Nano-Particle Removal from Surface of Materials Used in EUV Mask Fabrication

With device scaling, the current optical lithography technique is reaching its technological limit to print small features. Extreme Ultra-Violet (EUV) lithography has shown promise to print extremely thin lines reliably and cost-effectively. Many challenges remain before introducing EUV to large scale manufacturing. The main challenge addressed in this study is particle removal from EUV mask surfaces (CrON1, CrON2, and fused silica) and thermal oxide (SiO₂). Effective pre-clean procedures were developed for each surface. As chemical cleaning methods fail to meet SEMATECH criteria, addition of megasonic energy to EUV mask cleaning baths is seen as a promising cleaning methodology. As the requirement to print fine lines needs to be met, all materials used in EUV mask fabrication either absorb the incident EUV wavelength light or reflect it. Therefore, the masks used in the industry will be reflective instead of the conventional transmissive masks. Also, for the same reason, no protective pellicle can be used leading to all the surfaces unprotected from particle contamination. To avoid the detrimental effect of the particle contamination, a cleaning study for nano-particle removal was performed. A dark field microscope was utilized to study the removal of gold nano-particles from surfaces. The cleaning procedures utilized H₂SO₄ and NH₄OH chemistries with and without megasonic irradiation. The cleaning variables were bath concentration, temperature, and megasonic power. The contamination variables were the gold nanoparticles charge and size, from 40nm to 100nm. For 100 nm negatively charged gold nano-particles deposited on a CrON1 surface, a 1:10 H₂SO₄:DI bath at boiling temperature (101°C) without megasonics gave high particle removal efficiency (PRE) values as did a 1:10 H₂SO₄:DI bath at 35°C with 100W megasonics. Comparison of removal of poly diallyl-dimethyl ammonium chloride (PDAC) coated and uncoated gold nano-particles deposited on a CrON1 surface using dilute H₂SO₄ baths indicated that the coated, positively charged nano-particles were more difficult to remove. PRE trends for different baths indicate surface dissolution (shown to be thermodynamically favorable) as the particle removal mechanism. However, experimental etch rates indicated minimal surface etching in a 10 minute bath. Increased surface roughness indicated possible local galvanic corrosion at particle sites. Low surface etching results meet SEMATECH requirements. During the fused silica surface cleaning study, particle charge (negative) and size (100 nm) of the contamination source and cleaning bath chemistry (NH₄OH) were kept constant. Low PREs were obtained at room temperature for all NH₄OH bath concentrations; however, high PREs were obtained at an elevated temperature (78°C) without megasonics and at room temperature in more dilute chemistries with megasonic power applied. Similar PRE trends were demonstrated for thermal SiO₂ surfaces. The experimental etch rates of the thermal SiO₂ agree with published values.

Identiferoai:union.ndltd.org:arizona.edu/oai:arizona.openrepository.com:10150/194270
Date January 2006
CreatorsPandit, Viraj Sadanand
ContributorsParks, Harold G, Raghavan, Srini, Parks, Harold G, Raghavan, Srini, O'Hanlon, John F., Wang Roveda, Janet
PublisherThe University of Arizona.
Source SetsUniversity of Arizona
LanguageEnglish
Detected LanguageEnglish
Typetext, Electronic Dissertation
RightsCopyright © is held by the author. Digital access to this material is made possible by the University Libraries, University of Arizona. Further transmission, reproduction or presentation (such as public display or performance) of protected items is prohibited except with permission of the author.

Page generated in 0.0022 seconds