Previous issue date: 2011-06-21 / This works aims at investigating the effects of adding waste from RCBP-polyester
button manufacturing to Portland cement concrete, particularly regarding its
consistency and mechanic strength. The RCBP used came from a button factory
located in Parnamirim, RN, Brazil. The waste was added to the concrete on different
ratios: 5 %, 10 %, 15 % and 20 % of the total cement mass. A sample of concrete
without the RCBP was used as reference, 1:1,33:2,45:0,50. For the mechanic
strength test four samples were tested with different ages (3, 7 and 28 days old) and
mixtures. Furthermore, a Slump Test was also conducted in order to verify the
concrete s consistency. A tendency to a reduction in the compression resistance was
noticed for all samples. For the samples with 5 % and 10 %, there was also an
increase in the traction resistance during inflexion, regarding the reference concrete.
In the microstructural analysis, the RBCP was observed to show an irregular and
porous surface, thus explaining the consistency decrease / O presente trabalho objetivou avaliar a influ?ncia da incorpora??o do res?duo de
corte de bot?o em poli?ster-RCBP sobre a plasticidade e a resist?ncia mec?nica em
concreto de cimento Portland. O RCBP utilizado na pesquisa originou-se do material
descartado por uma empresa fabricante de bot?o localizada no munic?pio de
Parnamirim/RN. Utilizou-se o res?duo, como carga no concreto, nas concentra??es
de 0 %, 5 %, 10 %, 15 % e 20 %, em rela??o ? massa do cimento. O tra?o de
refer?ncia do concreto utilizado na pesquisa apresenta a propor??o, em massa, de
1:1,33:2,45:0,50 (cimento:areia:brita:?gua/cimento). Nos ensaios de resist?ncia ?
compress?o foram testados quatro corpos-de-prova para cada idade (3, 7 e 28 dias)
e tra?o, enquanto que para os ensaios de resist?ncia ? tra??o na flex?o foram
testados dois corpos-de-prova para cada tra?o. Al?m disso, fez-se o Slump Test,
com vistas a verificar a consist?ncia do concreto. Observou-se uma tend?ncia de
redu??o da resist?ncia ? compress?o e abatimento para todos os tra?os com
incorpora??o do RCBP. Houve um aumento de resist?ncia ? tra??o na flex?o para
os tra?os de 5 % e 10 %, em rela??o ao concreto sem incorpora??o do res?duo,
superando o sugerido pela NBR 6118/2003 que apresenta uma correla??o entre
resist?ncia ? tra??o e ? compress?o. Na an?lise microestrutural, observou-se que o
RCBP apresentou uma superf?cie irregular e porosa, podendo ser o motivo do
decr?scimo do abatimento
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/14835 |
Date | 21 June 2011 |
Creators | Avelino, Veruska Kelly Gomes Rocha |
Contributors | CPF:02209937426, http://lattes.cnpq.br/2173551172181329, Silva, Jaquel?gia Brito da, CPF:02585622428, http://lattes.cnpq.br/5948828937239319, Almeida, Maria das Vit?rias Vieira de, CPF:52402444487, http://lattes.cnpq.br/7590200701773198, Dutra, Ricardo Peixoto Suassuna, CPF:91875838449, http://lattes.cnpq.br/0075804072604913, Souza, Paulo Alysson Brilhante Faheina de |
Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Engenharia Civil, UFRN, BR, MEC?NICA DAS ESTRUTURAS, ESTRUTURAS DE CONCRETO E ALVENARIA E MATERIAIS E PROCESSOS CONSTRUTIVOS |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds