O objetivo deste trabalho foi avaliar, in vitro, ao Microscópio de Luz Polarizada (MLP), o potencial cariostático dos selantes resinosos, dos cimentos ionoméricos, do diamino fluoreto de prata e do verniz fluoretado aplicados em superfície oclusal de molares permanentes humanos. Para tanto, 70 terceiros molares humanos hígidos, extraídos por razões clínicas, foram divididos aleatoriamente em sete grupos (N=10): GI controle (sem selamento); GII selante resinoso sem flúor Delton ®; G III selante resinoso fluoretado Fluroshield ®; GIV cimento de ionômero de vidro (CIV) de presa rápida Ketac Molar ®; GV CIV modificado por resina Vitremer ®; GVI solução de diamino fluoreto de prata (DFP) a 30% Safluoride ®; GVII verniz fluoretado a 2,26% Duraflur ®. Após profilaxia com jato de bicarbonato, os materiais foram aplicados na superfície oclusal, de acordo com as orientações dos fabricantes, sendo os dentes impermeabilizados com verniz com exceção da área das fissuras e de 1 mm ao redor das mesmas, sendo submetidos a ciclagens de desremineralização durante 14 dias. Após a ciclagem, foram seccionados e as secções obtidas lixadas, polidas e embebidas em água durante 36 horas, para análise ao MLP, sendo medidas transversalmente nas fotografias, a profundidade (µm) e a área m2) da lesão através de grade quadriculada em seis pontos padronizados ao longo da lesão. As médias das 6 medidas foram calculadas nos 7 grupos e comparadas estatisticamente através do teste não-paramétrico de Kruskal-Wallis e de Comparações Múltiplas de Dunn, ao nível de 5% de probabilidade (p<0,05). Observou-se diferença estatisticamente significante (P= 0.000000372) a nível de profundidade da lesão (H= 50,5) com menores valores para o GVII (0,29 µm), GVI (0,61 µm) e GV (0,89 µm) em comparação aos materiais do GIV (3,69 µm), GII (3,67 µm) e GIII (2,10 µm) que não diferiram do GI (5,81 µm). Quanto à área da lesão, houve diferença estatisticamente significante (P= 0.0000256; H= 51,3), com os menores valores para os tratamentos do GV (0,81µm2), GVII (1,78µm2), GVI (2,86 µm2), GIV (3,69 µm2) e GIII (4,91 µm2), comparados ao GII (16,39 µm2) e GI (24,04µm2), que não diferiram entre si. Concluiu-se que, os materiais fluoretados são eficazes em controlar o início e/ou a progressão da lesão de cárie na superfície oclusal quando comparados com o selante resinoso sem flúor e o não selamento. / The aim of this research was to evaluate, in vitro, with polarized light microscopy (PLM), the cariostatic potential of resin sealants and glass-ionomer cements, diamine silver fluoride solution and fluoride varnish applied on occlusal surface of human permanent molars. In order to achieve this goal, 70 caries free third human molars, extracted for clinical reasons, were randomly divided into seven groups (N=10): GI control (no sealing treatment); GII resin sealant without fluoride Delton ®; GIII fluoride-releasing sealant Fluroshield ®; GIV glass-ionomer cement Ketac Molar ®; GV resin-modified glass-ionomer cement Vitremer ®; GVI 30% diamine silver fluoride solution (DSF) Safluoride ®; GVII 2,26% fluoride varnish Duraflur ®. After dental prophylaxis with sodium bicarbonate, the materials were applied on the occusal surface, according to the manufacturers instructions, and all tooth surfaces were covered with acid-resistant varnish except for the fissures and 1mm rim of exposed enamel surrounding this area. The specimens were then exposed to 14-day de-remineralization cycles. After this period, they were sectioned, grounded, polished and imbibed in water for 36 hours, then examined with PLM and photographed. The depth (µm) of the artificial caries lesions was assessed from the photomicrographs by measuring traverses running perpendicular to the enamel surface at six standardized points, whereas the area (µm2) was measured using a reticulated device. Data were analyzed using Kruskal-Wallis and Dunns multiple comparison tests at 5% of significance (p<0,05). It was observed a statistically significant difference (P= 0.000000372) in lesion depht (H=50,5) with lower values for GVII (0,29 µm), GVI (0,61 µm) and GV (0,89 µm) when compared to GIV (3,69 µm), GII (3,67 µm) and GIII (2,10 µm), which differences were not statistically significant in relation to GI (5,81 µm). Considering the lesion area, there was a statistically significant difference (P=0.0000256; H= 51,3), with lower values for GV (0,81µm2), GVII (1,78µm2), GVI (2,86 µm2), GIV (3,69 µm2) and GIII (4,91 µm2), when compared to GII (16,39 µm2) and GI (24,04µm2), which differences were not statistically significant. It was concluded that, fluoridated materials are effective in controlling the initiation and/or progression of caries lesion on the occlusal surface when compared to resin sealant without fluoride and no treatment.
| Identifer | oai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-10032005-165045 |
| Date | 18 October 2002 |
| Creators | Thereza Christina Lopes Coutinho |
| Contributors | Maria Francisca Thereza Borro Bijella, Izabel Cristina Santos Almeida, Marilia Afonso Rabelo Buzalaf, Marcia Cancado Figueiredo, Rafael Francisco Lia Mondelli |
| Publisher | Universidade de São Paulo, Odontologia (Odontopediatria), USP, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds