Estudo da cristalização não-isotérmica de Biocompósitos de poli(caprolactona)/fibra de cocoLIMA, Juliana Cisneiros 16 February 2017 (has links)
Submitted by Alice Araujo (alice.caraujo@ufpe.br) on 2018-04-12T22:46:57Z
No. of bitstreams: 1
DISSERTAÇÃO Juliana Cisneiros Lima.pdf: 1674644 bytes, checksum: 54eaeb5ffd90ebda0d4d98a0084cd8b1 (MD5) / Made available in DSpace on 2018-04-12T22:46:57Z (GMT). No. of bitstreams: 1
DISSERTAÇÃO Juliana Cisneiros Lima.pdf: 1674644 bytes, checksum: 54eaeb5ffd90ebda0d4d98a0084cd8b1 (MD5)
Previous issue date: 2017-02-16 / CNPQ / Compósitos de matriz polimérica biodegradável reforçados com fibras vegetais são vantajosos por serem biodegradáveis, de baixo custo e terem boas propriedades mecânicas. Neste trabalho, foram preparados compósitos de matriz de poli(caprolactona) reforçados com fibra de coco, com composição na faixa de 0 a 30% em massa de fibra. Uma parte dos compósitos foi feita com fibra natural e a outra com fibra modificada por mercerização seguida de acetilação. Teve-se como objetivo avaliar a influência da fibra e da sua modificação sobre o comportamento de cristalização dos compósitos, avaliando-se também o impacto sobre parâmetros reológicos e desempenho mecânico de tais materiais. Os compósitos, preparados em misturador interno de laboratório com fibras previamente secas e de granulometria selecionada, passaram por análises de DSC a diferentes taxas de resfriamento e ensaios mecânicos de tração. Com relação à reologia, foi verificado que o aumento no teor de fibra acarreta aumento da viscosidade do material e diminuição do seu índice de pseudoplasticidade; adicionalmente, o uso de fibras modificadas torna o material mais facilmente processável. As análises de DSC demonstraram que a presença de fibra antecipa o processo de cristalização, porém não afeta significativamente a cristalinidade absoluta desenvolvida pela matriz do compósito. A modificação da fibra não influenciou o comportamento de cristalização dos compósitos. A cinética de cristalização não isotérmica do PCL e seus compósitos foi modelada de acordo com o modelo Pseudo-Avrami, ou modelo de Avrami modificado, o qual se mostrou adequado para descrever os dados experimentais. Ensaios mecânicos indicaram que o aumento do teor de fibra de coco gera aumento no módulo de Young do material, tornando-o mais rígido, e gera diminuição na deformação na ruptura. Além disso, compósitos com teor de fibra a partir de 20% suportam tensões maiores que o polímero puro sem se deformar permanentemente, efeito que é potencializado pela modificação da superfície das fibras. / Biodegradable polymer matrix composites reinforced with vegetal fibres are advantageous due to their biodegradability, low cost and good mechanical properties. In the present work, polycaprolactone matrix composites reinforced with coconut fibre were prepared with fibre content ranging from 0 to 30% in weight. Some of the composites were prepared with natural fibres and some of them were prepared with mercerized and acetylated fibres. The aim of this work was to evaluate the influence of the fibre and its modification on the crystallization behaviour of the composites, also evaluating their impact on rheological parameters and mechanical performance of such materials. The composites, which were prepared in a lab internal mixer with dried and sieved fibres, underwent DSC analyses at different cooling rates and tensile tests. According to rheological analysis, it was verified that an increase in fibre content leads to an increase in the viscosity of the material and a decrease in its pseudoplasticity index; additionally, the use of modified fibres makes the material more easily processable. DSC analyses showed that the presence of the fibre anticipates the crystallization process, however it does not affect considerably the absolute crystallinity developed by the composite matrix. The modification of the fibre did not influence the crystallization behaviour of the composites. The non-isothermal crystallization kinetics of PCL and its composites was modelled according to Pseudo-Avrami model, or modified Avrami model, which was found to be suitable to describe the experimental data. Mechanical tests indicated that an increase in fibre content leads to an increase in Young’s modulus of the material, making it more rigid, and leads to a decrease in the elongation at break. Apart from this, composites with fibre content from 20% can stand higher tensile stress than the pure polymer without permanent deformation, and this effect is intensified by the surface modification applied to the fibres.
|
2 |
Compositos de PP com fibras de curaua obtidos por extrusão/injeção = processamento, formulação, degradação e estabilização / Composites of PP with curaua fibers : processing, formulation, degradation and stabilizationMano, Barbara Iria Silva 15 August 2018 (has links)
Orientador: Marco Aurelio De Paoli / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-15T06:04:56Z (GMT). No. of bitstreams: 1
Mano_BarbaraIriaSilva_M.pdf: 2057680 bytes, checksum: 859baca955b2cb03248e636dd9c52e70 (MD5)
Previous issue date: 2009 / Resumo: O desenvolvimento de materiais formulados com fibras vegetais é interessante para países muito ricos em recursos naturais, como o Brasil, pois se promove o desenvolvimento tecnológico aproveitando-se matéria-prima nacional, dando-lhe finalidades mais nobres. A aplicação de fibras vegetais curtas em compósitos com matrizes poliméricas tem recebido crescente atenção, pois as fibras melhoram as propriedades mecânicas dos polímeros e tem potencial para substituir fibras inorgânicas, em especial a fibra de vidro, com uma série de vantagens que incluem a leveza, biodegradabilidade e menor abrasividade aos equipamentos de processamento. Neste trabalho, estudou-se a incorporação de fibras de curauá em polipropileno, por extrusão seguida de injeção, variando-se a rotação das roscas da extrusora dupla-rosca, o teor de fibras e de agente de acoplamento. Os compósitos processados a 300 rpm e contendo 20 wt% de fibras e 2 wt% de agente de acoplamento apresentaram as melhores propriedades mecânicas nos ensaios mecânicos de tração, flexão e impacto. As propriedades não superam as dos compósitos com fibras de vidro, mas são competitivas. A degradação e estabilização foram avaliadas pelo ensaio de envelhecimento ambiental de amostras de polipropileno e compósitos com e sem estabilizantes comerciais, para analisar o efeito de cada componente sobre a degradação do sistema. Enquanto o agente de acoplamento atuou como pró-degradante, as fibras atuaram como bloqueadores da radiação e protegeram o compósito do envelhecimento. Essa parte do trabalho foi importante para definir a correta aditivação dos compósitos. Os estabilizantes escolhidos foram satisfatórios na prevenção do envelhecimento das amostras e reduziram o efeito pró-degradante do agente de acoplamento. A partir desses resultados, é possível definir a formulação adequada para cada aplicação específica. / Abstract: The development of materials formulated with vegetal fibers is interesting for countries with high availability of natural resources, like Brazil, due to the possibility of promoting technological development using their own raw materials. The use of short vegetal fibers composites with polymeric matrices have been receiving attention due to the fact that the fibers increase the mechanical properties of the polymers and have potential to substitute inorganic fibers, in special glass fiber, with many advantages that include being lighter, biodegradable and less abrasive to the processing equipments. In this work, the incorporation of curauá fibers on polypropylene matrix by extrusion and injection molding was studied, testing different screw rotation speed in the twin-screw extruder, the fiber and the coupling agent content. The composites prepared with the rotation of 300 rpm, 20 wt% of fiber and 2 wt% of coupling agent showed the best mechanical properties evaluated in tensile, flexural and impact tests This mechanical performance does not overcome the properties of the composites reinforced with glass fibers, but are competitive with them. The degradation and stabilization were evaluated through natural ageing of samples of PP and composites with and without commercial stabilizers, in order to analyze the effect of each component on the degradation of the system. While the coupling agent worked prodegrading the systems, the fibers had a screening effect and protected them from the ageing. This part of the work was important to choose suitable additivation for the composites. The stabilizers chosen for the formulation worked satisfactorily in preventing the ageing of the samples and reduced the prodegrading effect of the coupling agent. Based on these results, it is possible to define a suitable formulation of the composites for each final application. / Mestrado / Quimica Inorganica / Mestre em Química
|
3 |
Estudo de compósitos poliuretânicos reforçados com fibras de MalvaCunha, Juliana dos Santos Carneiro da, 92-99603-2218 14 December 2017 (has links)
Submitted by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2018-02-08T15:22:52Z
No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
DissertaçãoParcial_Juliana S. C. Cunha.pdf: 5451648 bytes, checksum: bdf3965ab05b80221d7638a34520dd29 (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2018-02-08T15:23:12Z (GMT) No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
DissertaçãoParcial_Juliana S. C. Cunha.pdf: 5451648 bytes, checksum: bdf3965ab05b80221d7638a34520dd29 (MD5) / Made available in DSpace on 2018-02-08T15:23:12Z (GMT). No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
DissertaçãoParcial_Juliana S. C. Cunha.pdf: 5451648 bytes, checksum: bdf3965ab05b80221d7638a34520dd29 (MD5)
Previous issue date: 2017-12-14 / FAPEAM - Fundação de Amparo à Pesquisa do Estado do Amazonas / In Brazil, it is possible to find a great diversity of lignocellulosic fibers with different
chemical, physical and mechanical properties capable of raising the resistance
of the polymers acting as reinforcement in polymer matrix. In this work,
composites were produced using as a matrix the polyurethane resin based on
castor oil reinforced with malva fibers. This native fiber is typical of the Amazon
region, easily found and still under studied. Composites with 30, 50 and 70%
mauve fiber (in mass) were prepared without and with treatment (with sodium
lignosulfonate, LS, in an ultrasonic bath for 1 h). The behavior of these malva
fibers inserted in the polyurethane matrix of castor oil (PU-OM) were evaluated
for physico-chemical and mechanical properties. The techniques of chemical
characterization of fibers (untreated and treated) and X-ray diffraction (XRD) (for
fibers), Thermogravimetry (TGA / DTG), Differential scanning calorimetry (DSC)
(DSC), IR spectroscopy, mechanical impact test, water absorption and finally
Optical Microscopy (OM) to investigate the fracture region of the composites after
impact test. The chemical analyzes showed that after treatment of the fibers with
LS, the total lignin Klason content increased by 3%. In addition, the peak in the
DTG curve after 470 °C, corresponding to lignin, had a significant increase in
intensity (about 30%). X-ray results showed that despite the decrease in cellulose
content in the fibers (from 59 to 53%) there was no change in the crystallinity
index (maintained at approximately 68%). The mechanical impact test showed
that the impact resistance increased significantly with the increase of the
percentage of fiber introduced in the composites. The treatment with LS /
ultrasonic had its proven efficiency in the composites of 70% of fiber whose
results of resistance stood out from the others. The water absorption test showed
that 70% fiber composites generally absorbed more water as a function of time,
due to the greater presence of fibers, consequently more polar groups, when
compared to the others. In general, the results were promising, as it allowed the
substitution of synthetic materials (PU) by renewable materials, fibers, manoma
oil and LS treatment. / No Brasil é possível encontrar grande diversidade de fibras lignocelulósicas com
diferentes propriedades químicas, físicas e mecânicas capazes de elevar a
resistência dos polímeros atuando como reforço em matrizes poliméricas. Neste
trabalho foram desenvolvidos compósitos poliméricos, utilizando como matriz a
resina poliuretana à base de óleo de mamona reforçada com fibras de malva.
Esta fibra nativa é típica da região amazônica, facilmente encontrada e ainda
pouco estudada. Foram preparados compósitos com 30, 50 e 70% de fibra (em
massa) de malva sem e com tratamento (com lignossulfonato de sódio, LS, em
banho de ultrassom durante 1h). O comportamento destas fibras de malva
inseridas na matriz poliuretânica de óleo de mamona (PU-OM) foram avaliadas
quanto às propriedades físico-químicas e mecânicas. Foram utilizadas as
técnicas de caracterizações químicas de fibras (não tratadas e tratadas) e
difração de raios X (DRX) (para as fibras), Termogravimetria (TGA/DTG),
Calorimetria Exploratória Diferencial (DSC), Espectroscopia na Região do
Infravermelho (FTIR), ensaio mecânico de impacto, absorção de água e por fim
Microscopia Óptica (MO) para investigar a região de fratura dos compósitos após
ensaio de impacto. As análises químicas mostraram que após o tratamento das
fibras com LS, o teor de lignina Klason total aumentou em 3%. Além disso, o pico
na curva DTG após 470 oC, correspondente à lignina, teve um aumento
significativo de intensidade (cerca de 30%). Os resultados de raio X mostraram
que apesar da diminuição do teor de celulose nas fibras (de 59 para 53%) não
houve alteração no índice de cristalinidade destas (mantido em
aproximadamente 68%). O ensaio mecânico de impacto apontou que a
resistência aumentou signitificamente com o aumento da porcentagem de fibra
introduzidos nos compósitos. O tratamento com LS/ultrassom teve sua eficiência
comprovada nos compósitos de 70% de fibra cujo resultados de resistência se
sobressaíram dos demais. O teste de absorção de água mostrou que os
compósitos com 70% de fibra em geral absorveram mais água em função do
tempo, devido à maior presença de fibras, consequentemente maior número de
grupos polares, quando comparado aos demais. No geral, os resultados foram
promissores, pois possibilitou a substituição de materiais sintéticos (PU) por
materiais de fontes renováveis, fibras, óleo de manoma e tratamento com LS.
|
4 |
Laminado de madeira reforçado com fibras naturaisSARAIVA, Marcelo Pires January 2013 (has links)
Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-11T13:45:02Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_LaminadoMadeiraReforcado.pdf: 2293625 bytes, checksum: 14daa65914076e022fb56a8d58eb1170 (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-23T01:59:21Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_LaminadoMadeiraReforcado.pdf: 2293625 bytes, checksum: 14daa65914076e022fb56a8d58eb1170 (MD5) / Made available in DSpace on 2014-06-23T01:59:21Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_LaminadoMadeiraReforcado.pdf: 2293625 bytes, checksum: 14daa65914076e022fb56a8d58eb1170 (MD5)
Previous issue date: 2013 / Visando a aplicação de recursos naturais renováveis da Amazônia, entre estes as fibras naturais, neste trabalho é apresentada a proposta de fabricação e caracterização de laminados de madeira reforçado por compósitos de matriz poliéster e fibras naturais. A matriz é um poliéster teraftálica insaturada e pré-acelerada obtida comercialmente (Duverpoly 754) e o agente de cura um peróxido de MEK (butanox M-50) na proporção de 0,33% em volume. As fibras naturais usadas para cada amostra de laminado fabricado foram o tecido de fibras de tururi, fibras de sisal e fibras de curauá e as laminas de madeira usadas foram as conhecidas comercialmente como imbuia. O tecido de tururi foi usado de duas formas: sem abertura e com abertura de 100% em relação a largura original. As fibras de sisal e curauá foram cortadas em comprimentos de 50 mm na usados na forma de pré-preg. A fabricação do material laminado foi feita através da inserção intercalada de lâmina de material compósito entre as laminas de madeira seguido de pressão controlada através de uma prensa hidráulica com pressão constante de 2 toneladas, produzindo desta forma o laminado de madeira reforçado. Características mecânicas e microestruturais foram obtidas para a lâmina de madeira e para os laminados de madeira reforçados, obtendo-se a resistência a tração, da lamina de madeira e imagens microscópicas depois do ensaio de tração. As laminas de madeira antes do reforço, foram ensaiadas tendo duas orientações de 90° e 0° de orientação das fibras. O laminado de 0°grau apresentou o melhor resistência mecânica, com valor correspondente a 35,64 MPa comparado com o valor de 0,40 MPa para a lamina de 90°. Os ensaios dos laminados de madeira reforçados, de madeira/tururi sem abertura, madeira/tururi com abertura de 100%, madeira/sisal de comprimento de fibras de 50 mm, madeira/curauá de comprimento de fibras de 50 mm, madeira/madeira com orientação de 90°a direção das fibras, alcançaram respectivamente os seguintes resultados de ensaio de tração: 61,33 MPa; 57,27 MPa; 49,27 MPA; 53,76 MPa e 68,29 MPa, sendo que o laminado de madeira/madeira apresentou o melhor resultado e a menor resistência mecânica foi registrado para o laminado de madeira reforçado por fibras de sisal. As imagens obtidas em microscopia eletrônica de varredura corroboraram com as propriedades mecânicas obtidas para cada situação do material e fibra fabricadas. / Towards the implementation of renewable natural resources of the Amazon, between these natural fibers. This paper presents the proposed fabrication and caracterization of wooden laminated matriz composites reinforced with polyester and natural fibers. The matrix is an unsaturated and pre-accelerated terephthalic polyester obtained commercially (Duverpoly 754) and a peroxide curing agent MEK (BUTANOX M-50) at a rate of 0.33 % vol. The natural fibers used for each sample of manufactured laminate were Tururi fiber tissue, sisal fibers and defibrated curauá and wood laminates known as Imbuia. The Turui tissue used with reinforcement was used in two ways: without opening and 100% opening relative to the original width. The curauá and sisal fibers were cut into lengths of 50 mm in the form of pre-preg. The manufacture of the laminated material was done by hand lay-up following controlled pressure through a hydraulic press with a constant pressure of 2 ton. Mechanical and microscopic characteristic were obtained for wood laminates. The wood laminates were assayed having two orientations of 90° and 0° of fiber orientation. The laminate of 0° degree showed the best result with a value corresponding to 35, 64 (MPa) compared to the value of 0,40 (MPa) of the lamina 90°. The tests of the laminates made of wood/Tururi without opening, wood/Tururi with opening 100%, wood/sisal fiber length of 50 mm, wood/curauá fiber length of 50 mm, wood/wood with an orientation of 90 ° the direction of the fibers, respectively achieved the following results in the Attraction tests: 61,33 (MPa), 57,27 (MPa), 49, 27 (MPa), 53, 76 (MPa) and 68, 29 (MPa), being that the laminate / wood presented the best results and lower mechanical strength was recorded for the wood laminate reinforced with sisal fibers. The images obtained in scanning electron microscopy corroborate the mechanical properties obtained for each situation of the manufactured material and fiber.
|
5 |
Perfis de polietileno reciclado carregado com fibra de açaíBRITO, Paulo Roberto de Oliveira 19 May 2012 (has links)
Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-14T13:49:29Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_PerfisPolietilenoReciclado.pdf: 1144692 bytes, checksum: b7eee342a89f5d9ad7aafd2239d2b86f (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-23T12:03:46Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_PerfisPolietilenoReciclado.pdf: 1144692 bytes, checksum: b7eee342a89f5d9ad7aafd2239d2b86f (MD5) / Made available in DSpace on 2014-06-23T12:03:46Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_PerfisPolietilenoReciclado.pdf: 1144692 bytes, checksum: b7eee342a89f5d9ad7aafd2239d2b86f (MD5)
Previous issue date: 2012 / Foram obtidos perfis tubulares porosos de polietileno (PE) e de polietileno/fibra de açaí (PE/PA) 80/20 extrudados a partir de partículas granuladas de polietileno de alta densidade reciclado de embalagens pós-consumo de 600 μm, e deste com fibra de açaí de 300 μm. Para o processamento das peças foi desenvolvida uma extrusora mono-rosca de bancada, com sistema mecânico acionado por um motor elétrico de ½ CV (0,37 kw) controlado por um inversor de freqüência, com canhões, roscas, matriz e sistema de aquecimento substituíveis. Para permitir uma visualização didática de condições de operação do equipamento de modo simplificado foram realizados testes com parafina em canhão de vidro variando-se a velocidade de rotação do parafuso e perfil de temperatura, ajustando vazão mássica e pressão na saída. Para a extrusão dos perfis porosos foram realizados ensaios reológicos de PE e PE/FA sendo selecionado rosca, barril e matriz de alumínio; rosca com passo de 9 mm e relação comprimento diâmetro (L/D) 22, composta de um elemento misturador e um elemento de flutuação na zona de controle de vazão; ângulo entre o filete e o eixo da rosca 17º, folga entre a rosca e o barril 0,15 mm; rotação de 1,3 rpm; aquecimento ao longo do canhão de 120ºC; matriz tubular com 21 mm de diâmetro interno e mandril de 19 mm de diâmetro externo. Os perfis PE e PE/FA apresentaram poros com diâmetros médios de 0,7 e 0,6 mm; densidade relativa à água a 28ºC de 0,77 e 0,73; módulo de elasticidade de 1,002 e 2,601 GPa e máximo inchamento aparente do extrudado de 100 e 80%. / Were obtained porous tubular profiles, polyethylene (PE) and polyethylene/fiber açai (PE/PA) 80/20 extruded from granulated particles of high-density polyethylene packaging recycled post-consumer 600 μm, and this with fiber açaí 300 μm. For parts processing was developed a mono-screw extruder bench, with System Mechanic powered by an electric motor of ½ HP (0.37 kw) controlled by a frequency inverter with cannons, bagels, array and replaceable heating system. To allow a preview of didactic equipment operating conditions so simplified were conducted tests with paraffin in glass ranging from Cannon-if the screw rotation speeds and temperature profile, adjusting mass flow and pressure in the output. For extrusion of profiles theological tests were conducted with porous of PE and PE/FA screw, barrel being selected and aluminum matrix; bagel with step 9 mm and length diameter ratio (L/D) 22, composed of an element mixer and a floating element in the zone of flow control; angle between the axis and thread screw 17 air gap between the screw and barrel 0.15 mm; 1.3 rpm rotation; heating along the cannon 120º C; tubular array with 21 mm internal diameter and Chuck 19 mm outside diameter. PE profiles and PE/FA showed average pore diameter 0.7 and 0.6 mm; specific gravity to water at a point 28º C 0.77 and 0.73; modulus GPa 1.002 and 2.601 and maximum apparent swelling of extruded 100 and 80%.
|
6 |
Estudo das propriedades físicas e mecânicas e da durabilidade de compósitos cimentícios reforçados com fibra amazônica / Study of physical and mechanical properties and durability of the cementation composites reinforced with amazon fiberMarques, Maria Gorett dos Santos 14 December 2015 (has links)
O presente estudo tem como objetivo principal desenvolver um compósito cimentício reforçado com fibras de arumã. O intuito é agregar valor a uma planta típica da região Amazônica, denominada arumã, pertencente à espécie do gênero Ischnosiphon arouma (aubl) Korn e originária da família Maranthaceae, de tal modo que possa ser obtido um Novo Material. Na primeira etapa do estudo foi realizada a caracterização da fibra vegetal de arumã e de todos os componentes da matriz cimentícia, a qual compreendeu ensaios químicos, físicos e mecânicos para a investigação e avaliação de suas propriedades. Na etapa seguinte, adotou-se o procedimento de trabalhar as características físicas e mecânicas das fibras junto à matriz cimentícia, compreendendo um estudo da modificação superficial da fibra por meio de tratamentos químicos à base de soluções de hidróxido de sódio ou utilizando processos com água quente e hornificação. Na terceira etapa, foram produzidas placas reforçadas com fibras sem e com tratamento, as quais, parte delas foram submetidas à cura por 28 dias e as restantes ao ensaio de envelhecimento acelerado. Os resultados obtidos na caracterização das fibras de arumã indicam o seu potencial uso como elemento de reforço para compósitos cimentícios. Por outro lado, os compósitos produzidos com telas de fibra de arumã sem e com tratamento (hornificação e alcalino), apresentaram comportamento pouco dúctil e com baixa resistência, como consequência da degradação das fibras na matriz cimentícia. Isso foi confirmado por meio de ensaios de envelhecimento acelerado com ciclos de molhagem e secagem. / This present study aims to develop a cementation composite reinforced with arumã fiber. The aim is to aggregate value to a typical plant of the Amazon region, called arumã, belonging to species of the genus Ischnosiphon arouma (Aubl) Korn and originally from Maranthaceae family, so that, it can be obtained a New Material. In the first stage of the study was performed the characterization the vegetable fiber arumã and all components of the cementicious matrix, which comprised chemical, physical and mechanical tests for research and evaluation of their properties. In the next stage, it was adopted the procedure of working the physical and mechanical characteristics of the fibers with the cementitious matrix comprising a study of the surface of the fiber modification by chemical treatments using sodium hydroxide solution or employing procedures with hot water and hornification. In the third step, the reinforced plates were produced without and with treatment, which, part of were subjected to cure for 28 days and the remaining subjected to the accelerated aging test. The results obtained in the characterization of arumã fibers indicate its potential use as a reinforcement element for cementicious composites. On the other hand, the composites produced with arumã fiber fabrics without and with a treatment (hornification and alkaline) showed slightly ductile behavior and low strength as a result of degradation of fibers in the cementitious matrix. This was confirmed through accelerated aging tests with wetting and drying cycles.
|
7 |
Estudo termo-hídrico e caracterização mecânica de compósitos de matriz polimérica reforçados com fibra vegetal: simulação 3D e experimentação. / Thermo-hydric study and mechanical characterization of polymeric matrix composites reinforced with vegetable fiber: 3d simulation and experimentation.SANTOS, Danielton Gomes dos. 12 June 2018 (has links)
Submitted by Emanuel Varela Cardoso (emanuel.varela@ufcg.edu.br) on 2018-06-12T17:23:29Z
No. of bitstreams: 1
DANIELTON GOMES DOS SANTOS – TESE (PPGEP) 2017.pdf: 7327356 bytes, checksum: f91b6ea7e4f5fe4da7e582491018b146 (MD5) / Made available in DSpace on 2018-06-12T17:23:29Z (GMT). No. of bitstreams: 1
DANIELTON GOMES DOS SANTOS – TESE (PPGEP) 2017.pdf: 7327356 bytes, checksum: f91b6ea7e4f5fe4da7e582491018b146 (MD5)
Previous issue date: 2017-03-03 / Capes / Fibras vegetais são altamente higroscópicas, e quando usadas como reforço em
compósitos poliméricos podem afetar as propriedades mecânicas do compósito. Neste trabalho avaliou-se a sorção de água e caracterização mecânica de compósitos de matriz polimérica reforçados com fibras de sisal nas condições seco e saturado com água em diferentes temperaturas (25, 50, 70°C). A matriz polimérica utilizada foi a resina poliéster insaturada (Resapol 10-316). Foram moldados por compressão corpos de prova de tração de seção transversal retangular (ASTM D 3039), corpos de prova de impacto (ASTM D 256) e corpos de prova de dimensões 20x20x3mm³ e 20x20x6mm³ para os ensaios de sorção em água (ASTM D 570). Utilizou-se compósitos na condição seco com teores de fibras em massa de: 20; 25,5; 37; 44,6 e 50%. Os compósitos confeccionados com 44,6% de fibras de sisal apresentaram as
melhores propriedades mecânicas; logo novas amostras foram submetidas a testes de imersão em água nas temperaturas de 25, 50 e 70°C e suas propriedades mecânicas avaliadas na condição saturada. Foi desenvolvido um modelo matemático (Lei de Fick) e sua solução analítica para predizer a distribuição de umidade no interior do compósito ao longo do processo e estimar o coeficiente de difusão de massa. Resultados do teor de umidade médio e distribuição do teor de umidade no sólido foram apresentados e analisados. Verificou-se que quanto maior a temperatura do banho de água, menor o tempo para atingir a saturação máxima, menor o valor das propriedades mecânicas em tração e impacto, e maior o coeficiente de difusão de massa no interior do sólido. Os estudos também indicaram que as amostras com maior relação área/volume apresentaram maiores taxas de difusão. / Vegetables fibers are highly hygroscopic, and when used as reinforcement in polymeric
composites can affect the mechanical properties of the composite. This study was carried out to evaluate the mechanical characterization and water sorption of polymeric matrix composites reinforced with sisal fibers in the dry and water saturated conditions at different temperatures (25, 50, 70°C). It was used an unsaturated polyester resin matrix (Resapol 10-316). Samples were made in rectangular cross section for tensile test (ASTM D 3039) and impact test (ASTM D256), and others samples with dimensions of 20 x 20 x 3 mm³ and 20 x 20 x 6 mm³ for water sorption tests (ASTM D570). With the aim of analyzing the tensile strength and the impact of the composite (dry conditions), samples were fabricated with fiber content (by weight): 20; 25.5; 37; 44.6 and 50%. The composites made with 44.6% sisal fibers presented the best mechanical properties, and new samples were subjected to water baths at different temperatures (25, 50 and 70°C), and their mechanical properties evaluated in the saturated condition. A
mathematical model (Fick's Law) and its analytical solution were developed to predict the distribution of moisture inside the composite throughout the process and to estimate the mass diffusion coefficient. Results of the average moisture content and distribution of the moisture content in the solid are presented and analyzed. The results exhibited how higher water bath temperature the sample takes less time to reach maximum saturation, lowest value of the mechanical properties of tensile and impact, and larger is the mass diffusion coefficient inside the solid. The studies also indicated that the samples with larger area/volume ratio presented higher diffusion rates.
|
8 |
Estudo das propriedades físicas e mecânicas e da durabilidade de compósitos cimentícios reforçados com fibra amazônica / Study of physical and mechanical properties and durability of the cementation composites reinforced with amazon fiberMaria Gorett dos Santos Marques 14 December 2015 (has links)
O presente estudo tem como objetivo principal desenvolver um compósito cimentício reforçado com fibras de arumã. O intuito é agregar valor a uma planta típica da região Amazônica, denominada arumã, pertencente à espécie do gênero Ischnosiphon arouma (aubl) Korn e originária da família Maranthaceae, de tal modo que possa ser obtido um Novo Material. Na primeira etapa do estudo foi realizada a caracterização da fibra vegetal de arumã e de todos os componentes da matriz cimentícia, a qual compreendeu ensaios químicos, físicos e mecânicos para a investigação e avaliação de suas propriedades. Na etapa seguinte, adotou-se o procedimento de trabalhar as características físicas e mecânicas das fibras junto à matriz cimentícia, compreendendo um estudo da modificação superficial da fibra por meio de tratamentos químicos à base de soluções de hidróxido de sódio ou utilizando processos com água quente e hornificação. Na terceira etapa, foram produzidas placas reforçadas com fibras sem e com tratamento, as quais, parte delas foram submetidas à cura por 28 dias e as restantes ao ensaio de envelhecimento acelerado. Os resultados obtidos na caracterização das fibras de arumã indicam o seu potencial uso como elemento de reforço para compósitos cimentícios. Por outro lado, os compósitos produzidos com telas de fibra de arumã sem e com tratamento (hornificação e alcalino), apresentaram comportamento pouco dúctil e com baixa resistência, como consequência da degradação das fibras na matriz cimentícia. Isso foi confirmado por meio de ensaios de envelhecimento acelerado com ciclos de molhagem e secagem. / This present study aims to develop a cementation composite reinforced with arumã fiber. The aim is to aggregate value to a typical plant of the Amazon region, called arumã, belonging to species of the genus Ischnosiphon arouma (Aubl) Korn and originally from Maranthaceae family, so that, it can be obtained a New Material. In the first stage of the study was performed the characterization the vegetable fiber arumã and all components of the cementicious matrix, which comprised chemical, physical and mechanical tests for research and evaluation of their properties. In the next stage, it was adopted the procedure of working the physical and mechanical characteristics of the fibers with the cementitious matrix comprising a study of the surface of the fiber modification by chemical treatments using sodium hydroxide solution or employing procedures with hot water and hornification. In the third step, the reinforced plates were produced without and with treatment, which, part of were subjected to cure for 28 days and the remaining subjected to the accelerated aging test. The results obtained in the characterization of arumã fibers indicate its potential use as a reinforcement element for cementicious composites. On the other hand, the composites produced with arumã fiber fabrics without and with a treatment (hornification and alkaline) showed slightly ductile behavior and low strength as a result of degradation of fibers in the cementitious matrix. This was confirmed through accelerated aging tests with wetting and drying cycles.
|
9 |
Governança da cadeia produtiva do Curauá, no oeste paraense, sob perspectiva do MonopsônioMaciel, Franciclei Burlamaque 19 February 2010 (has links)
Made available in DSpace on 2015-04-11T13:52:43Z (GMT). No. of bitstreams: 1
Dissertacao Franciclei Burlamaque.pdf: 2318349 bytes, checksum: bf68663e2952823cbad445e23b48f3e8 (MD5)
Previous issue date: 2010-02-19 / FAPEAM - Fundação de Amparo à Pesquisa do Estado do Amazonas / The goal of this research is to unravel the State of governance between business relations in the production chain
of Curauá; notably between the links in the household production and company link monopsonista fiber processor, situated in the West of Pará. This refers specifically: Exploring the predominant form of contract in respect of the marketing of fiber Curauá between production family and company monopsonista; Identify the determinant commercial governance; Knowing the social implications on families living Curauá production in a relationship of subordination of a monopsonista; Estimating the company's marketing margin monopsonista and Mark-up of Curauá fibres producers. In order to investigate the problem of the search was carried out
bibliographical allowing an understanding of the principal themes referenced and, a search field, where it was applied questionnaire interview with half-open questions to producers and the company monopsonista. The field research focused precípuo know the environment in the marketing of fiber Curauá and structure of the production chain. Were collected information on non-governmental and governmental institutions. The use of functionalist allowed developing an analysis of trade relations between producer and buyer monopsonista fiber. The data you have provided input to the study were of primary and secondary sources. The search covered the local production of Curauá municipalities of Juruti, Santarém and Belterra in the West of Pará State, respectively
the communities of Grand Lake, St. Benedict and Curuai Chibé. This study defines that the establishment of interrelated rules can ensure the integrity of the business of fiber Curauá. Governance in chain implies a market with efficient economic agreements. Incorporate the economic analysis is relevant to the institutional environment, especially when it comes to organizations, since the functioning of the economic system receives influence institutions. It is therefore imperative, the formation of a coordination that determine business rules, which causes an increase in production and at the same time create mechanisms of punishment to agents that eventually cease to comply with the agreements, this should help to mitigate the losses of surpluses of fiber. The absence of data on the costs of production restricts the possibility of competition, as soon as the producer of Curauá cannot but will find them, because it is a much needed tool in outline of decisions seeking business
success. It is concluded that this study contributes to increase the visibility of environment where spans the
commercialization of the fiber, in western Pará Curauá. We believe that relations between agents may take a new
direction if developed a governance for valuation and strengthening of the productive chain of Curauá in the region. / O objetivo desta pesquisa é desvendar o estado da governança entre as relações de negócios na cadeia produtiva
do Curauá; notadamente entre os elos da produção familiar e o elo da empresa monopsonista processadora da fibra, situados no oeste do Pará. Isso remete especificamente: Prospectar a forma de contrato predominante na comercialização da fibra do Curauá entre a produção familiar e a empresa monopsonista; Identificar o determinante comercial da governança; Saber as implicações sociais sobre as famílias que vivem da produção do Curauá em uma relação de subordinação de um monopsonista; Estimar a margem de comercialização da empresa monopsonista e o Mark-up dos produtores de fibras de Curauá. Com o intuito de investigar o problema da pesquisa, foi realizado levantamento bibliográfico que permitiu um entendimento das principais temáticas
referenciadas e, uma Pesquisa de Campo, onde foi aplicado questionário de entrevista com perguntas semiabertas
aos produtores e a empresa monopsonista. A pesquisa de campo teve como foco precípuo conhecer o ambiente da comercialização da fibra do Curauá e a estrutura da cadeia produtiva. Foram coletado informações em instituições não governamentais e governamentais. O uso do método funcionalista permitiu desenvolver uma análise das relações de comércio entre o produtor e o comprador monopsonista de fibra. Os dados que proporcionaram aporte ao estudo constituíram-se de fontes primária e secundária. O local da pesquisa abrangeu a produção do Curauá dos municípios de Santarém, Juruti e Belterra no Oeste do Estado do Pará, respectivamente as comunidades do Lago Grande do Curuai, São Benedito e Chibé. O presente estudo define que o
estabelecimento de regras inter-relacionadas pode garantir a integridade do negócio da fibra do Curauá. A governança na cadeia implica em um mercado com acordos econômicos eficientes. Incorporar à análise econômica ao ambiente institucional é relevante, sobretudo em se tratando das organizações, uma vez que o funcionamento do sistema econômico recebe influência das instituições. É, portanto imperioso, a formação de uma coordenação que determine as regras do negócio, que instigue o aumento da produção e ao mesmo tempo crie mecanismos de punição aos agentes que eventualmente deixarem de cumprir os acordos, isso deve
contribuir para mitigar as perdas dos excedentes da fibra. A ausência de dados sobre os custos da produção restringe a possibilidade de competição, logo o produtor do Curauá não pode deixar de apurá-los, por ser uma ferramenta bastante necessária no contorno das decisões que buscam o sucesso do negócio. Conclui-se que, este estudo contribui para ampliar a visibilidade do ambiente onde transcorre a comercialização da fibra do Curauá, no oeste paraense. Acreditamos que as relações entre os agentes podem tomar um novo rumo se ford esenvolvido uma governança em prol da valoração e do fortalecimento da cadeia produtiva do Curauá na região.
|
10 |
Avaliação de substratos orgânicos no cultivo de orquídeas nativas da APA ilha do Combu, Belém, Pará, BrasilVALENCIA, Wilmer Herrera 22 May 2009 (has links)
Submitted by Irvana Coutinho (irvana@ufpa.br) on 2012-11-05T14:26:38Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_AvaliacaoSubstratosOrganicos.pdf: 1910716 bytes, checksum: 61aa968c59981eac8d4d51eead573989 (MD5) / Made available in DSpace on 2012-11-05T14:26:38Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_AvaliacaoSubstratosOrganicos.pdf: 1910716 bytes, checksum: 61aa968c59981eac8d4d51eead573989 (MD5)
Previous issue date: 2009 / CNPq - Conselho Nacional de Desenvolvimento Científico e Tecnológico / MPEG - Museu Paraense Emílio Goeldi / As fibras naturais vem se destacando no cultivo de orquídeas, entre elas a fibra do coco é a mais promissora. Entretanto, existem outros resíduos orgânicos naturais que podem usados no cultivo. Foi realizado um estudo na Área de Proteção Ambiental Ilha do Combu, localizada no município de Belém, com o objetivo de avaliar os efeitos de substratos orgânicos no cultivo de orquídeas. As orquídeas selecionadas foram Brassia chloroleuca Barb.Rodr. e Sobralia macrophylla Rchb f. ambas nativas da APA. Entre os substratos testados, incluiu-se produto do aproveitamento do açaí, a palmeira mais freqüente na ilha. As orquídeas foram submetidas a quatro substratos considerados como tratamentos (T1 - fibra do caule do açaizeiro; T2 - fibra do coco; T3 - sementes do açaizeiro e T4 - serragem). O delineamento experimental foi inteiramente casualizado com 4 tratamentos e 4 repetições (10 indivíduos/repetição). Os parâmetros avaliados foram: o diâmetro, o comprimento, o número de brotações, número de folhas e Taxa de Sobrevivência para pseudobulbos de Brassia chloroleuca e para rebrotações de Sobralia macrophylla. Os dados foram inseridos em planilhas do Programa Bioestat 5.0. e submetidos à análise de variância e as médias comparadas pelo teste Tuckey a 5% para avaliar o grau de significância dos efeitos dos tratamentos. Os resultados mostraram que a fibra do caule do açaí promoveu o melhor desenvolvimento das estruturas vegetativas seguida da serragem em pseudobulbos de B. chloroleuca e para S. macrophylla a fibra do caule e a semente do açaí promoveram o maior desenvolvimento vegetativo. Conclui-se que a fibra do caule do açaizeiro pode ser utilizada no cultivo das espécies com aproveitamento sustentável e ecológico após o corte do palmito do açaizeiro. / The natural fibers are being considered in the cultivation of orchids, including the coconut fiber as the most promising. However, other natural organic waste can be used in the cultivation. The study was conducted in the Area of Environmental Protection Island Combu located in Belém. The objective was to evaluate the effects of organic substrates in orchids cultivation, where were selected Brassia chloroleuca Barb.Rod. and Sobralia macrophylla Rchb f. native of APA and subjected to four substrates considered as treatments (T1 - fiber from the stem of açai palm; T2 - the coconut fiber, T3 - seeds of açai palm and T4 - sawdust). The experimental design was completely randomized with 4 treatments and 4 replicates (10 individuals/replicate). The parameters were evaluated: the diameter, length, number of shoots, leaf number and rate of survival for pseudobulbos of Brassia chloroleuca and shoots of Sobralia macrophylla. Data were inserting into the spreadsheet program Bioestat 5.0. and subjected to analysis of variance and averages compared by the Tuckey test at 5% to assess the degree of significance of the effects of treatments. The results showed that the fiber from the stem açaí palm promoved development of vegetative structures followed by sawing in pseudobulbos of B. chloroleuca and S. macrophylla fiber to the stem and seeds of the açaí palm promoved greater growth. It was concluded that the fiber of the stalk of açai palm can be used in the cultivation of species with ecological and sustainable recovery after cutting the açaí palm.
|