Cimentos resinosos endodônticos: selamento apical, aspectos micromorfológicos, características físicas e resistência de união à dentina / Resin-based root canal sealers: apical sealing, micromorphological aspects, physical characteristics and bond strength to dentin

Avaliou-se o selamento apical, os aspectos micromorfológicos da interface adesiva, as características físicas e a resistência de união à dentina de cimentos resinosos endodônticos. Setenta e dois pré-molares humanos unirradiculares foram preparados endodonticamente. Trinta e três dentes foram divididos aleatoriamente em 3 grupos, impermeabilizados externamente e obturados pela técnica da condensação lateral acorde as seguintes condições: AH Plus (AH Plus/Gutapercha); AH Primer (Epiphany primer/AH Plus/Gutapercha) e Epiphany (sistema Epiphany). Foram mantidos a 37oC e 100% de umidade por 72 h e, em seguida, imersos em solução aquosa de nitrato de prata a 50% por 24 h. Após secção longitudinal dos dentes, foram realizadas réplicas em resina epóxica. Réplicas e espécimes foram preparados para MEV. Nas réplicas, observou-se a freqüência de fendas apicais na interface dentina/cimento. Nos espécimes, detectou-se e confirmou-se com EDS (Energy Dispersive Spectroscopy) a microinfiltração apical. A interface dentina/cimento foi observada em seis espécimes de cada grupo, selecionados aleatoriamente. A microinfiltração foi similar entre os grupos (p>0,05), sendo influenciada pela freqüência de fendas (p<0,05). Foram observadas tanto regiões com fendas quanto com camada híbrida e longos tags para o grupo Epiphany. Para os grupos AH Primer e AH Plus foi verificada boa adaptação marginal com longos tags vazios e pequenos plugs, respectivamente, embora tenha ocorrido a formação de fendas em ambos. Os outros dentes foram utilizados para as avaliações adicionais: seis, para complementar o estudo micromorfológico da interface adesiva; três, para o ensaio de microdureza Knoop; e, trinta, para o teste de resistência de união. O cimento Epiphany mostrou maior escoamento (p<0,001) e tensão de polimerização (p<0,05), e a menor resistência de união (p<0,001). Os valores de microdureza Knoop decresceram acentuadamente de cervical para apical (p<0,001). Concluiu-se que a total impermeabilização do sistema de canais radiculares não foi obtida com nenhum dos cimentos testados, e que o sistema Epiphany formou mais fendas no ápice. / Resin-based root canal sealers had their apical sealing, micromorphological aspects, physical characteristics and bond strength to dentin evaluated in this study. For this purpose, seventy-two single-rooted human premolars were endodontically treated. Thirty-three teeth were randomly divided into three groups, externally coated with nail varnish and obturated by lateral condensation technique according to such conditions: AH Plus (AH Plus/Gutta-percha); AH Primer (Epiphany primer/AH Plus/ Gutta-percha) and Epiphany (Epiphany system). They were kept in 100% humidity at 37oC for 72 h, and then the specimens were immersed in 50% aqueous silver nitrate tracer solution for 24 h. The teeth were longitudinally sectioned and their epoxy resin replicas were obtained. Both the specimens and their corresponding replicas were prepared for SEM. In the replicas, the frequency of apical gaps at the dentin/cement interface was observed. In the specimens, the apical microleakage was detected and confirmed by EDS (Energy Dispersive Spectroscopy). The dentin/cement interface was observed in six specimens of each group randomly selected. The microleakage was similar among the groups (p>0,05) being influenced by gaps frequency (p<0,05). The Epiphany group presented gap-containing regions, hybrid layer formation and long tags. For AH Primer and AH Plus groups, good marginal adaptation with long empty tags and small plugs, respectively, although gaps formation was found in both groups. The remaining teeth were used for other evaluations: six, to finish micromorphological study at the adhesive interface; three, for Knoop microhardness; and thirty, for bond strength test. The Epiphany resin sealer has showed the highest flow (p<0.001) and polymerization stress (p<0.05), and the lowest bond strength values (p<0.001). The Knoop microhardness values have decreased excessively from the cervical to the apical third (p<0.001). It was concluded that none of the sealers tested achieved a complete sealing of the root canals system, and the Epiphany system has developed more gaps to the apex.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-09042009-120215
Date12 December 2007
CreatorsSouza, Soráia de Fátima Carvalho
ContributorsBombana, Antonio Carlos, Francci, Carlos Eduardo
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguageEnglish
TypeTese de Doutorado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0029 seconds