Orientador: Jose Ricardo de Albergaria-Barbosa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T12:30:17Z (GMT). No. of bitstreams: 1
Torezan_JoseFlavioRibeiro_M.pdf: 5925677 bytes, checksum: 9638126d2e9840d647a792544611be1f (MD5)
Previous issue date: 1998 / Resumo: Esse trabalho teve como objetivo a comparação histológica e biomecânica de dois tipos de superfícies de implantes cilíndricos de titânio comercialmente puros. Para esse estudo foram implantados cilindros de titânio com 6 mm de comprimento e com 3 sulcos regulares em forma de V, na metáfise tibial de 8 coelhos da raça Nova Zelândia. A tíbia esquerda de cada animal recebeu dois implantes com
superfície usinada e a tíbia direita recebeu dois implantes com superficie rugosa induzida por jateamento. A estabilidade inicial foi consegui da através do travamento do pescoço do implante na cortical óssea, ma vez que o diâmetro dos orificios ósseos preparados era cerca de 20 a 40 ].lm maior que o diâmetro externo dos cilindros. Os animais foram analisados e sacrificados nos períodos de 21 e 42 dias. Os testes de torque foram realizados em 6 animais e após o sacrificio foram retirados os fragmentos ósseos contendo os implantes, para que as peças fossem descalcificadas e analisadas por microscopia ótica. Os outros 2 animais não foram submetidos ao teste de torque com a finalidade de manter a interface intacta, pois essas peças foram preparadas para obter cortes não descalcificados. Os resultados mostraram que não houve diferenças histológicas e biomecânicas significantes entre os dois tipos de superficies estudadas. Os implantes, nos dois tipos de superficies analisadas e nos dois períodos estudados, mostraram sinais de terem áreas osseointegradas. Concluiu-se também, que o torque necessário para os desrosqueamento dos implantes aumentou em função do tempo / Abstract: The purpose of the present study was the histological and biomechanical comparison of two types of surface in commercially pUfe titanium cylinders implants. For this study the titanium implants with 6 mm oflength and 3 regular V Shaped furrows, were inserted in the tíbial metaphysis of 8 New Zealand rabbits. The left tibia, of each animal, received 2 machined surfaced cylinders and the right tibia received 2 sandblasted rough surfaced cylinders. The early stability was reached by the joining of the implant's neck in the cortical bone, because the ~diameter of the holes prepared in the bone was about 20 to 40 pm larger than the outer diameter of the cylinders. The animais were analized and killed at 21 and 42 days after implantation. The removal torque test was done in 6 animais and after the sacrifice the bone fragments that contained the implants were removed for deca1cifed sectioning preparation for light microscopic analysis. The other 2 animais were not submitted to the removal torque test, in order to preserve the intact interface, because these specimens were prepared for undeca1cified sectioning techinique. The results showed no histological and biomechanical differences between both surfaces analyzed. The implants, in both surfaces and in both times analyzed, showed signs of osseointegrated areas.It was concluded that the removal torque for the implants increased in function oftime offollow-u / Mestrado / Cirurgia e Traumatologia Buco-Maxilo-Faciais / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289427 |
| Date | 20 March 1998 |
| Creators | Torezan, José Flávio Ribeiro |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Albergaria-Barbosa, José Ricardo de, 1956-, Passeri, Luis Augusto, Mazzonetto, Renato |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 145f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0038 seconds