000828059.pdf: 280753 bytes, checksum: 5f2e10cc380917f920e1c412177bafa4 (MD5) / Os tratamentos de superfície convencionais realizados em cerâmicas feldspáticas são o condicionamento com ácido fluorídrico e a aplicação do silano. Porém em inúmeros estudos o condicionamento ácido tem sido questionado por sua toxidade química. Assim objetivou-se avaliar o efeito do tratamento térmico na cerâmica feldspática silanizada na adesão ao cimento resinoso. Por meio de um estudo in vitro foram seccionados 24 blocos de cerâmica feldspática sinterizada, com dimensões de 5 x 10 x 4 mm. Estes blocos foram divididos aleatoriamente em três grupos experimentais: G1 (HF + Silano); G2 (Silano + aquecimento 77 °C); G3 (HF+ Silano + aquecimento 77 °C). Os blocos cerâmicos foram cimentados a blocos de resina composta por meio de um cimento resinoso (Variolink, Ivoclair-Vivadent), posteriormente o conjunto foi cimentado a blocos idênticos de resina composta (Z-100, 3M-ESPE) e após a cimentação foram submetidos à ciclagem mecânica (10.000 ciclos 100 N). Após ciclagem foram seccionados em palitos de 1mm2 e submetido ao teste microtração a velocidade de 1 mm/min. Todos os corpos de prova foram analisados em estereomicroscópio com 20 x, para classificação das fraturas e apenas as amostras significativas em microscópio eletrônico de varredura com magnitudes com de 100 x, 300 x e 500 x. Os resultados obtidos foram submetidos à análise estatística Anova um fator e teste de Tukey (α = 0,05). A análise estatística demonstrou semelhança estatística (p - valor = 0,33)entre todos os grupos (G1 22,63 MPaA; G2 23,31 MPaA; G3 26,32 MPaA).A análise de falhas demonstrou predominância de falhas adesivas para todos os grupos. Conclui-se que o aquecimento do silano é efetivo para esta interface sendo possível eliminar o condicionamento com HF(ácido fluorídrico) / The conventional surface treatment performed on feldspathic ceramic is the fluoridric acid etching and silane application. But in several studies the etching has been questioned for its chemical toxicity. Thus this study aimed to evaluate the effect of heat treatment on silanized feldspathic ceramic bond strength to resin cement. Through an in vitro study 24 feldspathic ceramic sintered blocks were sectioned; 5 x 10 x 4 mm of dimensions. These blocks were randomly divided into three experimental groups: G1 ( HF + silane ) ; G2 ( + Silane heating 77 °C); (G3 + Silane + HF + heating 77 °C). The ceramic blocks were cemented with resin blocks composed of resinous cement ( Variolink , IvoclairVivadent ) , the set was later cemented identical blocks of composite resin ( Z - 100 , 3M - ESPE ) , after cementation were subjected to cycling mechanical (10,000 cycles 100 N). After cycling were sectioned into sticks of 1mm2 and submitted to microtensile test with speed of 1 mm / min. Representative samples were analyzed with a stereomicroscope at 20 x and scanning electron microscope with magnitudes of 100 x, 300 x and 500 x. The results were statistically analyzed by ANOVA one factor and by Tukey test (α = 0.05). Statistical analysis showed (p - value = 0.33) statistical similarity between all groups (G1 22.63 mPa, mPa 23.31 G2, G3 26.32 mPa). The failure analysis showed predominance of adhesive failures for all groups. It can be concluded that heating the silane is effective for this interface it is possible to eliminate the etching with HF (Flouridric acid)
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/123976 |
| Date | 05 August 2014 |
| Creators | Miranda, Geraldo Marques [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Pagani, Clovis [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 54 f. : il. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.0039 seconds