchemicals acting as a reference test for ESC).
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-241146 |
Date | January 2018 |
Creators | Kumar Bhalla, Ashish |
Publisher | KTH, Skolan för kemi, bioteknologi och hälsa (CBH) |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.1555 seconds