Orientador: Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-22T20:45:34Z (GMT). No. of bitstreams: 1
Soares_AnadeliaBorges_M.pdf: 5590690 bytes, checksum: b4038ac37f3102d78f8ba65bdda22c60 (MD5)
Previous issue date: 1997 / Resumo: Os cimentos de ionômero de vidro são dependentes do equilíbrio hídrico e apresentam contração durante a reação de geleificação. O propósito deste estudo foi avaliar o efeito da umidade relativa (U.R.) na estabilidade dimensional dos cimentos restauradores ionoméricos Vidrion R (SS White) e Chelon Fil (ESPE), modificados por resina (Vitremer-3M), duas resinas modificadas por poliácidos (Compoglass/ Vivadent e Dyract /Dentsply) e a resina composta Z100 (3M). Os corpos-de-prova foram obtidos em matrizes metálicas circulares medindo 6 mm de diâmetro por 2 mm de espessura. Foram confeccionados dez corpos-de-prova para cada material, ?endo cinco deles em ambiente controlado à temperatura de 23° :!: 1°C e 50 :!: 5% de U. R. e os outros cinco à mesma temperatura e à umidade relativa de 80%. Os materiais foram manipulados de acordo com as instruções dos fabricantes. Logo após os procedimentos de confecção, es corpos-de-prova foram armazenados a 37°C e 100% de U.R., durante uma hora. Decorrido o tempo de armazenagem, a interface matriz metálica-material restaurador foi mensurada através de uma ocular micrométrica com. tambor graduado acoplada na objetiva de um fotomicroscópio. Os valores obtidos foram submetidos a análise de variância e ao teste de Tukey em nível de 5% de significância. Os materiais Vidrion R e Chelon Fil apresentaram valores médios das fendas formadas na interface matriz-material restaurador significativamente maiores no ambiente de 50% de U.R, em relação ao ambiente com 80% de U.R. Os valores apresentados pelos demais materiais não diferiram estatisticamente entre si (p>0,05) e foram inferiores aqueles dos cimentos Vidrion R e Chelon Fi!. Os valores médios das fendas apresentados por todos os materiais foram significativamente diferentes entre si (p<0,05) nos ambientes de 50% ou 80% de U.R. na seguinte ordem decrescente: Vidrion R > Chelon Fil > Z100 > Vitremer > Compoglass > Dyract. Todos os materiais apresentaram fendas, independentes da composição e umidade relativa / Abstract: The purpose of this study was evaluate the effect of relative humidity (RH) on the dimensional stability of glass ionomer cements, Vidrion R (S.S.White) and Chelon Fil (ESPE), and one resin modified glass ionomer (Vitremer-3M), two polyacid modified resins (CompoglassNivadent and Dyract/Dentsply), and the composite resin Z 100 (3M). The specimens were obtained from metallic rounded molds (6mm diameter x 2mm thick). Ten specimens of each material were made, five of them on enviroment at 23° :t 1 ° C and 50 :t 5% RH and the remaining at 23° :t 1 ° C and RH of 80%. The materiais were manipulated according to the manufacturer's instructions. The specimens were stored at 37°C and 100 % RH for one hour. After the storage period, the gaps that were formed in materialmetallic mold interface were measured .through a graduated lens adapted to a microscope. The values were submitted to variance analysis and Tukey's test (p ~ 0,05). At 50% RH, gaps values for Vidrion R and Chelon .
Fil were significatly higher than at 80% RH. The values of other materiais were similar at both RH, and gaps values were lower than Vidrion R and Chelon Fi!. Ali the materiais showed different gaps values (p < 0,05) at both relatives humidities according to the following decreasing range: Vidrion R > Chelon Fil > Z 100 > Vitremer > Compoglass > Dyract. Ali materiais showed gaps, despite of composition and relative humidity / Mestrado / Materiais Dentarios / Mestre em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288175 |
| Date | 11 September 1997 |
| Creators | Soares, Anadelia Borges |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Goes, Mario Fernando de, 1954-, Consani, Simonides, Razaboni, Ana Maria |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 134f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds