Orientador: Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-22T21:31:33Z (GMT). No. of bitstreams: 1
Carvalho_ChristianeMartinsdeLannaSalles_M.pdf: 3513862 bytes, checksum: bd92d1818f3145a39d79f448b471a2d5 (MD5)
Previous issue date: 1997 / Resumo: A resistência à tração da porcelana sob influência de materiais cimentantes foi avaliada em 48 discos cerâmicos (Ouceram Oegussa) de 20,75 mm de diâmetro por 1,28 mm de espessura. As amostras foram divididas em 6 grupos: A - Amostras sem tratamento de superfície ou aplicação de material cimentante; B- A superfície não glazeada da amostra foi condicionada com ácido fluorídrico a 10% por 4 minutos; C - Procedimento similar ao do grupo B, seguido da aplicação do silano, adesivo e de cimento resinoso Choice Porcelain (Bisco); O - Procedimento similar ao grupo C, e aplicação do cimento resinoso (Resin Cement-3M); E Superfície não condicionada e utilização de cimento de fosfato de zinco(S.S.White); F- Superfície não condicionada e aplicação do Vitremer para cimentação (3M). Os corpos de prova foram armazenados por 24 horas a 37° C e 100% de umidade relativa. A seguir, foram posicionados na máquina MTS para a realização do ensaio de flexão através do teste biaxial, à velocidade de 2mm/min. Os valores obtidos foram submetidos à Distribuição de Weibull. Os valores médios de resistência à fratura foram: Grupo A=13,20 MPa; B=10,19 MPa; C=178,26 MPa; 0=154,96 MPa; E=125,59 MPa; F=128; 13 MPa. A resistência à tração da porcelana variou de acordo com o material cimentante e foi maior quando utilizada a associação condicionamento áciao/sistema adesivo/cimento resinoso / Abstract: The tensile strength of porcelain under the influence of luting cement was verified in forty-eight ceramic discs measuring 20.77 mm in diameter and 1.28 mm in thick, using Ouceram porcelain (Oegussa). The specimens were randomly divided into six groups: A - The specimens did not receive any treatment or IltIting cemen~; 8 The non glazed surface of the specimen was etched with a hidrofluoridric acid àt 10% for 4 minutes; C - Sil1i1ilar procedure of group 8, followed by the coating of silane/adhesive/resin cement (Choice Porcelain - 8isco); O - Similar pliocedure of group C, except that the ceramic surface was coated with Resin Cement (3M); E The ceramic surface was not etched and it was coated with zinc phosphate (S.S.White); F - The ceramic surface was not etched and it was coated with Vitremer Cement (3M). The specimens were stored. at 37°C and 100% relative humidity for 24 hours. Then, the biaxial test was carried by submiting the specimens to compressive stress on the MTS machine at crosshead of 2mm/min.The original' values were submited to the Weibull Oistribution. The mean values were: Group A=13.20 MPa; Group 8=10.19 MPa, Group C=178.63 MPa;Group 0=154.96 MPa; Group E=125.59 MPa; Group F=128.13 MPa. The porcelain tensi'le strength varied according with the luting cement and it was higher when the association acid etching/adhesive system/ luting resin cement was used. / Mestrado / Materiais Dentarios / Mestre em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288176 |
| Date | 08 September 1997 |
| Creators | Carvalho, Christiane Martins de Lanna Salles |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Goes, Mario Fernando de, 1954- |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Ciências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 116f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |