Made available in DSpace on 2015-04-22T22:08:45Z (GMT). No. of bitstreams: 1 Arquivo 1.pdf: 177114 bytes, checksum: 4332c797185836df7d25ada5d68629a1 (MD5) Previous issue date: 2010-07-10 / Açaí is the fruit of the açaí palm, a palm tree native of the Brazilian Amazon, found near the creeks. In the North there is a large consumption of fruit pulp of açaí, with an accumulation of waste without proper management. This residue causes harm to public health and environmental disturbances. In this work we developed panels with fiber from the seed of açaí (Euterpe Precatória ) from the physical, chemical and mechanical fiber. The research was divided into two stages, which was the morphological characterization, chemical of the physical and mechanical analysis fiber açaí, and then the panels were fabricated and therewere made tests of the panels. The principle was made a preliminary panel to set the level of fiber and resin, from the results of static bending, this was produced 6 (six) fiber panels with adhesive based on castor oil and polyurethane resin derived from petroleum. According to NBR 148103, assays were performed in static bending, tensile and screw perpendicular to the surface. The results were satisfactory, with values above the norm NBR 148103, meeting the technical requirements for construction and furniture industry / O açaí é fruto do açaizeiro, uma palmeira natural da Amazônia brasileira, encontrada próximo dos igarapés. Na região Norte existe um grande consumo da polpa do fruto do açaí, com um acúmulo de resíduo sem manejo adequado. Este resíduo provoca malefícios para a saúde pública e transtornos ambientais. No presente trabalho foram desenvolvidos painéis com a fibra da semente do açaí (Euterpe Precatória ), a partir da caracterização morfológica, física, química e mecânica da fibra. A pesquisa foi dividida em duas etapas, no qual foi feita a caracterização morfológica, análise química, análise física e mecânica da fibra do açaí, e em seguida foram confeccionados os painéis e feitos os ensaios dos painéis. A princípio foi feito um painel preliminar para definir o teor de fibra e de resina, a partir do resultado do ensaio de flexão estática, deste foram produzidos 07 (sete) painéis de fibra, com adesivo a base de mamona e resina poliuretana derivada de petróleo. De acordo com a norma NBR 148103, foram realizados os ensaios de flexão estática, tração perpendicular e arrancamento de parafuso de superfície. Os resultados obtidos foram satisfatórios, com valores acima da norma NBR 148103, atendendo requisitos técnicos da construção civil e para a indústria moveleira

Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-14T13:49:29Z No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_PerfisPolietilenoReciclado.pdf: 1144692 bytes, checksum: b7eee342a89f5d9ad7aafd2239d2b86f (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-23T12:03:46Z (GMT) No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_PerfisPolietilenoReciclado.pdf: 1144692 bytes, checksum: b7eee342a89f5d9ad7aafd2239d2b86f (MD5) / Made available in DSpace on 2014-06-23T12:03:46Z (GMT). No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_PerfisPolietilenoReciclado.pdf: 1144692 bytes, checksum: b7eee342a89f5d9ad7aafd2239d2b86f (MD5) Previous issue date: 2012 / Foram obtidos perfis tubulares porosos de polietileno (PE) e de polietileno/fibra de açaí (PE/PA) 80/20 extrudados a partir de partículas granuladas de polietileno de alta densidade reciclado de embalagens pós-consumo de 600 μm, e deste com fibra de açaí de 300 μm. Para o processamento das peças foi desenvolvida uma extrusora mono-rosca de bancada, com sistema mecânico acionado por um motor elétrico de ½ CV (0,37 kw) controlado por um inversor de freqüência, com canhões, roscas, matriz e sistema de aquecimento substituíveis. Para permitir uma visualização didática de condições de operação do equipamento de modo simplificado foram realizados testes com parafina em canhão de vidro variando-se a velocidade de rotação do parafuso e perfil de temperatura, ajustando vazão mássica e pressão na saída. Para a extrusão dos perfis porosos foram realizados ensaios reológicos de PE e PE/FA sendo selecionado rosca, barril e matriz de alumínio; rosca com passo de 9 mm e relação comprimento diâmetro (L/D) 22, composta de um elemento misturador e um elemento de flutuação na zona de controle de vazão; ângulo entre o filete e o eixo da rosca 17º, folga entre a rosca e o barril 0,15 mm; rotação de 1,3 rpm; aquecimento ao longo do canhão de 120ºC; matriz tubular com 21 mm de diâmetro interno e mandril de 19 mm de diâmetro externo. Os perfis PE e PE/FA apresentaram poros com diâmetros médios de 0,7 e 0,6 mm; densidade relativa à água a 28ºC de 0,77 e 0,73; módulo de elasticidade de 1,002 e 2,601 GPa e máximo inchamento aparente do extrudado de 100 e 80%. / Were obtained porous tubular profiles, polyethylene (PE) and polyethylene/fiber açai (PE/PA) 80/20 extruded from granulated particles of high-density polyethylene packaging recycled post-consumer 600 μm, and this with fiber açaí 300 μm. For parts processing was developed a mono-screw extruder bench, with System Mechanic powered by an electric motor of ½ HP (0.37 kw) controlled by a frequency inverter with cannons, bagels, array and replaceable heating system. To allow a preview of didactic equipment operating conditions so simplified were conducted tests with paraffin in glass ranging from Cannon-if the screw rotation speeds and temperature profile, adjusting mass flow and pressure in the output. For extrusion of profiles theological tests were conducted with porous of PE and PE/FA screw, barrel being selected and aluminum matrix; bagel with step 9 mm and length diameter ratio (L/D) 22, composed of an element mixer and a floating element in the zone of flow control; angle between the axis and thread screw 17 air gap between the screw and barrel 0.15 mm; 1.3 rpm rotation; heating along the cannon 120º C; tubular array with 21 mm internal diameter and Chuck 19 mm outside diameter. PE profiles and PE/FA showed average pore diameter 0.7 and 0.6 mm; specific gravity to water at a point 28º C 0.77 and 0.73; modulus GPa 1.002 and 2.601 and maximum apparent swelling of extruded 100 and 80%.