To address the challenges associated with urban expansion and environmental changes, innovative interlocking concrete block pavement (ICBP) is being researched for usage in urban areas. The ICBP is designed to have higher durability and better long-term performance compared to traditional asphalt pavement. Using recycled concrete aggregates (RCA) and supplementary cementing materials (SCMs) can provide many environmental benefits. The objective of this research is to investigate the mechanical properties of concrete with recycled materials. This also involves the assessment of deflection and stresses associated with ICBP using the finite element method.
Four concrete mixtures with different RCA and SCMs contents were designed and cast. The RCA replacement levels were 20% and 40%, while slag and glass pozzolan were added to improve mechanical properties. The results showed that the use of RCA had adverse impacts on workability. The 28 days compressive strength of the Control Mix was 40 MPa. The compressive strength of Mix 3 was 40.5 MPa which was the highest strength among all mixtures. It demonstrated that a 40% RCA replacement level could have a non-negative effect on mechanical properties when the SCMs are added.
A three-dimensional pavement model was established using ABAQUS software. The orthogonal experimental design was used to evaluate the effects of the length/width ratio of blocks, the block thickness, the elastic modulus, and the laying pattern of blocks on the deflection and von Mises stress of all ICBP models under the vertical load. Considering the deflection of the loading area, the length/width ratio had the greatest effect, then comes with thickness, elastic modulus, and laying pattern according to the Range Analysis. The bigger block size and higher elastic modulus of blocks could provide even better performance. Overall, the herringbone laying pattern is recommended as the optimum laying pattern with minimum deflection. It also contributes to better load spreading. / Thesis / Master of Applied Science (MASc)
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/27820 |
| Date | 11 1900 |
| Creators | Ni, Xinyue |
| Contributors | Tighe, Susan, Civil Engineering |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0017 seconds