Previous issue date: 2015-02-09 / CNPq / Neste trabalho, utilizando a técnica de intercalação por fusão, foram preparados híbridos à base de polipropileno homopolímero com 5% em peso de argila bentonítica organofílica, compatibilizante polipropileno enxertado com anidrido maleico em teores de 5 e 15%, e co-intercalante erucamida em teores de 0,5 e 1,0%. Os sistemas foram processados em misturador interno e extrusora dupla rosca corrotacional interpenetrante, sob uma única condição de processamento. Os híbridos foram caracterizados por índice de fluidez (MFI), calorimetria exploratória diferencial (DSC), termogravimetria (TG), difração de raios-X (DRX), microscopia óptica, microscopia eletrônica de varredura (MEV), microscopia eletrônica de transmissão (MET) e propriedades mecânicas em tração e impacto. Os resultados de índice de fluidez evidenciaram a redução deste parâmetro com a adição da argila e/ou aditivos (compatibilizante e co-intercalante), indicando aumento da viscosidade nos sistemas. Por DSC e TG foi possível observar que a presença da argila e do agente compatibilizante elevou a estabilidade térmica dos materiais quando comparados ao polipropileno puro. Os resultados de difração de raios X mostraram aumento da distância interplanar basal d(001) dos sistemas, formando estruturas intercaladas, em especial nas composições em que o agente co-intercalante foi empregado. A resistência à tração dos sistemas não foi afetada significativamente, mas foi observado um aumento no módulo de elasticidade e na resistência ao impacto com a incorporação dos compatibilizantes. A microscopia eletrônica de transmissão revelou a formação de nanocompósitos com estruturas parcialmente esfoliadas e/ou intercaladas. / In this work, hybrids of polypropylene homopolymer containing 5% by weight organoclay, 5 and 15% maleic anhydride grafted polypropylene and 0.5 and 1.0% erucamide, respectively, were prepared by melt intercalation. The systems were processed in an internal mixer and corotating twin screw extruder, at a single processing condition. The hybrids were characterized by melt flow index (MFI), differential scanning calorimetry (DSC), thermogravimetry (TG), X-ray diffraction (XRD), optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and tensile and impact properties. Melt flow rate results showed a decrease in this parameter with clay and/or additives (compatibilizer and co-intercalant) addition, which indicates an increase in the system´s viscosity. DSC and TG, data suggested that the thermal stability of the systems increased with clay and coupling agent incorporation. X-ray diffraction results showed increased basal interplanar distance d(001) of the systems forming intercalated structures, in particular in compositions where the co-intercalating agent was utilized. The tensile strength of the systems was not significantly affected, however, an increase on elastic modulus and on impact resistance was observed with the additives incorporation. Transmission electron microscopy revealed the formation of partially exfoliated and/or intercalated nanocomposites.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1156 |
Date | 12 July 2018 |
Creators | SILVA NETO, João Emídio da. |
Contributors | CARVALHO, Laura Hecker de., ALVES, Tatianny Soares., CANEDO, Eduardo Luis., MELO, Tomas Jéferson Alves de. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds