Yes / A transflectance near infra red (NIR) spectroscopy approach has been used to simultaneously measure drug and plasticiser content of polymer melts with varying opacity during hot melt extrusion. A high temperature reflectance NIR probe was mounted in the extruder die directly opposed to a highly reflective surface. Carbamazepine (CBZ) was used as a model drug, with polyvinyl pyrollidone-vinyl acetate co-polymer (PVP-VA) as a matrix and polyethylene glycol (PEG) as a plasticiser. The opacity of the molten extrudate varied from transparent at low CBZ loading to opaque at high CBZ loading. Particulate amorphous API and voids formed around these particles were found to cause the opacity. The extrusion process was monitored in real time using transflectance NIR; calibration and validation runs were performed using a wide range of drug and plasticiser loadings. Once calibrated, the technique was used to simultaneously track drug and plasticiser content during applied step changes in feedstock material. Rheological and thermal characterisations were used to help understand the morphology of extruded material. The study has shown that it is possible to use a single NIR spectroscopy technique to monitor opaque and transparent melts during HME, and to simultaneously monitor two distinct components within a formulation.
Identifer | oai:union.ndltd.org:BRADFORD/oai:bradscholars.brad.ac.uk:10454/7368 |
Date | 15 July 2015 |
Creators | Kelly, Adrian L., Halsey, S.A., Bottom, R.A., Korde, Sachin A., Gough, Tim, Paradkar, Anant R |
Source Sets | Bradford Scholars |
Language | English, English |
Detected Language | English |
Type | Article, Accepted manuscript |
Rights | © 2015 Elsevier. Reproduced in accordance with the publisher's self-archiving policy. This manuscript version is made available under the CC-BY-NC-ND 4.0 license (http://creativecommons.org/licenses/by-nc-nd/4.0/), CC-BY-NC-ND |
Page generated in 0.0016 seconds