Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-10T13:00:43Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_FabricacaoCaracterizacaoMaterial.pdf: 8428576 bytes, checksum: 0bc32946d9995cfa61971b1ff9fc900d (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-23T01:32:29Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_FabricacaoCaracterizacaoMaterial.pdf: 8428576 bytes, checksum: 0bc32946d9995cfa61971b1ff9fc900d (MD5) / Made available in DSpace on 2014-06-23T01:32:29Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_FabricacaoCaracterizacaoMaterial.pdf: 8428576 bytes, checksum: 0bc32946d9995cfa61971b1ff9fc900d (MD5)
Previous issue date: 2011 / Neste trabalho é apresentada a fabricação e caracterização de um material compósito de matriz
polimérica reforçada por fibras naturais. A matriz é um poliéster teraftélica insaturada préacelerada
obtida comercialmente como Denverpoly 754 e o agente de cura utilizado foi o
peróxido de Mek (Butanox M- 50), na proporção de 0,33 % , em volume. A fibra natural
usada foi o tururi, obtida da região do Marajó, município de Muaná. O tecido de fibra de tururi
foi submetido a dois tipos de abertura no sentido transversal, de [50 e 100]%, em relação a
uma largura original. A fabricação do material compósito foi através do método da laminação
manual (hand lay up), seguido de uma pressão controlada através de pesos previamente
quantificados. Características físicas, mecânicas e microscópicas foram obtidas para a fibra e o
material compósito, obtendo-se resistência a tração, massa específica, gramatura do tecido,
fração mássica e imagens microscópicas antes e depois do ensaio de tração para o tecido da
fibra e ensaio de tração depois do ensaio de tração para o material compósito. O tecido de
tururi apresentou resistência a tração de 29,95 MPa (sem abertura), 12,27 MPa (abertura de 50
%) e 9,38 MPa (abertura de 100 %). A abertura provoca a diminuição da resistência à tração
do tecido de tururi. A gramatura do tecido diminuiu com a abertura do tecido. A fração
mássica do tecido do compósito foi de 14,39 % (sem abertura), 9,35 % (abertura de 50 %) e
7,19 % (abertura de 100 %). A resistência a tração do compósito foi de 35,76 MPa (sem
abertura), 19,01 MPa (50 % de abertura) e 16,8 MPa (100 % de abertura). A resistência
mecânica apresentou valores aproximados aos encontrados na literatura para materiais
compósitos reforçados por fibras naturais. As imagens obtidas em microscopia eletrônica de
varredura corroboraram com as propriedades mecânicas obtidas para cada situação do material
e fibras. / The proposition of this work is to present and characterize a composite material produced with
a polymeric matrix reinforced with natural fibers. The matrix is an insaturated teraftalic
polyester pre -accelerated with the commercial name of Denverpoly 754 and the peroxide of
MEK (Butanox M-50 ) as a catalyst in a proportion of 0,33% in volume. The natural fiber
used was the “tururi”, obtained in the Marajó region, in the municipalite of Muaná. This fiber
was submitted to two types of aperture in the transversal axis, in a proportion of 50% and
100% of the original width. The fabrication method of the composite was made through a
manual lamination process (hand lay up) using a controlled pression by weights previously
quantified. Phisycal, mechanical and microscopic characteristics were obtained for the fiber
and the composite material , and in this way , the traction resistence, specific mass , weight of
the fabric , mass fraction and microscopic image before and after the traction tests for the
fiber fabric were made, and tests of traction for the composite material. The fabric of tururi,
has shown a traction resistence of 29,95 MPa (without aperture), 12,27 MPa (aperture of 50%)
and 9,38 MPa (aperture of 100% ). The aperture produces a reduction of the traction the
resistence of the tururi fabric, and consequently reducing the traction resistence of the
material. The weight of the fabric was reduced with the aperture. The mass fraction of the
fabric of the composite was 14,39%(without aperture), 9,35 % (aperture of 50%) and 7,19%
(aperture f 100%). The traction resistance was of 35,76 MPA (withot perture), 19,01 (50%
aperture) and 16,8 MPa (100% aperture). The mechanical resistence has shown values much
like those encountered in the literature for composites reinforced with natural fibers. The
images obtained with swapping electronic microscopie, validated the mechanical properties
obtained for each situation of the material and fibers.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/5104 |
| Date | 20 April 2011 |
| Creators | DUARTE, Cláudio |
| Contributors | FUJIYAMA, Roberto Tetsuo |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Mecânica, UFPA, Brasil, Instituto de Tecnologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds