<p>All conducting polymers are potentially electrochromic, owing to the injection of charge carriers that changes their electronic structure and results in a shift of their optical absorption towards higher wavelengths. PEDOT-PSS and PEDOT-S are very promising materials in terms of electrochromic properties, due to the good contrast existing between their doped and undoped forms. However this contrast has to be enhanced in order to design more efficient electrochromic devices, and new solutions should thus be found in order to solve this issue.</p><p>Surface plasmons are described as electromagnetic waves propagating along the surface between a dielectric and a metal. Coupled to an incident radiation, they create an energy loss in the light transmitted and reflected by the interface. When the metallic surface is periodically corrugated, this absorption phenomenon due to plasmonic resonance occurs at a specific wavelength that depends on several parameters, such as the incidence angle, the dielectric constants of the two media and the grating period. By coating metallic gratings with electrochromic polymers, we may thus be able to trigger a plasmonic absorption at a given wavelength and shift it upon reduction or oxidation of the material.</p><p>Electrochromic devices consisting of PEDOT-PSS or PEDOT-S spin-deposited on gold and silver gratings were investigated by UV-visible reflectance measurements. The periodically corrugated structures were reproduced from commercial gratings by soft nanolithography and were analyzed by AFM. Some electrochromic cells exhibited new colors or a high shift of the plasmonic resonance upon redox switching of the polymer film. Depending on the step and the nature of the grating employed, this shift could reach 20 nm in the case of PEDOT-PSS and more than 100 nm for PEDOT-S. A theoretical model was found to predict the wavelength of plasmonic excitation and the orientation of the shift.</p>
Identifer | oai:union.ndltd.org:UPSALLA/oai:DiVA.org:liu-11522 |
Date | January 2008 |
Creators | Garnier, Jérôme |
Publisher | Linköping University, Department of Science and Technology, Institutionen för fysik, kemi och biologi |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, text |
Page generated in 0.0014 seconds