Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T13:43:16Z (GMT). No. of bitstreams: 1
Reges_RogerioVieira_D.pdf: 465516 bytes, checksum: 5fc0375c76e29f88888b24dc2e9af545 (MD5)
Previous issue date: 2005 / Resumo: O objetivo deste estudo foi avaliar a influência de duas fontes de luz sobre a dureza Knoop dos cimentos resinosos Variolink II, nas cores XL transparente ¿ (A1), A3, A2 e Opaco e Enforce B1, A2 e Branco Opaco, nos período imediato e 24 horas após a polimerização. Corpos-de-prova com 5mm de diâmetro por 1mm de espessura dos cimentos resinosos Variolink II (Ivoclar-Vivadent) e Enforce (Denstisply) foram preparados num molde de teflon, cobertos com uma tira de poliéster e disco de cerâmica feldspática Duceram na espessura de 2,0 mm e fotoativados por 40 segundos com aparelho XL 2500 (3M), com 615 mW/cm2 e 40 segundos com o aparelho LED ¿ Ultrablue Is (D.M.C.) com 610 mW/cm2 . A dureza Knoop foi efetuada no aparelho HMV-2, com carga de 50 gramas por 15 segundos, imediatamente e após armazenagem por 24 horas a 37o C. Doze penetrações foram feitas em cada corpo-de-prova para o cimento resinoso Enforce, sendo que cinco corpos-de-prova foram confeccionados para cada cor do cimento e cinco para o grupo controle (sem cerâmica) em cada tempo de armazenagem, totalizando 60 corpos-de-prova. Para o cimento Variolink II, quatro penetrações foram feitas em cada corpo-de-prova, sendo que cinco corpos-de-prova foram confeccionados para cada cor do cimento em cada condição experimental, totalizando 80 corpos-de-prova. Os dados foram submetidos à análise de variância e ao teste de Tukey (5%) e mostraram que o cimento resinoso Variolink II opaco apresentou o menor valor de dureza Knoop em relação as outras cores do cimento, para as duas fontes de luz e dois períodos de ativação (mediato e 24 horas). O aparelho fotoativador de lâmpada halógena apresentou valores de dureza Knoop estatisticamente superior em relação ao aparelho LED para as cores do cimento A2, A3 e opaco para a condição mediato e XL, A2 e A3 após 24 horas. Quando os dois métodos de fotoativação foram comparados para a mesma cor do cimento, os aparelhos fotoativadores com lâmpada halógena e LED (24 horas) apresentaram valores de dureza Knoop estatisticamente superiores aos valores fotoativados na condição mediato. A regressão linear positiva da dureza Knoop foi estabelecida em função da profundidade de fotoativação da amostra do cimento resinoso (Enforce) pela fotoativação direta e indireta pela interposição da cerâmica. O cimento resinoso Enforce na cor opaca mostrou valores de dureza Knoop estatisticamente inferior às outras cores do cimento. A dureza Knoop mediata mostrou valores de dureza Knoop na região de topo (100 µm) estatisticamente superior em relação a dureza na região de fundo (700 µm) / Abstract: The aim of this study was to evaluate the influence of two light sources in Knoop hardness values of resin cement Variolink II in the shade XL transparent (A1), A3, A2, and Opaque and Enforce B1, A2 and Opaque White, in the immediate time and 24 hours after polymerization. The specimens with 5.0 mm in diameter and 1.0 mm in thickness of resin cements Variolink II (Ivoclar-Vivadent) and Enforce (Dentisply) were made in the Teflon mould, covered with a Mylar strip and fledspatic ceramic Duceram Plus (DeguDent) disc 2.0 mm thick and photoactivated for 40 seconds with halogen light unit XL 2500 (3M), with intensity of 615 mW/cm2 and 40 seconds with LED ¿Ultrablue Is (D.M.C.) with power density of 610 mW/cm2. Knoop hardness was measured using HMV-2 (Shimadzu), with a 50g load for 15 seconds, immediately stored at 37o C for 24 hours. Twelve indentations were made in each specimen for the resin cement (Enforce). Five specimens were made for each color and five specimens for the control group (without ceramic) in each stored time, totaling sixty specimens. For the resin cement Variolink II, four indentations were made in each specimen, and five specimens were made for each one in each stored time, totaling eighty specimens. The data were submitted to variance analysis and Tukey¿s test (5%) and showed that the opaque shade of the resin cement had lower Knoop hardness value in relation to the other shades for both light sources and both activation periods (mediate and 24 hours). The halogen units showed Knoop hardness values higher than LED¿s for A2, A3 and opaque for mediate and XL, A2 and A3 after 24 hours. When the photoactivation methods were compared for the same shade halogen and LED (24 hours) showed higher Knoop hardness values than mediate photoactivation. Knoop hardness positive linear regression is a function of depth of specimen of resin cement direct and indirectly photoactivated. Opaque shade showed KHN statistically inferior to the others resin cement groups. Mediate KHN reading showed that Knoop hardness near top (100 µm) is statistically different from bottom surface (700 µm) / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289588 |
| Date | 29 June 2005 |
| Creators | Reges, Rogerio Vieira |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Correr Sobrinho, Lourenço, 1960-, Garcia, Robson Rodrigues, Borges, Gilberto Antonio, Consani, Rafael Leonardo Xediek, Sinhoreti, Mário Alexandre Coelho |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 62f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds