Previous issue date: 2014-07-18 / Agentes de contraste são materiais de grande relevância para a qualidade das imagens obtidas por ressonância magnética, acentuando o contraste das imagens e facilitando o diagnóstico de patologias. As nanopartículas têm sido bastante utilizadas como agentes de contraste para ressonância magnética, sendo que as mais utilizadas são as nanopartículas de óxido de ferro. A segurança e toxicidade das nanopartículas tem sido objeto de uma preocupação cada vez maior, pois o conhecimento sobre os efeitos biológicos de materiais deste tipo ainda não é suficiente. As propriedades das
nanopartículas, por sua vez, dependem do tamanho, microestrutura e
revestimento da superfície, controlados pelas condições de síntese e
processamento das nanopartículas. O objetivo deste trabalho foi obter óxido de
ferro pelo Método Pechini, para utilização como agentes de contraste para uso
em ressonância magnética, de modo a caracterizá-los. Nanopartículas de óxido
de ferro foram sintetizadas pelo Método Pechini, com razão entre o ácido cítrico
em relação aos cátions metálicos de 3:1, sendo posteriormente calcinadas em
temperaturas de 400ºC e 900ºC, pelos períodos de 1h ou 2h. Logo após foram
caracterizadas por Microscopia Eletrônica de Varredura (MEV), Espectroscopia
de Energia Dispersiva de Raios-X (EDS), Difração de Raios X - (DRX), Análise
de Calorimetria Exploratória Diferencial (DSC), Termogravimetria (TG) e
Espectroscopia de Infravermelho com Transformada de Fourier (FTIR).
Também foi realizado Ensaio de Citotoxicidade – Viabilidade Celular. Os
resultados de DRX revelaram a formação da fase hematita e presença de
segunda fase magnetita. A morfologia é constituída de aglomerados de aspecto
rígido com partículas de formato irregular, com tamanho menor e maior que 10
µm. A temperatura de calcinação de 400ºC não foi suficiente para se obter
nanopartículas de óxido de ferro estáveis termicamente. Os pós obtidos pelo
Método Pechini não apresentaram viabilidade celular. / Contrast agents are materials of great relevance to the quality of the images obtained by magnetic resonance imaging, accentuating the contrast of images and facilitating the diagnosis of pathologies. Nanoparticles have been widely used as contrast agents for magnetic resonance imaging, and the most used are nanoparticles of iron oxide. The safety and toxicity of nanoparticles has been the subject of increasing concern, because knowledge about the biological effects of such materials is not enough. The properties of the nanoparticles, in turn, depend on the size, microstructure and surface coating, all of them controlled by the conditions of synthesis and processing of nanoparticles. The
aim of this study was to obtain iron oxide by Pechini method, for use as contrast
agents in diagnostic magnetic resonance imaging, in order to characterize
them. Iron oxide nanoparticles were synthesized by Pechini method with ratio of
citric acid to metal cations in relation 3:1, subsequently calcined at temperatures
of 400 º C and 900 º C, for periods of 1h or 2h. Soon after were characterized
by Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy Xray
(EDS), X-Ray Diffraction - (XRD), Differential Scanning Calorimetry analysis
(DSC) , Thermogravimetry (TG), and Fourier Transform Infrared Spectroscopy
(FTIR). Was also performed Cytotoxicity Assay - Cell Viability. The XRD
showed the formation of phase of hematite and presence of second phase of
magnetite. The morphology consists of rigid aspect of agglomerates with
particles of irregular shape and with a smaller size greater than 10 µm. The
calcination temperature of 400 ° C was not sufficient to obtain iron oxide
nanoparticles thermally stable. The powders obtained by the Pechini method
showed no cell viability.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/417 |
| Date | 18 April 2018 |
| Creators | PIRES, Thibério Mundim Ferreira. |
| Contributors | MENEZES, Romualdo Rodrigues., FOOK, Marcus Vinícius Lia., FOOK, Sayonara Maria Lia., SANTOS, Patrícia Tatiana Araújo dos. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0412 seconds